Polymer Property : Tensile Strength, Yield = 2320 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	16.0 MPa	2320 psi	50 mm/min; ASTM D638
Mytex Polymers AN16L-53 Polypropylene, Compounded Description: Compounded polypropylene produced for automotive exterior applications using Mytex® Technology.Key Applications: Body side moldingInformation provided by Mytex Polymers
Tensile Strength, Yield	16.0 MPa	2320 psi	50 mm/min; ISO 527
Mytex Polymers AS78L-GM Polypropylene, Rubber modified, Compounded Description: AS78L-GM is a compounded, rubber modified polypropylene with good impact and excellent material flow properties. This product is designed for painted and mold-in-color applications.Key..
Tensile Strength, Yield	16.0 MPa	2320 psi	ASTM D412
Precision Polymer Engineering Perlast® G60T Perfluoroelastomer A black perfluoroelastomer compound with excellent steam resistance and mechanical properties. It has extremely low outgassing properties.Applications: This grade is particularly suited to static ap..
Tensile Strength, Yield	16.0 MPa	2320 psi	ASTM D412
Precision Polymer Engineering Z80B Hydrogenated NBR Compound Peroxide cured, Hydrogenated Nitrile Rubber, 75-80 °IRHD. Medium acrylonitrile content (ACN = 33.5%). ASTM designation = HNBR. ASTM D2000 line call-out 4MDH716, A26, B36, EO16, EO36, F14, Z1. Z1 ..
Tensile Strength, Yield	16.0 MPa	2320 psi	Rate of 50 mm/min; ASTM D 638
NOVA Chemicals Surpass® IFs932-R Octene SLLDPE Injection Molding Resin IFs932-R complies with the U.S. FDA regulations for olefin polymers and may thus be used in the United States as an article or component of an article intended for use in contact with food.NOVA Chem..
Tensile Strength, Yield	16.0 MPa	2320 psi	ISO 527
Premix Thermoplastics PRE-ELEC® PE 1313 (discontinued **) PRE-ELEC PE 1313 is a conductive thermoplastic compound based on PE-LLD. Conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivity PRE-ELEC PE 13..
Tensile Strength, Yield	16.0 - 38.6 MPa	2320 - 5600 psi	Average value: 23.6 MPa Grade Count:32
Overview of materials for Polypropylene with 20% Mica Filler This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene with 20% Mica Filler". Specific grades with primary filler content between 15% and 24% are..
Tensile Strength, Yield	16.0 - 23.5 MPa	2320 - 3410 psi	Average value: 19.2 MPa Grade Count:6
Overview of materials for Polytetrafluoroethylene (PTFE), Glass Filled, Molded This property data is a summary of similar materials in the MatWeb database for the category "Polytetrafluoroethylene (PTFE), Glass Filled, Molded". Each property range of values reported is minimum..
Tensile Strength, Yield	16.0 MPa	2320 psi	50 mm/min; ASTM D638
ICO Polymers ICORENEâ„¢ 110-1327 LMDPE Rotational Molding Resin Description: ICORENE 110-1327 is a linear medium density polyethylene developed for use in rotational molding. This is a very fast processing material that quickly molds out to offer low surface po..
Tensile Strength, Yield	16.0 MPa	2320 psi	50mm/min; ASTM D638-64T
Micropol Microlin ML20 Linear Polyethylene Rotational Molding Powder Information provided by Micropol Limited
Tensile Strength, Yield	16.0 MPa	2320 psi	50mm/min; ASTM D638-64T
Micropol Microlin ML21 Linear Polyethylene Rotational Molding Powder Information provided by Micropol Limited
Tensile Strength, Yield	16.0 MPa	2320 psi	ISO 527-1, -2
LyondellBasell Hifaxâ„¢ ETA3081HS Thermoplastic Polyolefin Elastomer Description: Hifaxâ„¢ ETA3081HS medium melt flow, 800 MPa flexural modulus, paintable thermoplastic elastomeric olefin (TEO) resin has balanced physical properties, moldability and paintability. ..
Tensile Strength, Yield	16.0 MPa	2320 psi	ISO 527-1, -2
LyondellBasell Hostacomâ„¢ BR712GC Polypropylene Copolymer Description: Hostacomâ„¢ BR712GC conventional melt flow, 1,300 MPa flexural modulus, UV-stabilized, mineral-filled polypropylene copolymer has an excellent balance of stiffness, impact and weathe..
Tensile Strength, Yield	16.0 MPa	2320 psi	5 mm/min; ISO 527
SABIC Innovative Plastics LNP Thermocomp MX05038 PP (Europe-Africa-Middle East) Polypropylene compound, containing miniral. Added features include High ImpactThis data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
Tensile Strength, Yield	16.0 MPa	2320 psi	ISO 527
SABIC Innovative Plastics LNP THERMOCOMP TH0450C PUR (Asia Pacific) LNP* Thermocomp* TH0450C is a compound based on Polyurethane resin containing High Specific Gravity Filler. Added features of this material include: High Specific Gravity.
Tensile Strength, Yield	16.0 MPa	2320 psi	ISO 527
SABIC Innovative Plastics LNP THERMOCOMP TH0750A PUR (Asia Pacific) LNP THERMOCOMP* TH0750A is a compound based on Polyurethane resin. Added features of this material include: High Specific Gravity.
Tensile Strength, Yield	16.0 MPa	2320 psi	9.8 in/min; ASTM D638
Teknor Apex Sinvicomp SSH 5509 Polyvinyl Chloride, Flexible Availability: Asia Pacific Features: Good Flexibility Uses: Cable Jacketing; Wire and Cable Applications Wire Types: ST1; ST2; Type 9; Class 1/3 Agency Ratings: BS 6746; IEC 60502; JIS 6723 Forms: ..
Tensile Strength, Yield	16.0 MPa	2320 psi	50mm/min; ISO 527-2
Borealis Daplen™ EE255AE Polypropylene TPO Compound Daplen™ EE255AE is a 20% mineral filled elastomer modified polypropylene compound intended for injection molding. This material has an excellent balance between impact strength and stiffness, give..
Tensile Strength, Yield	16.0 MPa	2320 psi	50mm/min; ISO 527-2
Borealis Daplen™ EE340AE Polypropylene TPO Compound Daplen™ EE340AE is a 30% mineral filled elastomer modified polypropylene compound intended for injection molding. This material has excellent balanced mechanical properties, gives a good surface q..
Tensile Strength, Yield	16.0 MPa	2320 psi	ASTM D638
A. Schulman POLYFORT™ FXP 1245U UV Stable Copolymer Polypropylene DescriptionPolyfort® FXP 1245U is a 40% CAC03 filled UV stable copolymer polypropylene product. Information provided by A. Schulman.
Tensile Strength, Yield	16.0 MPa	2320 psi	At 50 mm/min; ISO 527-2
Borealis Daplen™ VB4411 TPO Compound Daplen VB4411 is a 10% mineral and elastomer modified polypropylene compound intended for injection molding. Daplen VB4411 is a material with excellent impact /stiffness ratio. Thanks to its low th..
Tensile Strength, Yield	16.0 MPa	2320 psi
Trelleborg R520 Natural Rubber Polyisoprene All information provided by Trelleborg
Tensile Strength, Yield	16.0 MPa @Strain 50.0 %	2320 psi @Strain 50.0 %	50 mm/min
Arkema Group Rilsan® BESN F15 TL Nylon 11, Flexible Tubing Grade (Dry) Designation ISO 1874-PA11-P,EHL,16-001High flexible grade for tubes extrusion. Available color: black and natural. Light and heat stabilized.High flexibility. High burst pressure and impact strength..
Tensile Strength, Yield	16.0 MPa	2320 psi	ASTM D638
Aclo Accutech Polypropylene Copolymer CP0437T20L Talc Reinforced
Tensile Strength, Yield	16.0 MPa	2320 psi	ASTM D638
Aclo Accutech Polypropylene Copolymer CP0437T30L Talc Reinforced
Tensile Strength, Yield	16.0 MPa	2320 psi	ASTM D638
Aclo Accutech Polypropylene Copolymer CP0437T40L Talc Reinforced
Tensile Strength, Yield	16.0 MPa	2320 psi	ASTM D638
Aclo Accutech Polypropylene Copolymer CP0437W20L Wollastonite Reinforced
Tensile Strength, Yield	>= 16.0 MPa	>= 2320 psi	ASTM D638
Buckeye Polymers BP FLEX D6020 BLK Thermoplastic Polyolefin Product Information: TPO's are a family of thermoplastic elastomers which exhibit rubber-like properties and are processable on conventional thermoplastic equipment.Product Features:High tear resist..
Tensile Strength, Yield	16.0 MPa	2320 psi
BASF Novolen® 2800 J Polypropylene Injection molded partsData was collected by ISO methods and provided by BASF.
Tensile Strength, Yield	16.0 MPa	2320 psi	At 50 mm/min; ISO 527-2
Borealis Daplen™ PB4432 TPO Compound Daplen PE4432 is a 10% mineral and elastomer modified polypropylene compound intended for injection molding. Daplen PE4432 is a material with excellent impact /stiffness ratio. Thanks to its low th..