Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Modulus of Elasticity | 137 GPa @Temperature 1000 °C |
19900 ksi @Temperature 1830 °F |
|
Haynes 214® alloy, 0% cold reduction Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
Modulus of Elasticity | 137 GPa @Temperature 1000 °C |
19900 ksi @Temperature 1830 °F |
|
Haynes 214® alloy, 10% cold reduction, 925°C for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
Modulus of Elasticity | 137 GPa @Temperature 1000 °C |
19900 ksi @Temperature 1830 °F |
|
Haynes 214® alloy, 10% cold reduction, 980°C (1800°F) for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
Modulus of Elasticity | 137 GPa @Temperature 1000 °C |
19900 ksi @Temperature 1830 °F |
|
Haynes 214® alloy, 20% cold reduction Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
Modulus of Elasticity | 137 GPa @Temperature 1000 °C |
19900 ksi @Temperature 1830 °F |
|
Haynes 214® alloy, 20% cold reduction, 1095°C (2000°F) for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
Modulus of Elasticity | 137 GPa @Temperature 1000 °C |
19900 ksi @Temperature 1830 °F |
|
Haynes 214® alloy, 20% cold reduction, 925°C for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
Modulus of Elasticity | 137 GPa @Temperature 1000 °C |
19900 ksi @Temperature 1830 °F |
|
Haynes 214® alloy, 30% cold reduction, 1095°C (2000°F) for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
Modulus of Elasticity | 137 GPa @Temperature 1000 °C |
19900 ksi @Temperature 1830 °F |
|
Haynes 214® alloy, 30% cold reduction, 925°C for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
Modulus of Elasticity | 137 GPa @Temperature 1000 °C |
19900 ksi @Temperature 1830 °F |
|
Haynes 214® alloy, 40% cold reduction Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
Modulus of Elasticity | 137 GPa @Temperature 1000 °C |
19900 ksi @Temperature 1830 °F |
|
Haynes 214® alloy, 40% cold reduction, 1095°C (2000°F) for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
Modulus of Elasticity | 137 GPa @Temperature 1000 °C |
19900 ksi @Temperature 1830 °F |
|
Haynes 214® alloy, 40% cold reduction, 980°C (1800°F) for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
Modulus of Elasticity | 137 GPa @Temperature 1000 °C |
19900 ksi @Temperature 1830 °F |
|
Haynes 214® alloy, 50% cold reduction Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
Modulus of Elasticity | 137 GPa @Temperature 1000 °C |
19900 ksi @Temperature 1830 °F |
|
Haynes 214® alloy, 50% cold reduction, 1095°C (2000°F) for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
Modulus of Elasticity | 137 GPa @Temperature 1000 °C |
19900 ksi @Temperature 1830 °F |
|
Haynes 214® alloy, 50% cold reduction, 925°C for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
Modulus of Elasticity | 137 GPa @Temperature 1000 °C |
19900 ksi @Temperature 1830 °F |
|
Haynes 214® alloy, cold rolled annealed sheet 2.0-3.2 mm thick Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
Modulus of Elasticity | 137 GPa @Temperature 1000 °C |
19900 ksi @Temperature 1830 °F |
|
Haynes 214® alloy, hot rolled solution annealed plate 12.7 mm (1/2 in.) thick Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
Modulus of Elasticity | 137 GPa @Temperature 1000 °C |
19900 ksi @Temperature 1830 °F |
|
Haynes 214® alloy, sheet, 100 hours exposure at 760°C (1400°F) Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
Modulus of Elasticity | 137 GPa @Temperature 1000 °C |
19900 ksi @Temperature 1830 °F |
|
Haynes 214® alloy, sheet, 1000 hours exposure at 870°C (1600°F) Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
Modulus of Elasticity | 137 GPa @Temperature 1000 °C |
19900 ksi @Temperature 1830 °F |
|
Haynes 214® alloy, sheet, 1000 hours exposure at 980°C (1800°F) Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
Modulus of Elasticity | 137 GPa @Temperature 1000 °C |
19900 ksi @Temperature 1830 °F |
|
Haynes 214® alloy, sheet, 32 hours exposure at 760°C (1400°F) Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
Modulus of Elasticity | 137 GPa @Temperature 1000 °C |
19900 ksi @Temperature 1830 °F |
|
Haynes 214® alloy, sheet, 32 hours exposure at 870°C (1600°F) Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
Modulus of Elasticity | 137 GPa @Temperature 980 °C |
19900 ksi @Temperature 1800 °F |
|
Haynes HR-160® alloy plate, aged 1000 hours at 649°C (1200°F) Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
Modulus of Elasticity | 137 GPa @Temperature 980 °C |
19900 ksi @Temperature 1800 °F |
|
Haynes HR-160® alloy, plate, aged 1000 hours at 871°C (1600°F) Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
Modulus of Elasticity | 137 GPa @Temperature 980 °C |
19900 ksi @Temperature 1800 °F |
|
Haynes HR-160® alloy, plate, aged 4000 hours at 760°C (1400°F) Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
Modulus of Elasticity | 137 GPa @Temperature 980 °C |
19900 ksi @Temperature 1800 °F |
|
Haynes HR-160® alloy, plate, aged 4000 hours at 871°C (1600°F) Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
Modulus of Elasticity | 137 GPa @Temperature 980 °C |
19900 ksi @Temperature 1800 °F |
|
Haynes HR-160® alloy, plate, aged 8000 hours at 871°C (1600°F) Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
Modulus of Elasticity | 137 GPa @Temperature 980 °C |
19900 ksi @Temperature 1800 °F |
|
Haynes HR-160® alloy, solution annealed sheet Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
Modulus of Elasticity | 137 GPa @Temperature 1000 °C |
19900 ksi @Temperature 1830 °F |
|
Haynes 214® alloy, 10% cold reduction, 1095°C (2000°F) for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
Modulus of Elasticity | 137 GPa @Temperature 1000 °C |
19900 ksi @Temperature 1830 °F |
|
Haynes 214® alloy, 30% cold reduction Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
Modulus of Elasticity | 137 GPa @Temperature 980 °C |
19900 ksi @Temperature 1800 °F |
|
Haynes HR-160® alloy plate, aged 8000 hours at 649°C (1200°F) Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |