Eurostar Starflam P10002E PA6, Injection Molded

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced, Flame Retardant
Manufacturer Eurostar Engineering Plastics
Trade Name Starflam
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Eurostar Starflam P10002E PA6, Injection Molded.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Starflam P10002E is a Unfilled, Halogen Free and Red Phosphorous Free, Flame Retardant, Polyamide 6 Injection Molding Resin (also known as P1000Z220 or PA6 U2 Z22)Information provided by Polymer Technology & Services, the North American exclusive supplier.
Physical Properties Metric English Comments
Density 1.17 g/cc
0.0423 lb/in³
ISO 1183
Linear Mold Shrinkage, Flow 0.0080 - 0.015 cm/cm

@Time 86400 sec
 0.0080 - 0.015 in/in

@Time 24.0 hour
 ISO 294
Mechanical Properties Metric English Comments
Tensile Strength at Break 75.0 MPa
10900 psi
ISO 527
Elongation at Break 5.0 %
5.0 %
ISO 527
Tensile Modulus 3.40 GPa
493 ksi
1 mm/min; ISO 527
Flexural Strength 105 MPa
15200 psi
ISO 178
Flexural Modulus 3.50 GPa
508 ksi
ISO 178
Izod Impact, Notched (ISO) 4.00 kJ/m²
1.90 ft-lb/in²
80x10x4; ISO 180/1A
Izod Impact, Unnotched (ISO) 60.0 kJ/m²
28.6 ft-lb/in²
80x10x4; ISO 180/1U
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 200 °C
392 °F
Flatw 80x10x4, sp=64 mm; ISO 75/Bf
Deflection Temperature at 1.8 MPa (264 psi) 80.0 °C
176 °F
Flatw 80x10x4, sp=64 mm; ISO 75/Af
UL RTI, Electrical 120 °C

@Thickness 0.750 mm
 248 °F

@Thickness 0.0295 in
120 °C

@Thickness 1.50 mm
 248 °F

@Thickness 0.0591 in
120 °C

@Thickness 3.00 mm
 248 °F

@Thickness 0.118 in
UL RTI, Mechanical with Impact 65.0 °C

@Thickness 0.750 mm
 149 °F

@Thickness 0.0295 in
75.0 °C

@Thickness 1.50 mm
 167 °F

@Thickness 0.0591 in
75.0 °C

@Thickness 3.00 mm
 167 °F

@Thickness 0.118 in
UL RTI, Mechanical without Impact 85.0 °C

@Thickness 0.750 mm
 185 °F

@Thickness 0.0295 in
85.0 °C

@Thickness 1.50 mm
 185 °F

@Thickness 0.0591 in
85.0 °C

@Thickness 3.00 mm
 185 °F

@Thickness 0.118 in
Flammability, UL94 V-0

@Thickness 0.750 mm
 V-0

@Thickness 0.0295 in
 IEC 60695-11-10
V-0

@Thickness 1.50 mm
 V-0

@Thickness 0.0591 in
 IEC 60695-11-10
V-0

@Thickness 3.00 mm
 V-0

@Thickness 0.118 in
 IEC 60695-11-10
Glow Wire Test 725 °C

@Thickness 0.750 mm
 1340 °F

@Thickness 0.0295 in
 Glow-Wire Ignition; IEC 60695-2-13
960 °C

@Thickness 0.750 mm
 1760 °F

@Thickness 0.0295 in
 Glow-Wire Flammability; IEC 60695-2-12
Electrical Properties Metric English Comments
Comparative Tracking Index >= 600 V
>= 600 V
PLC 0
Hot Wire Ignition, HWI 7.0 - 15 sec

@Thickness 0.750 mm
 7.0 - 15 sec

@Thickness 0.0295 in
 PLC 4
High Amp Arc Ignition, HAI >= 120 arcs

@Thickness 0.750 mm
 >= 120 arcs

@Thickness 0.0295 in
 PLC 0
>= 120 arcs

@Thickness 1.50 mm
 >= 120 arcs

@Thickness 0.0591 in
 PLC 0
>= 120 arcs

@Thickness 3.00 mm
 >= 120 arcs

@Thickness 0.118 in
 PLC 0
Processing Properties Metric English Comments
Rear Barrel Temperature 230 - 240 °C
446 - 464 °F
Zone 1
Middle Barrel Temperature 235 - 245 °C
455 - 473 °F
Zone 2
Front Barrel Temperature 240 - 260 °C
464 - 500 °F
Zone 3
Melt Temperature 240 - 260 °C
464 - 500 °F
Mold Temperature 60.0 - 80.0 °C
140 - 176 °F
Drying Temperature 75.0 - 85.0 °C
167 - 185 °F
Dry Time 4.00 - 6.00 hour
4.00 - 6.00 hour
Moisture Content 0.20 %
0.20 %