- Polymer Property : Tensile Strength at Break = 10900 psi
Polymer Property : Tensile Strength at Break = 10900 psi Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 75.0 MPa | 10900 psi | STN EN ISO 527-2 |
| Plastcom SLOVAMID 66 W 30 Polyamide 66, 30% Mineral Filled FeaturesPA 66 with the content of 30% chemically modified mineral filler. Used for grips of electric hand tools, hobby tools, gear wheels, covers of electric tools, flat products, automobile wheel .. |
|||
| Tensile Strength at Break | 75.0 MPa | 10900 psi | ISO 527 |
| Nilit FRIANYL A63 HS-GV10 Nylon 6.6 for injection molding, 10% glass fiber reinforced Nylon 6.6 for injection molding, high impact modified.Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
| Tensile Strength at Break | 75.0 MPa | 10900 psi | ISO 527 |
| Nilit FRIANYL B63 KV20 Nylon 6 for injection molding, 20% glass ball reinforced Nylon 6 for injection molding.Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
| Tensile Strength at Break | <= 75.0 MPa | <= 10900 psi | ISO/R527 |
| Polykemi AB SCANMID 6 B11^ Nylon 6 Information provided by Polykemi AB |
|||
| Tensile Strength at Break | >= 75.0 MPa | >= 10900 psi | 50 mm/min; ISO 527-1,2 |
| Qualchem Danamid AFGFS2HUV30 Polyamide 66, 30% Glass Fiber Reinforced with glass fiber. Impact modified, heat and UV stabilized, for long-lasting use at 120-140°C, resistant to artificial lights.Information provided by Qualchem Zrt. |
|||
| Tensile Strength at Break | 75.0 - 100 MPa @Temperature 23.0 °C |
10900 - 14500 psi @Temperature 73.4 °F |
ISO 527-2/5 |
| PolyOne Bergadur™ PB400 G30 UF UV Polybutylene Terephthalate (PBT) Information provided by PolyOne |
|||
| Tensile Strength at Break | 75.0 MPa | 10900 psi | ASTM D 638 |
| SABIC Innovative Plastics LNP Lubricomp DFL329EF PC LNP LUBRICOMP* DFL329EF is a compound based on Polycarbonate resin containing Flame Retardant, Glass Fiber, PTFE. Added features of this material include: Flame Retardant.This data was supplied by .. |
|||
| Tensile Strength at Break | <= 75.0 MPa | <= 10900 psi | ISO/R527 |
| Polykemi AB POLYfill PPH GF8030 PB Polypropylene Homopolymer, Glass Fibre-Reinforced, Chemically Coupled Information provided by Polykemi AB |
|||
| Tensile Strength at Break | 75.0 MPa | 10900 psi | ISO 527 |
| Gharda Chemicals GAFONE™-S 1300 PSU, High Thermal Stability
(discontinued **) High viscosity granules for extrusion and injection molding.Characteristics: Good dielectric propertiesHigh mechanical strengthGood dimensional stabilityGood oxidative stabilityInherent flame retard.. |
|||
| Tensile Strength at Break | 75.0 MPa | 10900 psi | ISO 527-1/-2 |
| DSM Akulon® S224-KMV7 Nylon 66-35% Mineral Reinforced (European and Asian Grade) (Dry)
(discontinued **) The Akulon® product portfolio is engineered for optimum performance to suit different processing techniques and end use markets. Akulon Nylon 6 is used for extrusion applications including barrier .. |
|||
| Tensile Strength at Break | 75.0 MPa | 10900 psi | Sample Type 1B, 50mm/min; ISO 527-1/2:1993 |
| Global EPP PA 6C OFN Cast Polyamide 6 + Blended Liquid Lubricant Cast nylons are generally accepted as the primary engineering polymer, suitable for virtually any plain bearing application. By varying the conditions of polymerisation the mechanical properties of .. |
|||
| Tensile Strength at Break | 75.0 MPa | 10900 psi | ISO 527 |
| Grupo Repol Dinalon® A1S25 H PA66 Heat Stabilized Mechanical properties for Dry As Molded samplesInformation provided by Grupo Repol |
|||
| Tensile Strength at Break | 75.0 MPa | 10900 psi | ISO 527 |
| Grupo Repol Dinalon® A1X25 V0 PA66, V0 red phosphorus and halogen free Mechanical properties for Dry As Molded samplesInformation provided by Grupo Repol |
|||
| Tensile Strength at Break | 75.0 MPa | 10900 psi | Conditioned; ISO 527-1,-2 |
| Lanxess Durethan® BKV 230 H3.0 000000 Nylon 6-Copolymer, 30% Glass Fibers PA 6-Copolymer, 30% glass fibers, injection molding, impact modified, heat-ageing stabilized |
|||
| Tensile Strength at Break | 75.0 MPa | 10900 psi | Sample Type 1B, 50mm/min; ISO 527-1/2:1993 |
| Global EPP PA 612 Copolymer Cast Polyamide 612 Cast nylons are generally accepted as the primary engineering polymer, suitable for virtually any plain bearing application. By varying the conditions of polymerisation the mechanical properties of .. |
|||
| Tensile Strength at Break | 75.0 MPa | 10900 psi | |
| LATI Latigray 62-01 CX/75 PA 6 Radiopaque compound based on Polyamide 6 (PA6). Special mineral filler. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria T.. |
|||
| Tensile Strength at Break | 75.0 MPa | 10900 psi | |
| LATI Latilub 66-20ST PA66, Silicone/PTFE Filled Self-lubricating product based on Polyamide 66 (PA66). Silicone / PTFE. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria T.. |
|||
| Tensile Strength at Break | 75.0 MPa | 10900 psi | ISO 527 Type 1A |
| Solvay TECHNYL® A 222 Black 1N PA66, DRY Description: Unreinforced polyamide PA66, medium viscosity, heat stabilized, for injection molding, fast crystallization, for short cycles .Available in: EuropeProduct Applications: TECHNYL A 222 of.. |
|||
| Tensile Strength at Break | 75.0 MPa | 10900 psi | 50 mm/min; ISO 527 |
| SABIC Innovative Plastics ULTEM 9075 PEI (Europe-Africa-Middle East) High flow Polyetherimide blend. Meets FAR 25.853 and OSU 65/65 with low toxicity, smoke, and flame evolution. |
|||
| Tensile Strength at Break | 75.0 MPa | 10900 psi | ASTM D 638 |
| SABIC Innovative Plastics LNP Thermocomp IF002 PA 6/12 (Asia Pacific) LNP* Thermocomp* IF002 is a compound based on Nylon 6/12 resin containing Glass Fiber.This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
| Tensile Strength at Break | 75.0 MPa | 10900 psi | ISO 527 |
| Vyncolit X680 Novolac Phenolic Glass fiber and glass bead filled phenolic molding compound with excellent mechanical and thermal properties. Easily transformed into complex shapes. UL listed.USES: Complex precision parts with t.. |
|||
| Tensile Strength at Break | 75.0 MPa | 10900 psi | ISO 527-93 |
| Wellman Wellamid® NY1875-BK1 Nylon 66, Unfilled All information provided by Wellman Engineered Resins. |
|||
| Tensile Strength at Break | 75.0 MPa | 10900 psi | 5 [mm/min]; ISO 527-1/2 |
| Akro-Plastic Akromid® B3 GF 15 (2469) PA 6 Conditioned, 15% Glass Filled AKROMID® B (Polyamide 6) is an engineering compound, characterized by high mechanical strength, stiffness and thermal resistance. Furthermore, this polyamide offers high toughness at low temperatur.. |
|||
| Tensile Strength at Break | 75.0 MPa | 10900 psi | ISO 527-2 |
| Ascend Performance Materials Vydyne® 20NSP1 Nylon 66, DAM Availability:Asia PacificEuropeNorth AmericaFiller/Reinforcement:Glass Fiber, 43% Filler by Weight Additive:Nucleating AgentLubricant Features:Fast Molding CycleGeneral PurposeGood Mold Release Good.. |
|||
| Tensile Strength at Break | 75.0 MPa | 10900 psi | 0.2 in/min; ASTM Test |
| BASF Ultramid® 8202 HS PA6 (Dry) Ultramid 8202 HS is a heat stabilized, low viscosity, general purpose nylon 6 injection molding homopolymer. It possesses the combination of strength and toughness and has excellent chemical and ab.. |
|||
| Tensile Strength at Break | 75.0 MPa @Temperature 130 - 150 °C, Time 7.20e+7 sec |
10900 psi @Temperature 266 - 302 °F, Time 20000 hour |
5 [mm/min], 50% Loss of Tensile Strength; ICE 216 |
| Akro-Plastic Akromid® B3 GF 20 (2470) PA 6 Dry, 20% Glass Filled AKROMID® B (Polyamide 6) is an engineering compound, characterized by high mechanical strength, stiffness and thermal resistance. Furthermore, this polyamide offers high toughness at low temperatur.. |
|||
| Tensile Strength at Break | 75.0 MPa | 10900 psi | MD |
| BASF Ultramid® B36 LN 0.04 mm Cast Film Cold Chillroll Product comes in 2-2.5 mm round pellets.Information provided by BASF |
|||
| Tensile Strength at Break | 75.0 MPa | 10900 psi | 5mm/min; ISO 527-2/1A |
| Celanese Celcon® GC10 POM, 10% Glass Reinforced
(Unverified Data**) Celcon® GC10 acetal copolymer is a 10% glass reinforced acetal for improved strength and stiffness.10% glass fiber, has been replaced with Hostaform® C 9021 GV1/10Standard reciprocating screw inje.. |
|||
| Tensile Strength at Break | 75.0 MPa | 10900 psi | |
| LATI Latilub 88/50-20T PEEK, PTFE Filled Self-lubricating product based on Polyetheretherketone (PEEK). PTFE. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Ter.. |
|||
| Tensile Strength at Break | 75.0 MPa | 10900 psi | ISO 527-1/-2 |
| Styrolution Luran® 368 R Crystal Clear Transparent 77851 SAN Description: General-purpose grade with well-balanced properties, suitable for injection molding and extrusion. Especially for applications where highest transparency and low natural color is requir.. |
|||