DuPont Performance Polymers Sorona® MT3401 NC010 Polytrimethylene Terephthalate (PTT)  (Unverified Data**)

Category Polymer , Renewable/Recycled Polymer , Thermoplastic , Polyester, TP , Polytrimethylene Terephthalate (PTT)
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Sorona® MT3401 NC010 Polytrimethylene Terephthalate (PTT)  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Sorona® MT3401 NC010 is a medium toughened polytrimethylene terephthalate resin containing 29% renewably sourced ingredients by weight. It was initially coded SE38001.Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.23 g/cc
0.0444 lb/in³
ISO 1183
Water Absorption 0.080 %

@Temperature 23.0 °C
 0.080 %

@Temperature 73.4 °F
 Immersion 24h; ISO 62, Similar to
0.11 %

@Temperature 23.0 °C
 0.11 %

@Temperature 73.4 °F
 Equilibrium 50%RH; ISO 62, Similar to
0.34 %

@Temperature 23.0 °C
 0.34 %

@Temperature 73.4 °F
 Saturation, immersed; ISO 62, Similar to
Linear Mold Shrinkage, Flow 0.014 cm/cm

@Thickness 1.00 mm
 0.014 in/in

@Thickness 0.0394 in
 ISO 294-4
0.015 cm/cm

@Thickness 2.00 mm
 0.015 in/in

@Thickness 0.0787 in
 ISO 294-4
0.020 cm/cm

@Thickness 3.00 mm
 0.020 in/in

@Thickness 0.118 in
 ISO 294-4
Linear Mold Shrinkage, Transverse 0.014 cm/cm

@Thickness 1.00 mm
 0.014 in/in

@Thickness 0.0394 in
 ISO 294-4
0.017 cm/cm

@Thickness 2.00 mm
 0.017 in/in

@Thickness 0.0787 in
 ISO 294-4
0.021 cm/cm

@Thickness 3.00 mm
 0.021 in/in

@Thickness 0.118 in
 ISO 294-4
Mechanical Properties Metric English Comments
Tensile Strength, Yield 35.0 MPa

@Temperature 23.0 °C
 5080 psi

@Temperature 73.4 °F
 ISO 527
Elongation at Break 15 %

@Temperature 23.0 °C
 15 %

@Temperature 73.4 °F
 nominal; ISO 527
20 %

@Temperature 23.0 °C
 20 %

@Temperature 73.4 °F
 50mm/min; ISO 527
Elongation at Yield 5.0 %

@Temperature 23.0 °C
 5.0 %

@Temperature 73.4 °F
 ISO 527
Tensile Modulus 1.60 GPa

@Temperature 23.0 °C
 232 ksi

@Temperature 73.4 °F
 ISO 527
Flexural Modulus 1.60 GPa

@Temperature 23.0 °C
 232 ksi

@Temperature 73.4 °F
 ISO 178
Izod Impact, Notched (ISO) 18.0 kJ/m²

@Temperature 23.0 °C
 8.57 ft-lb/in²

@Temperature 73.4 °F
 ISO 180/1A
Charpy Impact, Notched 2.20 J/cm²

@Temperature 23.0 °C
 10.5 ft-lb/in²

@Temperature 73.4 °F
 ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 500 µm/m-°C

@Temperature 23.0 - 55.0 °C
 278 µin/in-°F

@Temperature 73.4 - 131 °F
 ISO 11359-1/-2
CTE, linear, Transverse to Flow 138 µm/m-°C

@Temperature 23.0 - 55.0 °C
 76.7 µin/in-°F

@Temperature 73.4 - 131 °F
 ISO 11359-1/-2
Melting Point 229 °C
444 °F
10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi) 75.0 °C
167 °F
ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 53.0 °C
127 °F
ISO 75-1/-2
Flammability, UL94 HB

@Thickness 1.50 mm
 HB

@Thickness 0.0591 in
 IEC 60695-11-10
HB

@Thickness 3.00 mm
 HB

@Thickness 0.118 in
 IEC 60695-11-10
HB

@Thickness 0.750 mm
 HB

@Thickness 0.0295 in
 IEC 60695-11-10
HB

@Thickness 0.750 mm
 HB

@Thickness 0.0295 in
 UL94
HB

@Thickness 1.50 mm
 HB

@Thickness 0.0591 in
 UL94
HB

@Thickness 3.00 mm
 HB

@Thickness 0.118 in
 UL94
Oxygen Index <= 20 %
<= 20 %
ISO 4589-1/-2
Glow Wire Test 650 °C

@Thickness 3.00 mm
 1200 °F

@Thickness 0.118 in
 IEC 60695-2-12
650 °C

@Thickness 1.50 mm
 1200 °F

@Thickness 0.0591 in
 IEC 60695-2-12
675 °C

@Thickness 1.00 mm
 1250 °F

@Thickness 0.0394 in
 IEC 60695-2-12
675 °C

@Thickness 3.00 mm
 1250 °F

@Thickness 0.118 in
 Ignition; IEC 60695-2-13
675 °C

@Thickness 1.50 mm
 1250 °F

@Thickness 0.0591 in
 Ignition; IEC 60695-2-13
700 °C

@Thickness 1.00 mm
 1290 °F

@Thickness 0.0394 in
 Ignition; IEC 60695-2-13
Electrical Properties Metric English Comments
Volume Resistivity 6.00e+16 ohm-cm

@Temperature 23.0 °C
 6.00e+16 ohm-cm

@Temperature 73.4 °F
 IEC 60093
Surface Resistance 6.00e+14 ohm

@Temperature 23.0 °C
 6.00e+14 ohm

@Temperature 73.4 °F
 IEC 60093
Dielectric Constant 3.4

@Frequency 1.00e+6 Hz,
Temperature 23.0 °C
 3.4

@Frequency 1.00e+6 Hz,
Temperature 73.4 °F
 IEC 60250
3.6

@Frequency 100 Hz,
Temperature 23.0 °C
 3.6

@Frequency 100 Hz,
Temperature 73.4 °F
 IEC 60250
3.6

@Frequency 1000 Hz,
Temperature 23.0 °C
 3.6

@Frequency 1000 Hz,
Temperature 73.4 °F
 IEC 60250
Dielectric Strength 23.0 kV/mm

@Thickness 2.00 mm,
Temperature 90.0 °C
 584 kV/in

@Thickness 0.0787 in,
Temperature 194 °F
 IEC 60243-1
24.0 kV/mm

@Thickness 2.00 mm,
Temperature 23.0 °C
 610 kV/in

@Thickness 0.0787 in,
Temperature 73.4 °F
 IEC 60243-1
32.0 kV/mm

@Thickness 1.00 mm,
Temperature 23.0 °C
 813 kV/in

@Thickness 0.0394 in,
Temperature 73.4 °F
 IEC 60243-1
32.0 kV/mm

@Thickness 1.00 mm,
Temperature 90.0 °C
 813 kV/in

@Thickness 0.0394 in,
Temperature 194 °F
 IEC 60243-1
Dissipation Factor 0.0020

@Frequency 100 Hz,
Temperature 23.0 °C
 0.0020

@Frequency 100 Hz,
Temperature 73.4 °F
 IEC 60250
0.0025

@Frequency 1000 Hz,
Temperature 23.0 °C
 0.0025

@Frequency 1000 Hz,
Temperature 73.4 °F
 IEC 60250
0.0205

@Frequency 1.00e+6 Hz,
Temperature 23.0 °C
 0.0205

@Frequency 1.00e+6 Hz,
Temperature 73.4 °F
 IEC 60250
Comparative Tracking Index 600 V

@Temperature 23.0 °C
 600 V

@Temperature 73.4 °F
 IEC 60112
Processing Properties Metric English Comments
Melt Temperature 260 °C
500 °F
Optimum
250 - 270 °C
482 - 518 °F
Mold Temperature 80.0 - 110 °C
176 - 230 °F
100 °C
212 °F
optimum
Drying Temperature 120 °C
248 °F
Dry Time 4.00 hour
4.00 hour
Moisture Content <= 0.020 %
<= 0.020 %
Descriptive Properties Value Comments
Additive Impact Modifier
Lubricant
Appearance Natural Color
Features Chemical Resistance, Good
Dimensional Stability, Good
Gloss, High
Moisture Absorption, Low
Renewable Resource Content
Strength, Good
Toughness, Good
Forms Pellets
Generic PTT
Material Status Preliminary Data
Part Marking Code >PTT-I<
ISO 11469
Polymer Family Polyester
Polymer Type PTT
Processing Method Injection Molding
Product Category Renewably Sourced Resins
Toughened Resins
Region Available - Global Yes
Resin Identification PTT-I
ISO 1043
RoHS Compliance Contact Manufacturer
Uses Automotive Applications
Consumer Applications
General Purpose
Industrial Applications
Parts, Engineering
Parts, Machine/Mechanical
Sporting Goods
Toys
Users viewing this material also viewed the following:
Copyright © lookpolymers.com All Rights Reserved