- Polymer Property : Tensile Modulus = 1.60 GPa
Polymer Property : Tensile Modulus = 1.60 GPa Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Modulus | 1.60 GPa | 232 ksi | ASTM D638 |
| NCMT NanoPAC™ N12 High Performance Polypropylene Nanocomposite Characteristics: Less shrinkage Solved distortion problem Good balance in impact and stiffness High gloss Reduce production cycleApplications: Household Industry Toys IndustryInformation provided by.. |
|||
| Tensile Modulus | 1.60 GPa | 232 ksi | 50 mm/min; ASTM D638 |
| Ovation Polymers Nima™ NH PC143P Polycarbonate Non-Hal FR-PC with High impact and improved processabilityAll properties after 48hrs conditioning at 23°C/50% RH |
|||
| Tensile Modulus | 1.60 GPa | 232 ksi | ISO 527-1,2 |
| Qualchem Danamid FES-21 Polyamide 6 Impact resistant, dryInformation provided by Qualchem Zrt. |
|||
| Tensile Modulus | 1.60 GPa @Thickness 0.100 mm |
232 ksi @Thickness 0.00394 in |
MD; ISO 527 |
| Victrex® APTIV® 2000-050 Polyetheretherketone (PEEK) Polymer Film, Amorphous APTIV PEEK 2000 series films are the unfilled amorphous films made from VICTREX® PEEK polymer. The film provides a material solution for engineers in ultra-high performance applications.APTIV PEEK .. |
|||
| Tensile Modulus | 1.60 GPa @Thickness 0.100 mm |
232 ksi @Thickness 0.00394 in |
TD; ISO 527 |
| Victrex® APTIV® 2000-050 Polyetheretherketone (PEEK) Polymer Film, Amorphous APTIV PEEK 2000 series films are the unfilled amorphous films made from VICTREX® PEEK polymer. The film provides a material solution for engineers in ultra-high performance applications.APTIV PEEK .. |
|||
| Tensile Modulus | 1.60 GPa | 232 ksi | 1mm/min |
| Eastman Tenite 130-33 Cellulose Acetate
(discontinued **) 33% Plasticized, contains 100% fiber grade ester.ISO data as provided by the manufacturer, Eastman Chemical. |
|||
| Tensile Modulus | 1.60 GPa | 232 ksi | ASTM D638 |
| Iran Petrochemical (PCC) HIPS 8350 High Impact Polystyrene HIPS 8350 is a very high impact polystyrene used in the extrusion industry. This grade has an improved environmental stress crack resistance (ESCR) in comparison with standard high impact polystyre.. |
|||
| Tensile Modulus | 1.60 GPa | 232 ksi | |
| LATI Latistat 45/7-02 HDPE Dissipative product based on High density polyethylene (HD-PE). Unfilled. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria.. |
|||
| Tensile Modulus | 1.60 GPa | 232 ksi | ISO 527 |
| Styrolution PS 2710 HIPS Styrolution PS 2710 is a high impact grade of polystyrene with improved stress crack resistance, developed for extrusion and thermoforming applications, especially for the refrigerator industry.Impr.. |
|||
| Tensile Modulus | 1.60 GPa | 232 ksi | 1mm/min; ISO 527 |
| Styrolution Terblend® N NM-19 ABS/PA6 (Conditioned) Terblend N NM-19 is a UV stabilized ABS/PA6 blend combining very high impact strength, even at low temperatures with an excellent processability and surface appearance.Information provided by STYROL.. |
|||
| Tensile Modulus | 1.60 GPa | 232 ksi | 1mm/min; ISO 527 |
| Styrolution Terblend® N NMX04 ABS/PA6 (Conditioned) Terblend N NMX04 is an ABS/PA6 blend specially developed for painted exterior applications, combining impact resistance with excellent processability and paintability.Information provided by STYROLU.. |
|||
| Tensile Modulus | 1.60 GPa | 232 ksi | 1 mm/min; ISO 527 |
| SABIC Innovative Plastics LNP THERMOTUF RN001IX4 PA 66 (Europe-Africa-Middle East) LNP* LUBRICOMP* RN001X4 is a compound based on PA 66 resin containing MoS2. Added features include: Internally Lubricated, High Impact, Heat Stabilized. |
|||
| Tensile Modulus | 1.60 GPa | 232 ksi | ISO 527-2 |
| Total PPC 7642 Polypropylene, Heterophasic Copolymer ATOFINA Propylene 7642 is a nucleated and antistatic heterophasic copolymer. PPC 7642 is characterized by a very high stiffness. |
|||
| Tensile Modulus | 1.60 GPa | 232 ksi | ISO 527-2 |
| Total PPC 9642 Polypropylene, Heterophasic Copolymer ATOFINA Propylene 9642 is nucleated heterophasic copolymer. PPC 9642 is characterized by improved stiffness, creep resistance, high impact resistance, excellent antistatic properties and has been f.. |
|||
| Tensile Modulus | 1.60 GPa | 232 ksi | ISO 527-2 |
| Total PPH 10060 Polypropylene, Homopolymer ATOFINA Polypropylene PPH 10060 homopolymer. PPH 10060 is characterized by high fluidity and is particularly suitable for injection molding applications. The material provides a good balance betwe.. |
|||
| Tensile Modulus | 1.60 GPa | 232 ksi | ISO 527-2 |
| Total PPM H350 Polypropylene, Homopolymer Medical Grade Polypropylene PPM H350 is a homopolymer with a Melt Flow Index of 35 g/10 min recommended for the manufacture of medical packaging and medical devices, to the exclusion of implants.Polypropylene PPM.. |
|||
| Tensile Modulus | 1.60 GPa | 232 ksi | ISO 527-2 |
| Total PPC 13442 Polypropylene, Heterophasic Copolymer ATOFINA Propylene 13442 is a nucleated antistatic heterophasic copolymer. PPC 13442 is characterized by very high fluidity with good mechanical properties. It has been formulated for excellent ant.. |
|||
| Tensile Modulus | 1.60 GPa | 232 ksi | dry; ISO 527-1/-2 |
| EMS-Grivory Grivory® TR 90 PAMACM12 Product description: Grilamid TR 90 natural is a high purity transparent thermoplastic polyamide, based on aliphatic and cycloaliphatic monomers. Grilamid TR 90 natural offers outstanding properties.. |
|||
| Tensile Modulus | 1.60 GPa | 232 ksi | dry; ISO 527-1/-2 |
| EMS-Grivory Grivory® TSZ 3 PA666 Product description: Grilon TSZ 3 is a heat stabilized, normal viscosity, high impact modified PA66 + PA6 injection molding grade. Grilon TSZ 3 has the following important properties: Excellent toug.. |
|||
| Tensile Modulus | 1.60 GPa | 232 ksi | ISO 527-1/-2 |
| DuPont Performance Polymers Crastin® BM6450XD BK560 Polybutylene Terephthalate (PBT)
(Unverified Data**)& Unreinforced Polybutylene Terephthalate Developed for Blow MoldingCrastin BM6450XD BK560 is an unreinforced supertough polybutylene terephthalate resin with very high viscosity for extrusion and blo.. |
|||
| Tensile Modulus | 1.60 GPa | 232 ksi | 1 mm/min; ISO 527 |
| Eurostar Starpylen MK001AS PP, Mineral Filled, Injection Molding Starpylen MK001AS is a Mineral Filled Polypropylene Injection Molding ResinInformation provided by Eurostar. |
|||
| Tensile Modulus | 1.60 GPa | 232 ksi | dry; ISO 527-1/-2 |
| EMS-Grivory Grivory® L 25 H PA12 Product Description: Grilamid L 25 H is a high viscosity heat stabilized Polyamide 12 extrusion grade and is suitable for application requiring a long-term usage temperature of 100 - 120°C. The mai.. |
|||
| Tensile Modulus | 1.60 GPa | 232 ksi | 1 mm/min |
| Arkema Group Orgalloy® RS 76E101 Nylon 66 Alloy, Rigid Grade (Conditioned) RS 66 series, rigid polyamide 66 alloy: easy to process, chemical resistance (no known solvents) and low moisture absorption leading to stability of mechanical, electrical and dimensional properti.. |
|||
| Tensile Modulus | 1.60 GPa | 232 ksi | ASTM D638 |
| Aclo Accutech Polypropylene Homopolymer HP0334C20L1 Calcium Reinforced |
|||
| Tensile Modulus | 1.60 GPa | 232 ksi | ISO 527-2/1 |
| Cathay PA513 Renewable Engineering Polyamide Cathay engineering polyamides contain 26-100% renewably sourced material. Advantages: Operates at similar conditions to PA66; Suitable for injection, compounding and extrusion; Stable mechanical pr.. |
|||
| Tensile Modulus | 1.60 GPa | 232 ksi | ISO 527-2 |
| Ascend Performance Materials Vydyne® 21SPF Nylon 66, General Purpose, High Productivity, Conditioned Vydyne® 21SPF is general-purpose PA66 resin. Available in natural, it is designed principally for injection-molding fabrication. This grade offers a well-balanced combination of engineering propert.. |
|||
| Tensile Modulus | 1.60 GPa | 232 ksi | ISO 527-2 |
| Ascend Performance Materials Vydyne® 21SPF BLK Nylon 66, DAM Vydyne® 21SPF BLK is a, general-purpose PA66 resin used for extrusion-compounding. Available in black, it is designed principally for injection-molding fabrication. This grade offers a well-balance.. |
|||
| Tensile Modulus | 1.60 GPa | 232 ksi | |
| Radici Radilon® A 42 (cond.) Nylon 66 Radilon® A is a range of polyamide 66 (PA66) products obtained through the polymerization of hexamethylendiamine and adipic acid, and used for injection, extrusion and blow-molding.Information prov.. |
|||
| Tensile Modulus | 1.60 GPa | 232 ksi | ASTM D638 |
| Azdel SuperLite® SL551400-100 PP Resin Matrix / 55% Glass Fiber (6 mm Molded Thickness) AZDEL SuperLite® SL551400-100 is a low pressure, thermoformable, thermoplastic composite of polypropylene and long chopped glass fibers. Usually combined with outer layers as needed for the applic.. |
|||
| Tensile Modulus | 1.60 GPa | 232 ksi | ISO 527-1/-2 |
| Unitika BV2120 PA66, Flame Retardant, Conditioned Information provided by Unitika Ltd. |
|||