DuPont Performance Polymers Delrin® 100T NC010 Acetal Homopolymer  (Unverified Data**)

Category Polymer , Thermoplastic , Acetal (POM)
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Delrin® 100T NC010 Acetal Homopolymer  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Delrin® 100T NC010 is a toughened, high viscosity acetal homopolymer grade with high impact resistance.Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.37 g/cc
0.0495 lb/in³
ISO 1183
Water Absorption 0.30 %

@Temperature 23.0 °C
 0.30 %

@Temperature 73.4 °F
 Equilibrium 50%RH; ISO 62, Similar to
0.90 %

@Temperature 23.0 °C
 0.90 %

@Temperature 73.4 °F
 Saturation, immersed; ISO 62, Similar to
Linear Mold Shrinkage, Flow 0.021 cm/cm

@Thickness 2.00 mm
 0.021 in/in

@Thickness 0.0787 in
 ISO 294-4
Linear Mold Shrinkage, Transverse 0.019 cm/cm

@Thickness 2.00 mm
 0.019 in/in

@Thickness 0.0787 in
 ISO 294-4
Melt Flow 2.0 g/10 min

@Load 2.16 kg,
Temperature 190 °C
 2.0 g/10 min

@Load 4.76 lb,
Temperature 374 °F
 ISO 1133
Melt Index of Compound 2.0 g/10 min

@Load 2.16 kg,
Temperature 190 °C
 2.0 g/10 min

@Load 4.76 lb,
Temperature 374 °F
 cm3/10 min; ISO 1133
Mechanical Properties Metric English Comments
Hardness, Rockwell M 59
59
ISO 2039/2
Hardness, Rockwell R 113
113
ISO 2039/2
Tensile Stress 8.54 MPa

@Strain 1.63 %,
Temperature 90.0 °C
 1240 psi

@Strain 1.63 %,
Temperature 194 °F
 ISO 527
13.6 MPa

@Strain 3.26 %,
Temperature 90.0 °C
 1970 psi

@Strain 3.26 %,
Temperature 194 °F
 ISO 527
14.0 MPa

@Strain 2.00 %,
Temperature 60.0 °C
 2030 psi

@Strain 2.00 %,
Temperature 140 °F
 ISO 527
17.1 MPa

@Strain 4.89 %,
Temperature 90.0 °C
 2480 psi

@Strain 4.89 %,
Temperature 194 °F
 ISO 527
19.3 MPa

@Strain 6.52 %,
Temperature 90.0 °C
 2800 psi

@Strain 6.52 %,
Temperature 194 °F
 ISO 527
21.0 MPa

@Strain 8.14 %,
Temperature 90.0 °C
 3050 psi

@Strain 8.14 %,
Temperature 194 °F
 ISO 527
21.7 MPa

@Strain 4.00 %,
Temperature 60.0 °C
 3150 psi

@Strain 4.00 %,
Temperature 140 °F
 ISO 527
22.0 MPa

@Strain 1.90 %,
Temperature 40.0 °C
 3190 psi

@Strain 1.90 %,
Temperature 104 °F
 ISO 527
22.1 MPa

@Strain 9.78 %,
Temperature 90.0 °C
 3210 psi

@Strain 9.78 %,
Temperature 194 °F
 ISO 527
22.9 MPa

@Strain 11.41 %,
Temperature 90.0 °C
 3320 psi

@Strain 11.41 %,
Temperature 194 °F
 ISO 527
23.4 MPa

@Strain 13.04 %,
Temperature 90.0 °C
 3390 psi

@Strain 13.04 %,
Temperature 194 °F
 ISO 527
23.6 MPa

@Strain 14.67 %,
Temperature 90.0 °C
 3420 psi

@Strain 14.67 %,
Temperature 194 °F
 ISO 527
23.7 MPa

@Strain 16.29 %,
Temperature 90.0 °C
 3440 psi

@Strain 16.29 %,
Temperature 194 °F
 ISO 527
27.0 MPa

@Strain 6.00 %,
Temperature 60.0 °C
 3920 psi

@Strain 6.00 %,
Temperature 140 °F
 ISO 527
29.0 MPa

@Strain 2.54 %,
Temperature 23.0 °C
 4210 psi

@Strain 2.54 %,
Temperature 73.4 °F
 ISO 527
30.7 MPa

@Strain 8.00 %,
Temperature 60.0 °C
 4450 psi

@Strain 8.00 %,
Temperature 140 °F
 ISO 527
31.0 MPa

@Strain 3.80 %,
Temperature 40.0 °C
 4500 psi

@Strain 3.80 %,
Temperature 104 °F
 ISO 527
33.0 MPa

@Strain 10.0 %,
Temperature 60.0 °C
 4790 psi

@Strain 10.0 %,
Temperature 140 °F
 ISO 527
34.5 MPa

@Strain 12.0 %,
Temperature 60.0 °C
 5000 psi

@Strain 12.0 %,
Temperature 140 °F
 ISO 527
35.2 MPa

@Strain 14.0 %,
Temperature 60.0 °C
 5110 psi

@Strain 14.0 %,
Temperature 140 °F
 ISO 527
35.4 MPa

@Strain 16.0 %,
Temperature 60.0 °C
 5130 psi

@Strain 16.0 %,
Temperature 140 °F
 ISO 527
35.6 MPa

@Strain 18.0 %,
Temperature 60.0 °C
 5160 psi

@Strain 18.0 %,
Temperature 140 °F
 ISO 527
35.7 MPa

@Strain 20.0 %,
Temperature 60.0 °C
 5180 psi

@Strain 20.0 %,
Temperature 140 °F
 ISO 527
36.0 MPa

@Strain 2.64 %,
Temperature 0.000 °C
 5220 psi

@Strain 2.64 %,
Temperature 32.0 °F
 ISO 527
36.8 MPa

@Strain 5.70 %,
Temperature 40.0 °C
 5340 psi

@Strain 5.70 %,
Temperature 104 °F
 ISO 527
40.0 MPa

@Strain 7.60 %,
Temperature 40.0 °C
 5800 psi

@Strain 7.60 %,
Temperature 104 °F
 ISO 527
40.0 MPa

@Strain 2.31 %,
Temperature -20.0 °C
 5800 psi

@Strain 2.31 %,
Temperature -4.00 °F
 ISO 527
40.9 MPa

@Strain 5.08 %,
Temperature 23.0 °C
 5930 psi

@Strain 5.08 %,
Temperature 73.4 °F
 ISO 527
42.0 MPa

@Strain 9.50 %,
Temperature 40.0 °C
 6090 psi

@Strain 9.50 %,
Temperature 104 °F
 ISO 527
43.2 MPa

@Strain 11.4 %,
Temperature 40.0 °C
 6270 psi

@Strain 11.4 %,
Temperature 104 °F
 ISO 527
44.0 MPa

@Strain 13.3 %,
Temperature 40.0 °C
 6380 psi

@Strain 13.3 %,
Temperature 104 °F
 ISO 527
44.5 MPa

@Strain 15.2 %,
Temperature 40.0 °C
 6450 psi

@Strain 15.2 %,
Temperature 104 °F
 ISO 527
44.6 MPa

@Strain 17.1 %,
Temperature 40.0 °C
 6470 psi

@Strain 17.1 %,
Temperature 104 °F
 ISO 527
44.7 MPa

@Strain 21.0 %,
Temperature 40.0 °C
 6480 psi

@Strain 21.0 %,
Temperature 104 °F
 ISO 527
46.32 MPa

@Strain 7.62 %,
Temperature 23.0 °C
 6718 psi

@Strain 7.62 %,
Temperature 73.4 °F
 ISO 527
48.68 MPa

@Strain 10.16 %,
Temperature 23.0 °C
 7060 psi

@Strain 10.16 %,
Temperature 73.4 °F
 ISO 527
49.37 MPa

@Strain 5.28 %,
Temperature 0.000 °C
 7161 psi

@Strain 5.28 %,
Temperature 32.0 °F
 ISO 527
49.92 MPa

@Strain 12.7 %,
Temperature 23.0 °C
 7240 psi

@Strain 12.7 %,
Temperature 73.4 °F
 ISO 527
50.53 MPa

@Strain 15.24 %,
Temperature 23.0 °C
 7329 psi

@Strain 15.24 %,
Temperature 73.4 °F
 ISO 527
50.93 MPa

@Strain 17.77 %,
Temperature 23.0 °C
 7387 psi

@Strain 17.77 %,
Temperature 73.4 °F
 ISO 527
51.13 MPa

@Strain 20.32 %,
Temperature 23.0 °C
 7416 psi

@Strain 20.32 %,
Temperature 73.4 °F
 ISO 527
51.24 MPa

@Strain 22.86 %,
Temperature 23.0 °C
 7432 psi

@Strain 22.86 %,
Temperature 73.4 °F
 ISO 527
51.24 MPa

@Strain 25.4 %,
Temperature 23.0 °C
 7432 psi

@Strain 25.4 %,
Temperature 73.4 °F
 ISO 527
53.92 MPa

@Strain 7.92 %,
Temperature 0.000 °C
 7820 psi

@Strain 7.92 %,
Temperature 32.0 °F
 ISO 527
55.5 MPa

@Strain 4.62 %,
Temperature -20.0 °C
 8050 psi

@Strain 4.62 %,
Temperature -4.00 °F
 ISO 527
56.05 MPa

@Strain 10.56 %,
Temperature 0.000 °C
 8129 psi

@Strain 10.56 %,
Temperature 32.0 °F
 ISO 527
57.22 MPa

@Strain 13.2 %,
Temperature 0.000 °C
 8299 psi

@Strain 13.2 %,
Temperature 32.0 °F
 ISO 527
57.85 MPa

@Strain 15.84 %,
Temperature 0.000 °C
 8390 psi

@Strain 15.84 %,
Temperature 32.0 °F
 ISO 527
58.25 MPa

@Strain 18.48 %,
Temperature 0.000 °C
 8448 psi

@Strain 18.48 %,
Temperature 32.0 °F
 ISO 527
58.53 MPa

@Strain 21.12 %,
Temperature 0.000 °C
 8489 psi

@Strain 21.12 %,
Temperature 32.0 °F
 ISO 527
58.54 MPa

@Strain 23.76 %,
Temperature 0.000 °C
 8491 psi

@Strain 23.76 %,
Temperature 32.0 °F
 ISO 527
58.64 MPa

@Strain 26.4 %,
Temperature 0.000 °C
 8505 psi

@Strain 26.4 %,
Temperature 32.0 °F
 ISO 527
61.0 MPa

@Strain 6.93 %,
Temperature -20.0 °C
 8850 psi

@Strain 6.93 %,
Temperature -4.00 °F
 ISO 527
63.89 MPa

@Strain 9.24 %,
Temperature -20.0 °C
 9266 psi

@Strain 9.24 %,
Temperature -4.00 °F
 ISO 527
65.21 MPa

@Strain 11.54 %,
Temperature -20.0 °C
 9458 psi

@Strain 11.54 %,
Temperature -4.00 °F
 ISO 527
66.2 MPa

@Strain 13.85 %,
Temperature -20.0 °C
 9600 psi

@Strain 13.85 %,
Temperature -4.00 °F
 ISO 527
67.0 MPa

@Strain 16.16 %,
Temperature -20.0 °C
 9720 psi

@Strain 16.16 %,
Temperature -4.00 °F
 ISO 527
Users viewing this material also viewed the following: