DuPont Performance Polymers Crastin® SK601 NC010 Polybutylene Terephthalate (PBT)  (Unverified Data**)

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 10% Glass Fiber Filled
Manufacturer DuPont Performance Polymers
Trade Name Crastin®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Crastin® SK601 NC010 Polybutylene Terephthalate (PBT)  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
10% Glass Reinforced Polybutylene Terephthalate Crastin SK601 NC010 is a 10% glass fiber reinforced lubricated polybutylene terephthalate resin for injection molding.Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.19 g/cc
0.0430 lb/in³
1.37 g/cc
0.0495 lb/in³
ISO 1183
Water Absorption 0.40 %

@Thickness 2.00 mm
 0.40 %

@Thickness 0.0787 in
 Sim. to ISO 62
Moisture Absorption 0.200 %

@Thickness 2.00 mm
 0.200 %

@Thickness 0.0787 in
 Sim. to ISO 62
Viscosity 78230 cP

@Shear Rate 5000 1/s,
Temperature 260 °C
 78230 cP

@Shear Rate 5000 1/s,
Temperature 500 °F
 ISO 11403-1 -2
89660 cP

@Shear Rate 5000 1/s,
Temperature 250 °C
 89660 cP

@Shear Rate 5000 1/s,
Temperature 482 °F
 ISO 11403-1 -2
103700 cP

@Shear Rate 5000 1/s,
Temperature 240 °C
 103700 cP

@Shear Rate 5000 1/s,
Temperature 464 °F
 ISO 11403-1 -2
224100 cP

@Shear Rate 500 1/s,
Temperature 260 °C
 224100 cP

@Shear Rate 500 1/s,
Temperature 500 °F
 ISO 11403-1 -2
268600 cP

@Shear Rate 500 1/s,
Temperature 250 °C
 268600 cP

@Shear Rate 500 1/s,
Temperature 482 °F
 ISO 11403-1 -2
323100 cP

@Shear Rate 500 1/s,
Temperature 240 °C
 323100 cP

@Shear Rate 500 1/s,
Temperature 464 °F
 ISO 11403-1 -2
Viscosity Test 110 cm³/g
110 cm³/g
ISO 307 1157 1628
Linear Mold Shrinkage, Flow 0.0070 cm/cm
0.0070 in/in
ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.012 cm/cm
0.012 in/in
ISO 294-4 2577
Mechanical Properties Metric English Comments
Tensile Strength at Break 90.0 MPa
13100 psi
ISO 527-1/-2
Tensile Stress 3.06 MPa

@Strain 0.250 %,
Temperature 160 °C
 444 psi

@Strain 0.250 %,
Temperature 320 °F
 ISO 11403-1 -2
8.55 MPa

@Strain 0.250 %,
Temperature 40.0 °C
 1240 psi

@Strain 0.250 %,
Temperature 104 °F
 ISO 11403-1 -2
11.1 MPa

@Strain 0.250 %,
Temperature 23.0 °C
 1610 psi

@Strain 0.250 %,
Temperature 73.4 °F
 ISO 11403-1 -2
12.1 MPa

@Strain 0.250 %,
Temperature 0.000 °C
 1750 psi

@Strain 0.250 %,
Temperature 32.0 °F
 ISO 11403-1 -2
13.2 MPa

@Strain 0.250 %,
Temperature -20.0 °C
 1910 psi

@Strain 0.250 %,
Temperature -4.00 °F
 ISO 11403-1 -2
13.7 MPa

@Strain 0.250 %,
Temperature -40.0 °C
 1990 psi

@Strain 0.250 %,
Temperature -40.0 °F
 ISO 11403-1 -2
14.5 MPa

@Strain 1.50 %,
Temperature 160 °C
 2100 psi

@Strain 1.50 %,
Temperature 320 °F
 ISO 11403-1 -2
21.6 MPa

@Strain 3.00 %,
Temperature 160 °C
 3130 psi

@Strain 3.00 %,
Temperature 320 °F
 ISO 11403-1 -2
45.5 MPa

@Strain 1.50 %,
Temperature 40.0 °C
 6600 psi

@Strain 1.50 %,
Temperature 104 °F
 ISO 11403-1 -2
59.5 MPa

@Strain 1.50 %,
Temperature 23.0 °C
 8630 psi

@Strain 1.50 %,
Temperature 73.4 °F
 ISO 11403-1 -2
67.0 MPa

@Strain 3.00 %,
Temperature 40.0 °C
 9720 psi

@Strain 3.00 %,
Temperature 104 °F
 ISO 11403-1 -2
69.2 MPa

@Strain 1.50 %,
Temperature 0.000 °C
 10000 psi

@Strain 1.50 %,
Temperature 32.0 °F
 ISO 11403-1 -2
72.9 MPa

@Strain 1.50 %,
Temperature -20.0 °C
 10600 psi

@Strain 1.50 %,
Temperature -4.00 °F
 ISO 11403-1 -2
75.0 MPa

@Strain 1.50 %,
Temperature -40.0 °C
 10900 psi

@Strain 1.50 %,
Temperature -40.0 °F
 ISO 11403-1 -2
90.2 MPa

@Strain 3.00 %,
Temperature 23.0 °C
 13100 psi

@Strain 3.00 %,
Temperature 73.4 °F
 ISO 11403-1 -2
10.0 MPa

@Strain 0.270 %,
Time 36000 sec
 1450 psi

@Strain 0.270 %,
Time 10.0 hour
 isochronous; ISO 11403-1 -2
10.0 MPa

@Strain 0.249 %,
Time 3600 sec
 1450 psi

@Strain 0.249 %,
Time 1.00 hour
 isochronous; ISO 11403-1 -2
10.0 MPa

@Strain 0.398 %,
Time 3.60e+6 sec
 1450 psi

@Strain 0.398 %,
Time 1000 hour
 isochronous; ISO 11403-1 -2
25.0 MPa

@Strain 0.730 %,
Time 360000 sec
 3630 psi

@Strain 0.730 %,
Time 100 hour
 isochronous; ISO 11403-1 -2
40.0 MPa

@Strain 1.75 %,
Time 3.60e+6 sec
 5800 psi

@Strain 1.75 %,
Time 1000 hour
 isochronous; ISO 11403-1 -2
40.0 MPa

@Strain 1.17 %,
Time 36000 sec
 5800 psi

@Strain 1.17 %,
Time 10.0 hour
 isochronous; ISO 11403-1 -2
50.0 MPa

@Time 3600 sec,
Strain 1.40 %
 7250 psi

@Time 1.00 hour,
Strain 1.40 %
 isochronous; ISO 11403-1 -2
60.0 MPa

@Strain 2.75 %,
Time 360000 sec
 8700 psi

@Strain 2.75 %,
Time 100 hour
 isochronous; ISO 11403-1 -2
Elongation at Break 4.7 %
4.7 %
ISO 527-1/-2
Tensile Modulus 4.50 GPa
653 ksi
ISO 527-1/-2
Flexural Strength 140 MPa
20300 psi
ISO 178
Shear Modulus 0.288 GPa

@Temperature 160 °C
 41.8 ksi

@Temperature 320 °F
 Dynamic; ISO 11403-1 -2
0.340 GPa

@Temperature 120 °C
 49.3 ksi

@Temperature 248 °F
 Dynamic; ISO 11403-1 -2
0.513 GPa

@Temperature 70.0 °C
 74.4 ksi

@Temperature 158 °F
 Dynamic; ISO 11403-1 -2
1.24 GPa

@Temperature 20.0 °C
 180 ksi

@Temperature 68.0 °F
 Dynamic; ISO 11403-1 -2
1.35 GPa

@Temperature -20.0 °C
 196 ksi

@Temperature -4.00 °F
 Dynamic; ISO 11403-1 -2
1.49 GPa

@Temperature -50.0 °C
 216 ksi

@Temperature -58.0 °F
 Dynamic; ISO 11403-1 -2
Secant Modulus 1.04 GPa

@Strain 3.50 %,
Temperature 100 °C
 151 ksi

@Strain 3.50 %,
Temperature 212 °F
 ISO 11403-1 -2
1.25 GPa

@Strain 3.50 %,
Temperature 80.0 °C
 181 ksi

@Strain 3.50 %,
Temperature 176 °F
 ISO 11403-1 -2
1.47 GPa

@Strain 1.50 %,
Temperature 100 °C
 213 ksi

@Strain 1.50 %,
Temperature 212 °F
 ISO 11403-1 -2
1.57 GPa

@Strain 1.50 %,
Temperature 80.0 °C
 227 ksi

@Strain 1.50 %,
Temperature 176 °F
 ISO 11403-1 -2
1.66 GPa

@Strain 0.250 %,
Temperature 100 °C
 241 ksi

@Strain 0.250 %,
Temperature 212 °F
 ISO 11403-1 -2
1.80 GPa

@Strain 0.250 %,
Temperature 80.0 °C
 261 ksi

@Strain 0.250 %,
Temperature 176 °F
 ISO 11403-1 -2
1.98 GPa

@Strain 3.50 %,
Temperature 40.0 °C
 287 ksi

@Strain 3.50 %,
Temperature 104 °F
 ISO 11403-1 -2
2.46 GPa

@Strain 3.70 %,
Temperature 23.0 °C
 357 ksi

@Strain 3.70 %,
Temperature 73.4 °F
 ISO 11403-1 -2
3.03 GPa

@Strain 1.50 %,
Temperature 40.0 °C
 440 ksi

@Strain 1.50 %,
Temperature 104 °F
 ISO 11403-1 -2
3.42 GPa

@Strain 0.250 %,
Temperature 40.0 °C
 496 ksi

@Strain 0.250 %,
Temperature 104 °F
 ISO 11403-1 -2
3.97 GPa

@Strain 1.50 %,
Temperature 23.0 °C
 575 ksi

@Strain 1.50 %,
Temperature 73.4 °F
 ISO 11403-1 -2
4.44 GPa

@Strain 0.250 %,
Temperature 23.0 °C
 644 ksi

@Strain 0.250 %,
Temperature 73.4 °F
 ISO 11403-1 -2
4.61 GPa

@Strain 1.50 %,
Temperature 0.000 °C
 669 ksi

@Strain 1.50 %,
Temperature 32.0 °F
 ISO 11403-1 -2
4.84 GPa

@Strain 0.250 %,
Temperature 0.000 °C
 702 ksi

@Strain 0.250 %,
Temperature 32.0 °F
 ISO 11403-1 -2
4.86 GPa

@Strain 1.50 %,
Temperature -20.0 °C
 705 ksi

@Strain 1.50 %,
Temperature -4.00 °F
 ISO 11403-1 -2
5.00 GPa

@Strain 1.50 %,
Temperature -40.0 °C
 725 ksi

@Strain 1.50 %,
Temperature -40.0 °F
 ISO 11403-1 -2
5.28 GPa

@Strain 0.250 %,
Temperature -20.0 °C
 766 ksi

@Strain 0.250 %,
Temperature -4.00 °F
 ISO 11403-1 -2
5.48 GPa

@Strain 0.250 %,
Temperature -40.0 °C
 795 ksi

@Strain 0.250 %,
Temperature -40.0 °F
 ISO 11403-1 -2
Izod Impact, Notched (ISO) 4.50 kJ/m²
2.14 ft-lb/in²
ISO 180/1A