Polymer Property : Tensile Stress = 2100 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Stress	14.5 MPa @Strain 100 %	2100 psi @Strain 100 %	ASTM D412
Polymax® Maxelast® P3897M TPE, PP Overmold or Standalone use Polymax's TPE material complies with UL, VDE, FDA, RoHS and PAH's standards.Uses:Consumer ProductsToys & NoveltiesAuto PartsTool Hand GripsSporting GoodsWire & Cable ElectronicsMedical DevicesPlasti..
Tensile Stress	14.5 MPa @Strain 1.50 %, Temperature 160 °C	2100 psi @Strain 1.50 %, Temperature 320 °F	ISO 11403-1 -2
DuPont Performance Polymers Crastin® SK601 NC010 Polybutylene Terephthalate (PBT) (Unverified Data**) 10% Glass Reinforced Polybutylene Terephthalate Crastin SK601 NC010 is a 10% glass fiber reinforced lubricated polybutylene terephthalate resin for injection molding.Information provided by DuPont P..
Tensile Stress	14.5 MPa @Strain 50.0 %	2100 psi @Strain 50.0 %	ISO 527-1/-2
DuPont Performance Polymers Hytrel® 5556 Polyester Elastomer TPC-ET (Unverified Data**) 55 Shore D High Performance Polyester ElastomerInformation provided by DuPont Performance Polymers
Tensile Stress	14.5 MPa @Strain 5.00 %, Temperature 120 °C	2100 psi @Strain 5.00 %, Temperature 248 °F	50%RH; ISO 527
DuPont Performance Polymers Zytel® E42A NC010 Nylon 66 (Unverified Data**) Zytel® E42A is a high viscosity polyamide 66 for injection molding and extrusion. It has improved break resistance for thick-walled parts.Information provided by DuPont Performance Polymers
Tensile Stress	14.48 MPa @Strain 1.00 %, Temperature 40.0 °C	2100 psi @Strain 1.00 %, Temperature 104 °F	ISO 11403-1 -2
DuPont Performance Polymers Crastin® ST830FRUV NC010 Polybutylene Terephthalate (PBT) (Unverified Data**) Unreinforced Flame Retardant UV Stabilized Polybutylene Terephthalate Crastin ST830FRUV NC010 is an unreinforced Super Tough flame retardant polybutylene terephthalate resin for injection molding. I..