Polymer Property : Tensile Stress = 13.7 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Stress	13.7 MPa @Strain 300 %	1990 psi @Strain 300 %	ASTM D412
Polymax® Maxelast® P3895 TPE, PP Overmold or Standalone use Polymax's TPE material complies with UL, VDE, FDA, RoHS and PAH's standards.Uses:Consumer ProductsToys & NoveltiesAuto PartsTool Hand GripsSporting GoodsWire & Cable ElectronicsMedical DevicesPlasti..
Tensile Stress	13.7 MPa @Strain 0.250 %, Temperature -40.0 °C	1990 psi @Strain 0.250 %, Temperature -40.0 °F	ISO 11403-1 -2
DuPont Performance Polymers Crastin® SK601 NC010 Polybutylene Terephthalate (PBT) (Unverified Data**) 10% Glass Reinforced Polybutylene Terephthalate Crastin SK601 NC010 is a 10% glass fiber reinforced lubricated polybutylene terephthalate resin for injection molding.Information provided by DuPont P..
Tensile Stress	13.7 MPa @Strain 100.15 %, Temperature 100 °C	1990 psi @Strain 100.15 %, Temperature 212 °F	TPE; ISO 11403-1 -2
DuPont Performance Polymers Hytrel® 8238 Polyester Elastomer TPC-ET (Unverified Data**) 82 Shore D Standard Performance Polyester ElastomerInformation provided by DuPont Performance Polymers
Tensile Stress	13.7 MPa @Strain 99.16 %, Temperature 90.0 °C	1990 psi @Strain 99.16 %, Temperature 194 °F	TPE; ISO 11403-1 -2
DuPont Performance Polymers Hytrel® HTR8441 BK316 Polyester Elastomer TPC-ET (Unverified Data**) 55 Shore D High Viscosity Polyester Elastomer Developed for Blow MoldingInformation provided by DuPont Performance Polymers
Tensile Stress	13.7 MPa @Strain 200 %, Temperature 23.0 °C	1990 psi @Strain 200 %, Temperature 73.4 °F	ISO 527 (1BA bar)
DuPont Performance Polymers Hytrel® HTR8636 NC010 TPC-ET (Unverified Data**) Hytrel® HTR8636 NC010 is a medium modulus Hytrel® grade with nominal durometer hardness of 40D. It contains non_discoloring stabilizer. It is specially suitable for extrusion processing.Informatio..