Dow DOWLEX™ IP-10262 High Density Polyethylene

Category Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Injection Molded
Manufacturer Dow Chemical
Trade Name DOWLEX™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Dow DOWLEX™ IP-10262 High Density Polyethylene.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
DOWLEX® IP-10262 resin is an improved processing high density polyethylene resin with controlled molecular weight distribution for use in reusable case applications including, poultry, fast food, automotive, retail, fresh produce, beverage (soft drinks), food service and chemicals and plastics. This U.V. stabilized version of DOWLEX IP-10 resin offers excellent processability due to its easy flow at low temperatures. This material complies with FDA regulation 21 CFR c 3.1 for food contact applications.Data provided by Dow Chemical.
Physical Properties Metric English Comments
Density 0.960 g/cc
0.0347 lb/in³
Viscosity 50000 cP

@Shear Rate 5000 1/s,
Temperature 190 °C
50000 cP

@Shear Rate 5000 1/s,
Temperature 374 °F
Apparent Dynamic Viscosity
82000 cP

@Shear Rate 1000 1/s,
Temperature 190 °C
82000 cP

@Shear Rate 1000 1/s,
Temperature 374 °F
Apparent Dynamic Viscosity
153000 cP

@Shear Rate 300 1/s,
Temperature 190 °C
153000 cP

@Shear Rate 300 1/s,
Temperature 374 °F
Apparent Dynamic Viscosity
Melt Flow 9.0 g/10 min

@Load 2.16 kg
9.0 g/10 min

@Load 4.76 lb
Melt flow ratio I10/I2 is 8.
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 14.0 MPa
2030 psi
Tensile Strength, Yield 21.0 MPa
3050 psi
Elongation at Break 680 %
680 %
Modulus of Elasticity 0.738 GPa
107 ksi
Molded Sample 2% Secant Modulus
Flexural Modulus 1.11 GPa
161 ksi
Izod Impact Resistance 5.90 J/cm²
28.1 ft-lb/in²
Thermal Properties Metric English Comments
Vicat Softening Point 127 °C
261 °F