Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 14.0 MPa | 2030 psi | |
3M Dyneon™ Fluorel™ FE-5840Q Fluoroelastomer VF2 + HFP + TFE Terpolymer
(discontinued **) Data provided by the manufacturer, Dyneon LLC.Incorporated cure polymer, 70.1%F in polymer with 22% Medium Thermal Carbon Black (N990), 2% MgO, and 4% Ca(OH)2. The FE series O-ring grades are the c.. |
|||
Tensile Strength, Ultimate | 14.0 MPa | 2030 psi | ASTM D638 |
Huntsman PE 1008 Film Extrusion Polyethylene
(discontinued **) Homopolymer, and FDA compliant.Features: Superior strength, good machinability, and heat seal characteristics.Applications: Film extrusion: industrial packaging, frozen food, produce bags, shrink, a.. |
|||
Tensile Strength, Ultimate | 14.0 MPa | 2030 psi | ASTM D638 |
Huntsman PE1031 Film Extrusion Polyethylene
(discontinued **) Homopolymer, and FDA compliant.Features: Superior strength, good machinability, and heat seal characteristics.Applications: Film extrusion: clarity packaging, frozen food, produce bags, shrink, bund.. |
|||
Tensile Strength, Ultimate | 14.0 MPa | 2030 psi | ASTM D638 |
Chevron Phillips HiD® 9706 HDPE Injection Molding Resin
(discontinued **) Resin Type: linear homopolymerCharacteristics: moderate flow, good impact strength, excellent stiffness, good ESCR, moderate shrinkage resistanceApplications: crates and totes, structural foamInform.. |
|||
Tensile Strength, Ultimate | 14.0 MPa | 2030 psi | ASTM D638 |
ExxonMobil Escorene® LD-767 High EVA Film and Compounding Resin
(discontinued **) Data provided by the manufacturer, Exxon Chemical.A low gel 29.5% vinyl acetate copolymer designed for film and compounding applications. The resin provides very low modulus films with high tensile.. |
|||
Tensile Strength, Ultimate | 14.0 - 51.0 MPa | 2030 - 7400 psi | Average value: 38.4 MPa Grade Count:15 |
Overview of materials for PVC, Powder This property data is a summary of similar materials in the MatWeb database for the category "PVC, Powder". Each property range of values reported is minimum and maximum values of appropriate MatWeb.. |
|||
Tensile Strength, Ultimate | 14.0 - 26.0 MPa | 2030 - 3770 psi | Average value: 18.9 MPa Grade Count:11 |
Overview of materials for Polypropylene, Mineral Reinforced, Impact Modified This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene, Mineral Reinforced, Impact Modified". Each property range of values reported is minimum a.. |
|||
Tensile Strength, Ultimate | 14.0 - 250 MPa @Temperature -40.0 - 250 °C |
2030 - 36300 psi @Temperature -40.0 - 482 °F |
Average value: 83.4 MPa Grade Count:3 |
Overview of materials for Liquid Crystal Polymer (LCP), 30% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Liquid Crystal Polymer (LCP), 30% Glass Fiber Filled". Specific grades with glass content between 25% an.. |
|||
Tensile Strength, Ultimate | 14.0 MPa | 2030 psi | IV, 2 in/min; ASTM D638 |
LyondellBasell Sequel® 1718 Engineered Polyolefin Data provided by Solvay Engineered Polymers.An engineered polyolefin designed for exterior painted automotive applications requiring dimensional stability over a broad temperature range. This mater.. |
|||
Tensile Strength, Ultimate | 14.0 MPa | 2030 psi | ASTM D638 |
LyondellBasell Astryn SZ021-2 Polypropylene Copolymer, 20% Talc Key Features: medium melt flow, medium modulus, mineral-filled, utility grade polypropylene copolymer, good impact and stiffness balance, versatileApplications: inner door panels and seat supportsDe.. |
|||
Tensile Strength, Ultimate | 14.0 MPa | 2030 psi | ISO R527-1 |
LyondellBasell Hifaxâ„¢ BB222GC Thermoplastic Olefin Resin Key Features: medium melt flow, very high modulus, UV-stabilized thermoplastic elastomeric olefin resin, excellent impact and stiffness balance, excellent weatherability, high stiffness, good dimens.. |
|||
Tensile Strength, Ultimate | 14.0 MPa | 2030 psi | DIN 53504 |
Lubrizol ESTANE® T4086 Ester Based Thermoplastic Polyurethane (European Grade) Description: Estane® thermoplastic polyurethanes (TPUs) include elastomeric materials that bridge the gap between flexible rubber and rigid plastics. These materials offer toughness and durability .. |
|||
Tensile Strength, Ultimate | 14.0 MPa | 2030 psi | Type IV, crosshead speed 2 in/min; ASTM D638 |
DuPont Elvax® 260 Ethylene-Vinyl Acetate Copolymer Resin Elvax resins offer a unique combination of processing and performance characteristics. They provide outstanding toughness and resilience and maintain flexibility over a broad temperature range with.. |
|||
Tensile Strength, Ultimate | 14.0 MPa | 2030 psi | butt tensile strength per ASTM D426 on brass |
Von Roll Isola IMI E-Solder® 3021 Electrically Conductive Adhesive Data provided by Von Roll Isola USA.E-SOLDER® epoxy based resin systems can be used at room temperature on heat sensitive materials, can bond dissimilar materials, and do not have flux or residue t.. |
|||
Tensile Strength, Ultimate | >= 14.0 MPa | >= 2030 psi | |
Von Roll Isola IMI Irrathene® 210 Irradiated Polyethylene Film, Encapsulation Grade Data provided by Von Roll Isola USA.Produced by electron bombardment of specially formulated polyethylene film used in a wide variety of electrical applications. Irrathene film is nonmelting and hi.. |
|||
Tensile Strength, Ultimate | 14.0 MPa @Time 605000 sec |
2030 psi @Time 168 hour |
Heat Aging; ASTM D 412/ASTM D 573 |
Zylog Neoplast® 180 HOFR Thermoplastic Vulcanizate Neoplast 180 HOFR is a flame retardant thermoplastic vulcanizate (TPV) compound, based on polyolefin chemistry, suitable for Injection Molding and Extrusion applications.RoHS Compliant, UV Stabilize.. |
|||
Tensile Strength, Ultimate | 14.0 MPa | 2030 psi | Type IV, crosshead speed 2 in/min; ASTM D638 |
DuPont Elvax® 550 Ethylene-Vinyl Acetate Copolymer Resin Elvax resins offer a unique combination of processing and performance characteristics. They provide outstanding toughness and resilience and maintain flexibility over a broad temperature range with.. |
|||
Tensile Strength, Ultimate | 14.0 MPa | 2030 psi | Type IV, crosshead speed 2 in/min; ASTM D638 |
DuPont Elvax® 750 Ethylene-Vinyl Acetate Copolymer Resin Elvax resins offer a unique combination of processing and performance characteristics. They provide outstanding toughness and resilience and maintain flexibility over a broad temperature range with.. |
|||
Tensile Strength, Ultimate | 14.0 MPa | 2030 psi | GB/T 528 |
Chengdu Polyster 8500 General Grade TPV Information provided by Chengdu Polyster Co., Ltd. |
|||
Tensile Strength, Ultimate | 14.0 MPa | 2030 psi | ISO 527-1 |
Chengdu Polyster H3030 Thermoplastic Polyether-ester Elastomer (TPEE) Information provided by Chengdu Polyster Co., Ltd. |
|||
Tensile Strength, Ultimate | 14.0 MPa | 2030 psi | ISO 527-1/-2 |
DSM Arnitel® PL381-H TPC-ET Injection Molding |
|||
Tensile Strength, Ultimate | 14.0 MPa | 2030 psi | |
Dow DOWLEX™ IP-10262 High Density Polyethylene DOWLEX® IP-10262 resin is an improved processing high density polyethylene resin with controlled molecular weight distribution for use in reusable case applications including, poultry, fast food, a.. |
|||
Tensile Strength, Ultimate | 14.0 MPa | 2030 psi | ASTM D638 |
A. Schulman ComAlloy Comtuf® 109 Polypropylene, Mineral Reinforced, Impact Modified Data provided by the manufacturer, ComAlloy International Company.40% Mineral Reinforced. Superior toughness and impact resistance characterize Comtuf® materialsThe ComAlloy product line has been i.. |
|||
Tensile Strength, Ultimate | 14.0 MPa | 2030 psi | ASTM D638 |
Huntsman PE6010 Blow Molding Polyethylene
(discontinued **) Homopolymer, Drug Master File listed product, complies with USP Classification VI, and FDA compliant.Features: Meets exacting requirements of blow molded containers and processes well with parison s.. |
|||
Tensile Strength, Ultimate | 14.0 MPa | 2030 psi | ASTM D638 |
Huntsman PE7011 Profile Extrusion Polyethylene
(discontinued **) Homopolymer and FDA compliant.Features: Excellent strength, good machinability, and foaming characteristics.Applications: Extrusion: profile extrusion.FDA Notes: Conforms to FDA regulation 21 CFR 17.. |
|||
Tensile Strength, Ultimate | 14.0 MPa | 2030 psi | ASTM D638 |
ExxonMobil Escorene® UL-7560 EVA Copolymer, Adhesive and Sealant Grade
(discontinued **) Data provided by the manufacturer, Exxon Chemical.An 18% vinyl acetate copolymerApplications: Hot melt adhesives; Wax blends; Industrial sealants. |
|||
Tensile Strength, Ultimate | 14.0 MPa | 2030 psi | ASTM D412-80 |
DuPont Performance Polymers Hypalon® 30 Chlorosulfonated Polyethylene Rubber, Mineral Filled Compound
(discon Mineral filled compound with 100 parts Hypalon; 80 parts hard clay; 4 parts magnesia; 30 parts aromatic process oil; 3 parts pentaerythritol; and 2 parts Tetrone® A rubber accelerator (from DuPont .. |
|||
Tensile Strength, Ultimate | 14.0 - 33.8 MPa | 2030 - 4900 psi | Average value: 26.2 MPa Grade Count:22 |
Overview of materials for Polypropylene with 30% Mica Filler This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene with 30% Mica Filler". Specific grades with primary filler content between 25% and 34% are.. |