Dow BETAMATE™ 5103-2 Epoxy

Category Polymer , Thermoset , Epoxy
Manufacturer Dow Chemical
Trade Name BETAMATE™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Dow BETAMATE™ 5103-2 Epoxy.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
BETAMATE™ 5103-2 is a one component heat curing Epoxy paste adhesive. The material is readily pumped at ambient temperatures. It shows excellent adhesion to automotive steel, including coated steels, is resistant to degradation and to substrate corrosion on environmental aging. The product is precurabel to induction and compatible with electro-coat paint process.Information provided by Dow
Physical Properties Metric English Comments
Density 1.45 - 1.51 g/cc
0.0524 - 0.0546 lb/in³
Solids Content >= 98 %
>= 98 %
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 51.0 MPa
7400 psi
DIN 53 504
Elongation at Break 1.3 %
1.3 %
DIN 53 504
Modulus of Elasticity 6.60 GPa
957 ksi
DIN 53 504
Adhesive Bond Strength 15.0 MPa

@Thickness 0.750 mm
2180 psi

@Thickness 0.0295 in
Lap Shear (CRS St 1203); EN 1465
20.0 MPa

@Thickness 1.50 mm
2900 psi

@Thickness 0.0591 in
Lap Shear (CRS St 1203); EN 1465
Peel Strength 2.00 kN/m
11.4 pli
T-Peel (CRS St 1203, 0.5mm)
3.40 kN/m
19.4 pli
Impact Peel
Thermal Properties Metric English Comments
Flash Point 245 °C
473 °F
Processing Properties Metric English Comments
Extrusion Rate 78.0 g/min
78.0 g/min
3 bar, 3mm aperture
Cure Time 30.0 min

@Temperature 180 °C
0.500 hour

@Temperature 356 °F