SABIC Innovative Plastics LNP THERMOCOMP DF002ER PC

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP THERMOCOMP
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP THERMOCOMP DF002ER PC.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP THERMOCOMP* DF002ER is a compound based on Polycarbonate resin containing 10% Glass Fiber. Added features of this material include: Easy Molding. Mold Release
Physical Properties Metric English Comments
Density 1.27 g/cc
0.0459 lb/in³
ISO 1183
1.275 g/cc
0.04606 lb/in³
ASTM D792
Moisture Absorption 0.150 %
0.150 %
50% RH, 24 hrs; ASTM D570
Linear Mold Shrinkage, Flow 0.0040 cm/cm

@Time 86400 sec
0.0040 in/in

@Time 24.0 hour
ASTM D955
0.0043 cm/cm

@Time 86400 sec
0.0043 in/in

@Time 24.0 hour
ISO 294
Linear Mold Shrinkage, Transverse 0.0050 cm/cm

@Time 86400 sec
0.0050 in/in

@Time 24.0 hour
ASTM D955
0.0051 cm/cm

@Time 86400 sec
0.0051 in/in

@Time 24.0 hour
ISO 294
Mechanical Properties Metric English Comments
Tensile Strength at Break 83.0 MPa
12000 psi
ASTM D638
84.0 MPa
12200 psi
ISO 527
Elongation at Break 3.6 %
3.6 %
ISO 527
3.8 %
3.8 %
ASTM D638
Tensile Modulus 4.10 GPa
595 ksi
1 mm/min; ISO 527
4.17 GPa
605 ksi
50 mm/min; ASTM D638
Flexural Strength 117 MPa
17000 psi
ISO 178
149 MPa
21600 psi
ASTM D790
Flexural Modulus 3.92 GPa
569 ksi
ISO 178
4.28 GPa
621 ksi
ASTM D790
Izod Impact, Notched 0.970 J/cm
1.82 ft-lb/in
ASTM D256
Izod Impact, Unnotched 9.29 J/cm
17.4 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 8.00 kJ/m²
3.81 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 61.0 kJ/m²
29.0 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 13.0 J
9.59 ft-lb
Instrumented Impact Energy @ peak; ASTM D3763
Impact Test 9.00 J
6.64 ft-lb
Multiaxial Impact; ISO 6603
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 38.1 µm/m-°C

@Temperature -40.0 - 40.0 °C
21.2 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
38.2 µm/m-°C

@Temperature -40.0 - 40.0 °C
21.2 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
CTE, linear, Transverse to Flow 53.4 µm/m-°C

@Temperature -40.0 - 40.0 °C
29.7 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
53.5 µm/m-°C

@Temperature -40.0 - 40.0 °C
29.7 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 141 °C
286 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
141 °C

@Thickness 3.20 mm
286 °F

@Thickness 0.126 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 137 °C
279 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
136 °C

@Thickness 3.20 mm
277 °F

@Thickness 0.126 in
unannealed; ASTM D648