BASF Ultramid® KR 4355 G5 25% Glass Filled PA6/6T (Conditioned)
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled |
| Manufacturer | BASF |
| Trade Name | Ultramid® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BASF Ultramid® KR 4355 G5 25% Glass Filled PA6/6T (Conditioned).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: 25% glass-fiber reinforced product for injection-molding; high toughness, strength and stiffness, low water absorption, high melting point (295°C [563°F]). The mechanical properties remain constant after moisture absorption up to a temperature of 60°C [140°F], for instance, for brush collars (electric motors).Information provided by BASF
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.500 - 0.800 g/cc | 0.0181 - 0.0289 lb/in³ | |
| Density | 1.35 g/cc | 0.0488 lb/in³ | ISO 1183 |
| Water Absorption | 5.0 - 6.0 % | 5.0 - 6.0 % | Saturation; ISO 62 |
| Moisture Absorption at Equilibrium | >= 1.3 % | >= 1.3 % | 50% RH; ISO 62 |
| 1.1 - 1.5 % | 1.1 - 1.5 % | 23°C; 50% RH; ISO 62 | |
| >= 5.5 % | >= 5.5 % | Saturation; ISO 62 | |
| Viscosity Measurement | 130 | 130 | ISO 307 |
| Linear Mold Shrinkage | 0.0039 cm/cm | 0.0039 in/in | restricted |
| Linear Mold Shrinkage, Flow | 0.0045 cm/cm | 0.0045 in/in | ISO 2577 |
| Linear Mold Shrinkage, Transverse | 0.010 cm/cm | 0.010 in/in | ISO 2577 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 170 MPa @Temperature 23.0 °C |
24700 psi @Temperature 73.4 °F |
50 mm/min; ISO 527-1/-2 |
| 203 MPa @Temperature -40.0 °C |
29400 psi @Temperature -40.0 °F |
ISO 527 | |
| Elongation at Yield | 3.0 % | 3.0 % | ISO 527 |
| Modulus of Elasticity | 9.00 GPa | 1310 ksi | ISO 527 |
| Tensile Creep Modulus, 1000 hours | 6500 MPa @Strain <=0.500 % |
943000 psi @Strain <=0.500 % |
ISO 899-1 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Heat Capacity | 1.40 J/g-°C | 0.335 BTU/lb-°F | |
| Thermal Conductivity | 0.250 W/m-K | 1.74 BTU-in/hr-ft²-°F | DIN 52612 |
| Melting Point | 295 °C | 563 °F | DIN 53765 |
| Maximum Service Temperature, Air | 135 °C | 275 °F | for 50% loss of tensile strength after 20000hr |
| 160 °C | 320 °F | for 50% loss of tensile strength after 5000hr | |
| 270 °C | 518 °F | ||
| Decomposition Temperature | >= 350 °C | >= 662 °F |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | IEC 60093 |
| Dielectric Constant | 4.5 @Frequency 1.00 Hz |
4.5 @Frequency 1.00 Hz |
IEC 60250 |
| Dielectric Strength | 31.0 kV/mm | 787 kV/in | IEC 60243-1 |
| Dissipation Factor | 0.040 @Frequency 1.00e+6 Hz |
0.040 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Comparative Tracking Index | 600 V | 600 V | Test solution A; IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Zone 1 | 300 °C | 572 °F | Feed Zone |
| Zone 2 | 310 °C | 590 °F | Compression |
| Zone 3 | 320 °C | 608 °F | Metering-zone |
| Zone 4 | 320 °C | 608 °F | Nozzle |
| Melt Temperature | 310 - 330 °C | 590 - 626 °F | Injection-molding/Extrusion |
| 320 °C | 608 °F | Optimal | |
| Mold Temperature | 80.0 - 120 °C | 176 - 248 °F | Injection-molding |
| 100 °C | 212 °F | Optimal | |
| Drying Temperature | 110 °C | 230 °F | |
| Dry Time | 8 hour | 8 hour | |
| Moisture Content | <= 0.030 % | <= 0.030 % | Optimal |
| <= 0.15 % | <= 0.15 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Commercial Status | Europe and North America | |
| Ignition Temperature | >470°C | ASTM D1929 |