- Aremco Corr-Paint™ CP2050-XX High Temperature Protective Coating Epoxy-Phenolic, Glass Fiber Filled
Aremco Corr-Paint™ CP2050-XX High Temperature Protective Coating Epoxy-Phenolic, Glass Fiber Filled
| Category | Ceramic , Other Engineering Material , Ceramic/Metallic Coating |
| Manufacturer | Aremco |
| Trade Name | Corr-Paint™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Aremco Corr-Paint™ CP2050-XX High Temperature Protective Coating Epoxy-Phenolic, Glass Fiber Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
This epoxy and urethane based coating is used for producing corrosion and wear resistant barriers to 500 °F. Typical applications include tanks, pipelines, boilers, precipitators, scrubbers, bag houses, cyclones, hoppers and other process equipment used in the power, pulp and paper, and chemical processing industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.60 g/cc | 1.60 g/cc | |
| Solids Content | 100 % | 100 % | weight |
| 100 % | 100 % | volume | |
| Volatile Organic Compounds (VOC) Content | 0.00 g/l | 0.00 g/l | |
| Thickness | >= 1270 microns | >= 50.0 mil | estimated wet film thickness |
| >= 1270 microns | >= 50.0 mil | recommended dry film thickness | |
| Storage Temperature | 4.44 - 32.2 °C | 40.0 - 90.0 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 86 | 86 | for Epoxy Coating |
| Elongation at Break | 3.0 % | 3.0 % | for Epoxy Coating |
| Flexural Strength | 92.4 MPa | 13400 psi | for Epoxy Coating |
| Compressive Strength | 71.0 MPa | 10300 psi | for Epoxy Coating |
| Adhesive Bond Strength | 2.07 MPa @Temperature 175 °C |
300 psi @Temperature 347 °F |
Lap Shear Strength vs. Aluminum |
| 6.21 MPa @Temperature 150 °C |
900 psi @Temperature 302 °F |
Lap Shear Strength vs. Aluminum | |
| 12.4 MPa @Temperature 100 °C |
1800 psi @Temperature 212 °F |
Lap Shear Strength vs. Aluminum | |
| 18.6 MPa @Temperature 25.0 °C |
2700 psi @Temperature 77.0 °F |
Lap Shear Strength vs. Aluminum |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 204 °C | 400 °F | |
| Flash Point | >= 93.3 °C | >= 200 °F |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 10.0 - 32.2 °C | 50.0 - 90.0 °F | Application Temperature |
| Dry Time | 6.00 - 8.00 hour | 6.00 - 8.00 hour | Touch |
| 12.0 - 14.0 hour | 12.0 - 14.0 hour | Handling | |
| 4.00 - 48.0 hour | 4.00 - 48.0 hour | Recoat | |
| Cure Time | 240 min @Temperature 79.4 °C |
4.00 hour @Temperature 175 °F |
>2 Hour Air Set Required Prior to Curing |
| 2880 min @Temperature 22.2 °C |
48.0 hour @Temperature 72.0 °F |
>2 Hour Air Set Required Prior to Curing | |
| Pot Life | 42.0 min @Temperature 23.0 °C |
42.0 min @Temperature 73.4 °F |
|
| Shelf Life | 12.0 Month @Temperature 23.0 °C |
12.0 Month @Temperature 73.4 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Brown-Red | |
| Dry Film Coverage ft2/gal | 1604 | at 1 mil |
| Mix Ratio | 1:1 | Epoxy:Phenolic |
| Mix Ratio By Weight | 1:1 | resin:activator |
| Mixed Viscosity | Paste | |
| Primer | Not Required or Recommended | |
| Thinner | Not Required or Recommended |