- Lanxess Durethan® AKV 15 H2.0 901510 Nylon 66, 15% Glass Fiber
Lanxess Durethan® AKV 15 H2.0 901510 Nylon 66, 15% Glass Fiber
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 20% Glass Fiber Filled |
| Manufacturer | Lanxess |
| Trade Name | Durethan® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lanxess Durethan® AKV 15 H2.0 901510 Nylon 66, 15% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PA 66, injection molding grade, 15% glass fibers, good heat-ageing resistance
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.23 g/cc | 0.0444 lb/in³ | ISO 1183 |
| Water Absorption | 7.0 % | 7.0 % | Test Sim. to ISO 62 |
| Moisture Absorption at Equilibrium | 2.4 % | 2.4 % | 23°C/50% R.H.; Test Sim. to ISO 62 |
| Viscosity Test | 146 cm³/g | 146 cm³/g | Viscosity number; ISO 307, 1157, 1628 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 90.0 MPa | 13100 psi | Conditioned; ISO 527-1/-2 |
| 125 MPa | 18100 psi | ISO 527-1/-2 | |
| Elongation at Break | 3.0 % | 3.0 % | ISO 527-1/-2 |
| 3.6 % | 3.6 % | Nominal; ISO 527-1/-2 | |
| 8.0 % | 8.0 % | Conditioned; ISO 527-1/-2 | |
| Tensile Modulus | 3.80 GPa | 551 ksi | Conditioned; ISO 527-1/-2 |
| 6.30 GPa | 914 ksi | ISO 527-1/-2 | |
| Charpy Impact Unnotched | 4.00 J/cm² @Temperature -30.0 °C |
19.0 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU |
| 4.00 J/cm² @Temperature -30.0 °C |
19.0 ft-lb/in² @Temperature -22.0 °F |
Conditioned; ISO 179/1eU | |
| 4.00 J/cm² @Temperature 23.0 °C |
19.0 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU | |
| 6.00 J/cm² @Temperature 23.0 °C |
28.6 ft-lb/in² @Temperature 73.4 °F |
Conditioned; ISO 179/1eU | |
| Charpy Impact, Notched | <= 1.00 J/cm² @Temperature -30.0 °C |
<= 4.76 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| <= 1.00 J/cm² @Temperature -30.0 °C |
<= 4.76 ft-lb/in² @Temperature -22.0 °F |
Conditioned; ISO 179/1eA | |
| <= 1.00 J/cm² @Temperature 23.0 °C |
<= 4.76 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA | |
| <= 1.00 J/cm² @Temperature 23.0 °C |
<= 4.76 ft-lb/in² @Temperature 73.4 °F |
Conditioned; ISO 179/1eA | |
| Impact | 610 | 610 | Puncture maximum force (N); ISO 6603-2 |
| 816 | 816 | Puncture maximum force, Conditioned (N); ISO 6603-2 | |
| 593 @Temperature -30.0 °C |
593 @Temperature -22.0 °F |
Puncture maximum force (N); ISO 6603-2 | |
| Puncture Energy | 1.70 J | 1.25 ft-lb | ISO 6603-2 |
| 2.10 J | 1.55 ft-lb | Conditioned; ISO 6603-2 | |
| 0.700 J @Temperature -30.0 °C |
0.516 ft-lb @Temperature -22.0 °F |
ISO 6603-2 | |
| 0.700 J @Temperature -30.0 °C |
0.516 ft-lb @Temperature -22.0 °F |
Conditioned; ISO 6603-2 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 40.0 µm/m-°C | 22.2 µin/in-°F | ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 90.0 µm/m-°C | 50.0 µin/in-°F | ISO 11359-1/-2 |
| Melting Point | 263 °C | 505 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 250 °C | 482 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | ISO 75-1/-2 |
| Deflection Temperature at 8.0 MPa | 70.0 °C | 158 °F | ISO 75-1/-2 |
| Vicat Softening Point | 230 °C | 446 °F | 50°C/h 50N; ISO 306 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
IEC 60695-11-10 |
| HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
IEC 60695-11-10 | |
| Oxygen Index | 24 % | 24 % | ISO 4589-1/-2 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | Conditioned; IEC 60093 |
| 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 | |
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | IEC 60093 |
| Dielectric Constant | 4.0 @Frequency 1.00e+6 Hz |
4.0 @Frequency 1.00e+6 Hz |
Conditioned; IEC 60250 |
| 4.0 @Frequency 1.00e+6 Hz |
4.0 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| 4.0 @Frequency 100 Hz |
4.0 @Frequency 100 Hz |
IEC 60250 | |
| 9.0 @Frequency 100 Hz |
9.0 @Frequency 100 Hz |
Conditioned; IEC 60250 | |
| Dielectric Strength | 35.0 kV/mm | 889 kV/in | IEC 60243-1 |
| 35.0 kV/mm | 889 kV/in | Conditioned; IEC 60243-1 | |
| Dissipation Factor | 0.0090 @Frequency 100 Hz |
0.0090 @Frequency 100 Hz |
IEC 60250 |
| 0.017 @Frequency 1.00e+6 Hz |
0.017 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| 0.070 @Frequency 1.00e+6 Hz |
0.070 @Frequency 1.00e+6 Hz |
Conditioned; IEC 60250 | |
| 0.22 @Frequency 100 Hz |
0.22 @Frequency 100 Hz |
Conditioned; IEC 60250 | |
| Comparative Tracking Index | 425 V | 425 V | IEC 60112 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Additives | Release agent | |
| Features | Heat stabilized or stable to heat | |
| Form | Pellets | |
| ISO Shortname | ISO 1874-PA 66,MHR,14-060,GF15 | |
| Processing | Injection molding | |
| Region | Asia Pacific | |
| Europe | ||
| Near East/Africa | ||
| North America | ||
| South and Central America |
Users viewing this material also viewed the following:
- Nilit FRIANYL B63 AL40 Nylon 6.6 for injection molding, 40% aluminum filled
- Permabond TA439 Toughened Acrylic Adhesive
- Westlake EMAC® SP2209 Specialty Copolymer (discontinued **)
- Huntsman IROGRAN® A 85 D 5001 Polyester-Based TPU-Injection Extrusion Grade
- Zeon Chemicals Nipol® 1072 Carboxylated Nitrile Elastomer
- ChevronTexaco FM Grease EP Aerosol
- Eagle Brass 101 OFE COPPER (Certified), 1/4 Hard
- AlphaGary Garathane™ X 96-320 B Polyurethane based compound
- Axiall 38901 Wire & Cable Flexible PVC
Copyright © lookpolymers.com All Rights Reserved