Solvay TECHNYL® A 60 G1 V25 PA66, 25% glass fiber, DRY

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled
Manufacturer Solvay
Trade Name Technyl®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay TECHNYL® A 60 G1 V25 PA66, 25% glass fiber, DRY.pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
Description: TECHNYL® A 60G1 V25 is a 25% GF reinforced organophosphorous flame retarded grade based on a patented high flow polyamide 66 resin. This product is heat stabilized and provides optimized injection molding performance. This product is available in natural, grey & black colors as standard and can be made in other specific colors upon request.Benefits: This product offers excellent flame retardancy properties (UL 94, 5VA, GWIT) combined with excellent processing, mechanical and electrical performance. It can withstand temperatures of 160°C for over 6000 hours and has a UL F1 rating for weatherability resistance.Available in: Asia Pacific, Europe, Latin America and North AmericaRegulations compliance: Grades produced or imported in Europe comply with directive 453/2010/EC, which amends REACH directive 1907/2006/EC. This grade complies with RoHS directive 2002/95/EC. Unless specified, this grade is not suitable for food contact, medical devices or toy applications.Applications: This product is ideally suited for industrial controls, power distribution or appliance applications such as MCBs and contactors. The long term thermal performance of this grade also make it ideal for under-the-bonnet Auto applications.Information provided by Rhodia, Rhodia has been acquired by Solvay.
Physical Properties Metric English Comments
Density 1.38 g/cc
0.0499 lb/in³
ISO 1183/A
Water Absorption 0.83 %

@Temperature 23.0 °C,
Time 86400 sec
 0.83 %

@Temperature 73.4 °F,
Time 24.0 hour
 ISO 62
Linear Mold Shrinkage 0.0050 cm/cm
0.0050 in/in
Isotropy
Linear Mold Shrinkage, Flow 0.0050 cm/cm
0.0050 in/in
Linear Mold Shrinkage, Transverse 0.0090 cm/cm
0.0090 in/in
Melt Flow 27 g/10 min

@Load 5.00 kg,
Temperature 275 °C
 27 g/10 min

@Load 11.0 lb,
Temperature 527 °F
 ISO/FDIS 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 130 MPa
18900 psi
ASTM D638
142 MPa
20600 psi
ISO 527 Type 1A
Tensile Stress 30.0 MPa

@Strain 1.00 %,
Temperature 140 °C
 4350 psi

@Strain 1.00 %,
Temperature 284 °F
37.0 MPa

@Strain 1.00 %,
Temperature 100 °C
 5370 psi

@Strain 1.00 %,
Temperature 212 °F
41.0 MPa

@Strain 2.00 %,
Temperature 140 °C
 5950 psi

@Strain 2.00 %,
Temperature 284 °F
45.0 MPa

@Strain 1.00 %,
Temperature 60.0 °C
 6530 psi

@Strain 1.00 %,
Temperature 140 °F
50.0 MPa

@Strain 4.00 %,
Temperature 140 °C
 7250 psi

@Strain 4.00 %,
Temperature 284 °F
60.0 MPa

@Strain 2.00 %,
Temperature 100 °C
 8700 psi

@Strain 2.00 %,
Temperature 212 °F
70.0 MPa

@Strain 4.00 %,
Temperature 100 °C
 10200 psi

@Strain 4.00 %,
Temperature 212 °F
80.0 MPa

@Strain 1.00 %,
Temperature -40.0 °C
 11600 psi

@Strain 1.00 %,
Temperature -40.0 °F
80.0 MPa

@Strain 1.00 %,
Temperature 23.0 °C
 11600 psi

@Strain 1.00 %,
Temperature 73.4 °F
80.0 MPa

@Strain 2.00 %,
Temperature 60.0 °C
 11600 psi

@Strain 2.00 %,
Temperature 140 °F
85.0 MPa

@Strain 4.00 %,
Temperature 60.0 °C
 12300 psi

@Strain 4.00 %,
Temperature 140 °F
122 MPa

@Strain 2.00 %,
Temperature 23.0 °C
 17700 psi

@Strain 2.00 %,
Temperature 73.4 °F
140 MPa

@Strain 2.00 %,
Temperature -40.0 °C
 20300 psi

@Strain 2.00 %,
Temperature -40.0 °F
Elongation at Break 2.0 %
2.0 %
ISO 527 Type 1A
2.8 %
2.8 %
ASTM D638
Tensile Modulus 9.50 GPa
1380 ksi
ISO 527 Type 1A
Flexural Strength 195 MPa
28300 psi
ASTM D790
Flexural Modulus 8.30 GPa
1200 ksi
ASTM D790
Izod Impact, Notched (ISO) 95.0 kJ/m²
45.2 ft-lb/in²
ISO 180/1eA
Charpy Impact Unnotched 6.00 J/cm²

@Temperature -30.0 °C
 28.6 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/1eU
6.50 J/cm²

@Temperature 23.0 °C
 30.9 ft-lb/in²

@Temperature 73.4 °F
 ISO 179/1eU
Charpy Impact, Notched 0.600 J/cm²
2.86 ft-lb/in²
ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 30.0 µm/m-°C

@Temperature 23.0 - 85.0 °C
 16.7 µin/in-°F

@Temperature 73.4 - 185 °F
 ISO 11359
Melting Point 262 °C
504 °F
ASTM D3417
263 °C
505 °F
ISO 11357
Deflection Temperature at 0.46 MPa (66 psi) 260 °C
500 °F
ISO 75/Bf
Deflection Temperature at 1.8 MPa (264 psi) 240 °C
464 °F
ISO 75/Af
246 °C
475 °F
ASTM D648
UL RTI, Electrical 65.0 °C

@Thickness 0.400 mm
 149 °F

@Thickness 0.0157 in
130 °C

@Thickness 0.800 mm
 266 °F

@Thickness 0.0315 in
130 °C

@Thickness 1.00 mm
 266 °F

@Thickness 0.0394 in
130 °C

@Thickness 1.50 mm
 266 °F

@Thickness 0.0591 in
130 °C

@Thickness 3.00 mm
 266 °F

@Thickness 0.118 in
UL RTI, Mechanical with Impact 65.0 °C

@Thickness 0.400 mm
 149 °F

@Thickness 0.0157 in
105 °C

@Thickness 0.800 mm
 221 °F

@Thickness 0.0315 in
105 °C

@Thickness 1.00 mm
 221 °F

@Thickness 0.0394 in
115 °C

@Thickness 1.50 mm
 239 °F

@Thickness 0.0591 in
115 °C

@Thickness 3.00 mm
 239 °F

@Thickness 0.118 in
Flammability, UL94 V-0

@Thickness 0.800 mm
 V-0

@Thickness 0.0315 in
 1210
V-0

@Thickness 1.60 mm
 V-0

@Thickness 0.0630 in
 1210
V-0

@Thickness 3.20 mm
 V-0

@Thickness 0.126 in
 1210
Oxygen Index 33 %
33 %
ISO 4589
Glow Wire Test 775 °C

@Thickness 1.60 mm
 1430 °F

@Thickness 0.0630 in
 ignition temperature; ISO 60695-2-13
775 °C

@Thickness 3.20 mm
 1430 °F

@Thickness 0.126 in
 ignition temperature; ISO 60695-2-13
960 °C

@Thickness 0.800 mm
 1760 °F

@Thickness 0.0315 in
 ISO 60695-2-12
960 °C

@Thickness 1.60 mm
 1760 °F

@Thickness 0.0630 in
 ISO 60695-2-12
960 °C

@Thickness 3.20 mm
 1760 °F

@Thickness 0.126 in
 ISO 60695-2-12
Electrical Properties Metric English Comments
Dielectric Strength 30.0 kV/mm
762 kV/in
IEC 60243
Comparative Tracking Index 550 V
550 V
Solution A; IEC 60112
Processing Properties Metric English Comments
Feed Temperature 260 - 275 °C
500 - 527 °F
Mold Temperature 60.0 - 80.0 °C
140 - 176 °F
Drying Temperature 80.0 °C
176 °F
Moisture Content <= 0.20 %
<= 0.20 %
Descriptive Properties Value Comments
Compression Zone 275-280°C
Mixing Zone 280-285°C