SABIC Innovative Plastics Lexan® FL933 PC
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Lexan® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Lexan® FL933 PC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Various weight reductions at 0.250"" wall. 30% GR. Superior flexural strength and modulus; good tensile strength. UV-stabilized.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.29 g/cc | 1.29 g/cc | foam molded; ASTM D792 |
| 1.43 g/cc | 1.43 g/cc | ASTM D792 | |
| Water Absorption | 0.12 % @Time 86400 sec |
0.12 % @Time 24.0 hour |
ASTM D570 |
| Moisture Absorption at Equilibrium | 0.26 % | 0.26 % | ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0040 cm/cm @Thickness 6.40 mm |
0.0020 - 0.0040 in/in @Thickness 0.252 in |
SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 72.0 MPa @Thickness 6.35 mm |
10400 psi @Thickness 0.250 in |
ASTM D638 |
| Elongation at Break | 3.0 % @Thickness 6.35 mm |
3.0 % @Thickness 0.250 in |
ASTM D638 |
| Tensile Modulus | 6.92 GPa @Thickness 6.40 mm |
1000 ksi @Thickness 0.252 in |
ASTM D638 |
| Flexural Yield Strength | 127 MPa | 18400 psi | 6.4 mm; ASTM D790 |
| Flexural Modulus | 6.89 GPa | 999 ksi | 6.4 mm; ASTM D790 |
| Izod Impact, Unnotched | 4.80 J/cm | 8.99 ft-lb/in | ASTM D4812 |
| Dart Drop, Total Energy | 40.0 J | 29.5 ft-lb | SABIC Method |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 21.6 µm/m-°C @Temperature -40.0 - 95.0 °C |
12.0 µin/in-°F @Temperature -40.0 - 203 °F |
ASTM E 831 |
| Specific Heat Capacity | 1.04 J/g-°C | 0.249 BTU/lb-°F | ASTM C351 |
| Thermal Conductivity | 0.160 W/m-K | 1.11 BTU-in/hr-ft²-°F | ASTM C177 |
| Deflection Temperature at 0.46 MPa (66 psi) | 143 °C @Thickness 6.40 mm |
289 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 138 °C @Thickness 6.40 mm |
280 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| Oxygen Index | 40.4 % | 40.4 % | ASTM D2863 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 2.40e+17 ohm-cm | 2.40e+17 ohm-cm | ASTM D257 |
| Surface Resistance | >= 1.10e+17 ohm | >= 1.10e+17 ohm | ASTM D257 |
| Dielectric Constant | 2.61 @Frequency 1.00e+6 Hz |
2.61 @Frequency 1.00e+6 Hz |
ASTM D150 |
| 2.7 @Frequency 100 Hz |
2.7 @Frequency 100 Hz |
ASTM D150 | |
| Dissipation Factor | 0.0034 @Frequency 100 Hz |
0.0034 @Frequency 100 Hz |
ASTM D150 |
| 0.0075 @Frequency 1.00e+6 Hz |
0.0075 @Frequency 1.00e+6 Hz |
ASTM D150 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| FOAM - ELECTRICAL 6.4 mm Wt Reduction | 20% | |
| FOAM - IMPACT 6.4 mm Wt Reduction | 10% | |
| FOAM - MECHANICAL 6.4 mm Wt Reduction | 10% | |
| FOAM - PHYSICAL 6.4mm Wt Reduction | 10% | |
| FOAM - THERMAL 6.4mm Wt Reduction | 10% |
Users viewing this material also viewed the following:
- NanoAmor 99%, OD/L: 40-60 nm/1-2 um Multi-Walled Carbon Nanotubes
- Nilit RECONYL A H Recycled nylon 6.6 for injection molding
- Polykemi AB SCANAMID 66 AL220L2M Nylon 66, Impact Modified
- Nilit FRIANYL B63 W-GV25 Nylon 6 for injection molding, 25% glass fiber reinforced
- LyondellBasell Alathon® L5332CP High Density Polyethylene
- Ferro EG 0225 Specialty Glass
- Special Metals INCONEL® 625LCF® Nickel Superalloy (UNS N06626) Annealed + 5% Cold Work
- ACC QM Skin 30 QSI Quantum Silicones 30 Durometer Condensation Cure moldmaking Material
- EMS-Grivory Grivory® BR 40 W PA6
Copyright © lookpolymers.com All Rights Reserved