SABIC Innovative Plastics NORYL GTX NX0031 PPE+PA
| Category | Polymer , Thermoplastic , Nylon , Polyphenylene Ether/PPO |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | NORYL GTX |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics NORYL GTX NX0031 PPE+PA.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
NORYL GTX* NX0031 resin is a conductive resin specially designed for electrostatic painting and powder coating applications. This material combines high impact, good flow and conductivity. The material is only available in black and is suitable for injection molding.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.09 g/cc | 1.09 g/cc | ASTM D792 |
| Density | 1.09 g/cc | 0.0394 lb/in³ | ISO 1183 |
| Moisture Absorption | 1.20 % | 1.20 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 4.2 % | 4.2 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.013 - 0.016 cm/cm @Thickness 3.20 mm |
0.013 - 0.016 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 8.0 g/10 min @Load 5.00 kg, Temperature 280 °C |
8.0 g/10 min @Load 11.0 lb, Temperature 536 °F |
ASTM D1238 |
| Melt Index of Compound | 8.0 g/10 min @Load 5.00 kg, Temperature 280 °C |
8.0 g/10 min @Load 11.0 lb, Temperature 536 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 48.0 MPa | 6960 psi | Type I, 50 mm/min; ASTM D638 |
| 48.0 MPa | 6960 psi | 50 mm/min; ISO 527 | |
| Tensile Strength, Yield | 50.0 MPa | 7250 psi | 50 mm/min; ISO 527 |
| 52.0 MPa | 7540 psi | Type I, 50 mm/min; ASTM D638 | |
| Elongation at Break | 30 % | 30 % | 50 mm/min; ISO 527 |
| 34 % | 34 % | Type I, 50 mm/min; ASTM D638 | |
| Elongation at Yield | 4.0 % | 4.0 % | 50 mm/min; ISO 527 |
| 5.0 % | 5.0 % | Type I, 50 mm/min; ASTM D638 | |
| Tensile Modulus | 2.00 GPa | 290 ksi | 1 mm/min; ISO 527 |
| 2.25 GPa | 326 ksi | 5 mm/min; ASTM D638 | |
| Flexural Yield Strength | 75.0 MPa | 10900 psi | 2 mm/min; ISO 178 |
| 79.0 MPa | 11500 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 1.90 GPa | 276 ksi | 2 mm/min; ISO 178 |
| 2.10 GPa | 305 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 2.24 J/cm | 4.20 ft-lb/in | ASTM D256 |
| 1.17 J/cm @Temperature -30.0 °C |
2.19 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| Izod Impact, Notched (ISO) | 20.0 kJ/m² | 9.52 ft-lb/in² | 80*10*4; ISO 180/1A |
| 10.0 kJ/m² @Temperature -30.0 °C |
4.76 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| Charpy Impact, Notched | 1.80 J/cm² | 8.57 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| 1.00 J/cm² @Temperature -30.0 °C |
4.76 ft-lb/in² @Temperature -22.0 °F |
Edgew 80*10*4 sp=62mm; ISO 179/1eA | |
| Dart Drop, Total Energy | 42.0 J @Temperature 23.0 °C |
31.0 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 100 µm/m-°C @Temperature -40.0 - 40.0 °C |
55.6 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 100 µm/m-°C @Temperature 23.0 - 60.0 °C |
55.6 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 90.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
50.0 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| 100 µm/m-°C @Temperature -40.0 - 40.0 °C |
55.6 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 176 °C @Thickness 3.20 mm |
349 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 136 °C @Thickness 3.20 mm |
277 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Vicat Softening Point | 175 °C | 347 °F | Rate B/50; ASTM D1525 |
| 175 °C | 347 °F | Rate B/50; ISO 306 | |
| 180 °C | 356 °F | Rate B/120; ISO 306 |
Users viewing this material also viewed the following:
- Teknor Apex Monprene® MP 1304 Thermoplastic Elastomer
- American Elements Tungsten Nanoparticles
- Polyram RamTough PZ307G6 Polycarbonate, 30% Glass Fiber, UV Stabilized
- A. Schulman SCHULAMID® 6 MV5 Unreinforced Nylon 6
- ChevronTexaco RPM® SAE 10W Heavy Duty Motor Oil
- ExxonMobil Label-Lyte™ 30LL666 OPP Film
- Arlon CP-594CX Bulk Compound
- Aaron Industries AAROLENE® ARPP 200-2 PP Black Polypropylene Copolymer
- SABIC Innovative Plastics Lexan® HF1110 PC (Asia Pacific)
Copyright © lookpolymers.com All Rights Reserved