Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 50.0 MPa | 7250 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics Cycoloy® C2100 PC+ABS (Europe-Africa-Middle East) CYCOLOY C2100 is a flame retardant blend, specifically developed to meet the stringent requirements of mains current carrying applications. CYCOLOY C2100 combinesThis data was supplied by SABIC-IP f.. |
|||
Tensile Strength, Yield | 50.0 MPa | 7250 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics Cycoloy® FXC630FE PC+ABS (Europe-Africa-Middle East) Multi purpose flame retarded PC+ABS injection moulding grade, suitable for those applications that require ferrite colour effects.This data was supplied by SABIC-IP for the Europe-Africa-Middle East.. |
|||
Tensile Strength, Yield | 50.0 MPa | 7250 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics Geloy FXTW30CP ASA Pearlescent GELOY ASA resin with copper-look for capstock extrusion. Outstanding weatherability.This data was supplied by SABIC-IP for the Americas region. |
|||
Tensile Strength, Yield | 50.0 MPa @Thickness 6.35 mm |
7250 psi @Thickness 0.250 in |
ASTM D638 |
SABIC Innovative Plastics Lexan® FL900 PC Lexan* resin FL900 is a Br- & Cl-free flame retardant grade that can be foamed for weight reductions. UL-94 V1 listed at 3.9mm together with good stiffness, heat, creep and impact performance make i.. |
|||
Tensile Strength, Yield | 50.0 - 70.0 MPa | 7250 - 10200 psi | Injection; ISO 527 |
Raschig Group SURAPLAST UPA 63 UP Glass fiber reinforced polyester molding compound. Minimal mold shrinkage and post-shrinkage, very good arc resistance, very good mechanical strength. This product meets the allowed upper limits for.. |
|||
Tensile Strength, Yield | 50.0 MPa | 7250 psi | ISO 527 |
GEHR Plastics PVDF Polyvinylidene Fluoride Polyvinylidene fluoride shows a higher tensile strength, pressure resistance and dimensional stability than the related PTFE, but friction and insulation properties are lower. PVDF has a high mechan.. |
|||
Tensile Strength, Yield | 50.0 MPa | 7250 psi | ISO 527-1/-2 |
Mitsubishi Xantar® C CM 406 FD C CM 406 Polycarbonate/ABS Blend (European Grade) Xantar® materials are engineered for performance, consistency and reliability. This makes Xantar® resins ideal for interior automotive components, electrical equipment and consumer appliances .. |
|||
Tensile Strength, Yield | 50.0 MPa | 7250 psi | ISO 527-1/-2 |
Lanxess Durethan® DP 2325 H3.0 000000 Nylon 66 PA 66, injection molding grade, non-reinforced, elastomer-modified, good heat-ageing resistance, extremely high notched impact strength even at dry state and at low temperatures |
|||
Tensile Strength, Yield | 50.0 MPa | 7250 psi | cond.; ISO 527-1, -2; 50 mm/min |
Lanxess Durethan® DP A 30 S FN30 DUS025 000000 Nylon 66 PA 66, non-reinforced, injection molding, halogen free flame retardant improved flowabilityInformation provided by LANXESS. |
|||
Tensile Strength, Yield | 50.0 MPa | 7250 psi | ISO 527-1/-2 |
Lanxess Durethan® DP BC 310 EF 000000 Nylon 6 PA 6, injection molding and extrusion grade, non-reinforced, elastomer modified, high impact strength, good flowability (Easy Flow) |
|||
Tensile Strength, Yield | 50.0 MPa | 7250 psi | Type I, 5 mm/min; ASTM D 638 |
SABIC Innovative Plastics Noryl V01505 PPE+HIPS Noryl* V01505 is a 15% milled fibre reinforced, injection moldable grade. Designed for good dimensional stability and low warpage, this resin also uses non-chlorinated, non-brominated FR additives t.. |
|||
Tensile Strength, Yield | 50.0 MPa | 7250 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Valox® 357X PBT (Europe-Africa-Middle East) VALOX 357X is an impact modified, flame retarted PBT+PC blend. Applications like bobbins, switches and enclosures. |
|||
Tensile Strength, Yield | 50.0 - 60.0 MPa @Thickness 2.00 mm |
7250 - 8700 psi @Thickness 0.0787 in |
50 mm/min; ASTM D638 |
Solvay Specialty Polymers Solef® 1006 Polyvinylidene Fluoride (PVDF) Solef® 1006 PVDF is a very low viscosity homopolymer resin mainly used in injection molding or in multifilament extrusion.Features: Homopolymer; Low ViscosityUses: General PurposeAdditional Prope.. |
|||
Tensile Strength, Yield | 50.0 MPa | 7250 psi | 5 mm/min; ASTM D638 |
Samsung Cheil Industries Starex® HG-0760LT ABS, Unreinforced Information provided by Samsung Cheil Industries. |
|||
Tensile Strength, Yield | 50.0 MPa | 7250 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP TF006 PU LNP THERMOCOMP TF006 is a compound based on Polyurethane containing 30% Glass Fiber. |
|||
Tensile Strength, Yield | 50.0 MPa | 7250 psi | ASTM-D638 |
Polyram PlusTek PA303G5 Nylon 6.6, 25% Glass Fiber 25% glass fiber reinforced, heat stabilized and hydrolysis resistant polyamide 6.6 for injection molding applicationsInformation provided by Polyram Ram On Ind. |
|||
Tensile Strength, Yield | 50.0 MPa @Strain 50.0 % |
7250 psi @Strain 50.0 % |
ISO 527 |
A. Schulman FORMION™ FI 131E Adhesive, Extrusion Grade DescriptionFormion® FI 131E is an adhesive grade extrusion product. It has been formulated to provide adhesion as a tie layer or resin modifier to bond Ionomer to polar and non polar substances, s.. |
|||
Tensile Strength, Yield | 50.0 MPa | 7250 psi | ASTM D638 |
Eastman Eastman 1223 Copolyester Applications:Blown filmCredit cardsDebit cardsDeodorant packagingElectronic packagingFabricated boxesFlexible packagingFood packagingFurniture/Furniture trimGaming cardsGift cardsIdentification card.. |
|||
Tensile Strength, Yield | 50.0 MPa | 7250 psi | dry; ISO 527-1/-2 |
DSM Akulon® Fuel Lock FL-LP PA6 Low fuel permeation PA6 suitable for use in injection molding/welding of small engine fuel tanks, UV stabilized |
|||
Tensile Strength, Yield | 50.0 MPa | 7250 psi | dry; ISO 527-1/-2 |
EMS-Grivory Grivory® L 20 G HL PA12 Product Description: Grilamid L 20 GHL is a, medium viscosity injection molding grade, based on Polyamide 12 (PA12). Grilamid L 20 GHL is UV-stabilized, and heat stabilized The special features of G.. |
|||
Tensile Strength, Yield | 50.0 MPa | 7250 psi | ISO 527 |
Eurotec® Tecoform® PO20 NL RT POM, PTFE modified, natural Information provided by Eurotec® |
|||
Tensile Strength, Yield | 50.0 MPa | 7250 psi | ASTM D638 |
Ashley Polymers Ashlene® 527LDS-B2 Nylon 66 A high impact lubricated nylon resin containing well dispersed carbon black for maximum resistance to weathering.Data provided by the manufacturer |
|||
Tensile Strength, Yield | 50.0 - 60.0 MPa | 7250 - 8700 psi | ISO 527 |
Beijing Ranger Chem BLUESTAR® 1084 PBT Can be used directly for spinning, and producing color concentrates. It can also be used for production after reinforcement & compounding.Information provided by Beijing Ranger Chemical Co. |
|||
Tensile Strength, Yield | 50.0 MPa | 7250 psi | 50 mm/min |
Arkema Group Kynar® 6000 HDC N 119 PVDF
(discontinued **) Designation ISO 12086-PVDF-E,GG1Z,Q.6E5.J.A.I.D, CD,Kynar PVDF are fluorinated thermoplastic homopolymers.Outstanding characteristics of Kynar: chemical resistance, imperviousness to UV, high barrie.. |
|||
Tensile Strength, Yield | 50.0 MPa | 7250 psi | ISO 527-1/-2 |
DSM Stanyl® TE350 Nylon 46 (European and Asian Grade) (Cond)
(discontinued **) Stanyl is a high performance polyamide providing unmatched performance and value across an amazingly broad range of automotive and electronic applications. Stanyl offers:Highest mechanical propertie.. |
|||
Tensile Strength, Yield | 50.0 MPa | 7250 psi | ASTM test; 50 mm/min. |
BASF Capron® 8360 HS 34% Mineral-Filled Nylon 6 (Conditioned)
(discontinued **) Capron 8360 HS is a heat stabilized 34% mineral reinforced nylon 6 injection molding resin possessing a high level of toughness and ductility combined with excellent processability and surface aesth.. |
|||
Tensile Strength, Yield | 50.0 - 70.0 MPa | 7250 - 10200 psi | Injection; ISO 527 |
Raschig Group MELOPLAS® 180 MF Wood flour-reinforced, phenol-modified MF molding compound (MPF) in dark colors. High surface hardness, good mechanical strength and electrical properties, good heat resistance. Self-extinguishing .. |