- Polykemi AB POLYblend 45FS GF20 PC/ABS-Blend, Glass Fiber reinforced
Polykemi AB POLYblend 45FS GF20 PC/ABS-Blend, Glass Fiber reinforced
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Glass Fiber Filled , Polycarbonate (PC) |
| Manufacturer | Polykemi AB |
| Trade Name | POLYblend |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polykemi AB POLYblend 45FS GF20 PC/ABS-Blend, Glass Fiber reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Polykemi AB
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.22 g/cc | 0.0441 lb/in³ | ISO 1183 |
| Filler Content | 20 % | 20 % | ±2%; Polykemi |
| Linear Mold Shrinkage | 0.0020 - 0.0040 cm/cm | 0.0020 - 0.0040 in/in | With Flow; ISO 2577 |
| 0.0020 - 0.0040 cm/cm | 0.0020 - 0.0040 in/in | Across Flow; ISO 2577 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | <= 45.0 MPa | <= 6530 psi | ISO/R527 |
| Elongation at Break | 5.0 % | 5.0 % | ISO/R527 |
| Flexural Strength | <= 75.0 MPa | <= 10900 psi | ISO 178 |
| Flexural Modulus | 3.50 GPa @Temperature 23.0 °C |
508 ksi @Temperature 73.4 °F |
ISO 178 |
| Charpy Impact, Notched | 0.600 J/cm² @Temperature 23.0 °C |
2.86 ft-lb/in² @Temperature 73.4 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 30.0 - 35.0 µm/m-°C | 16.7 - 19.4 µin/in-°F | Polykemi |
| Deflection Temperature at 0.46 MPa (66 psi) | 130 °C | 266 °F | 120°C/h; ISO 75/1 |
| Deflection Temperature at 1.8 MPa (264 psi) | 120 °C | 248 °F | 120°C/h; ISO 75/1 |
| Vicat Softening Point | 115 °C @Load 5.001 kg |
239 °F @Load 11.03 lb |
50°C/h; ISO 306 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 240 - 280 °C | 464 - 536 °F | |
| Mold Temperature | 70.0 - 100 °C | 158 - 212 °F | |
| Drying Temperature | 100 - 110 °C | 212 - 230 °F | |
| Dry Time | 2 - 8 hour | 2 - 8 hour | in circulation dryer |
| 2 - 8 hour | 2 - 8 hour | in fresh-air dryer | |
| 2 - 8 hour | 2 - 8 hour | in desiccant air dryer | |
| Injection Pressure | 90.0 - 150 MPa | 13100 - 21800 psi | |
| Back Pressure | 0.500 - 1.50 MPa | 72.5 - 218 psi |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Holding Pressure () | 20-50 | % of injection pressure |
| Injection Speed () | High |
Users viewing this material also viewed the following:
- Plastcom SLOVAMID 66/6 HI/1 PA66/6, improved strength
- Polimeri Europa Clearflex® CM 406 Hexene Copolymer Linear Low Density Polyethylene
- FKuR Kunststoff Terralene® LL 1101 Biobased Polyethylene
- Karina E 42/261-GEN Dark Red MBATCH (SP31543) for PVC
- Teknor Apex Sinpolene MBW1191 Linear Low Density Polyethylene
- Teknor Apex TEKRON® 4000-25 Thermoplastic Elastomer
- Braskem Idealis 500 High Molecular Weight Polyethylene Powder
- SABIC Innovative Plastics LNP LUBRICOMP DFL36E PC
- Kuraray SEPTON® A1 Hot Melt Adhesive
Copyright © lookpolymers.com All Rights Reserved