Polymer Property : Flexural Modulus = 2.10 GPa Product List

Mechanical Properties

Tips: 30 items are displayed at most.

Mechanical Properties	Metric	English	Comments
Flexural Modulus	2.10 GPa	305 ksi	ISO 178
Polyplastic Armlen® PP MF 40-4M Polypropylene Copolymer, 40% Calcium Carbonate High impact resistance at low temperatureInformation provided by PolyPlastic Group.
Flexural Modulus	2.10 GPa	305 ksi	2 mm/min; ISO 178
SABIC Innovative Plastics Lexan® EXL1330 PC Copolymer Lexan* EXL1330 polycarbonate (PC) siloxane copolymer resin is a UV stabilized opaque injection molding (IM) and sheet extrusion grade. This resin offers extreme low temperature (-60 C) ductility in ..
Flexural Modulus	2.10 GPa	305 ksi	ISO 178
SABIC Innovative Plastics LNP Colorcomp D10009 PC LNP* Colorcomp* D10009 is a compound based on Polycarbonate resin containing Flame Retardant, Unfilled Custom Color. Added features of this material include: Flame Retardant.This data was supplied ..
Flexural Modulus	2.10 GPa @Temperature 23.0 °C	305 ksi @Temperature 73.4 °F	ISO 178
Polykemi AB POLYform POM C M20 Polyoxymethylene Information provided by Polykemi AB
Flexural Modulus	2.10 - 2.10 GPa @Temperature 60.0 - 60.0 °C	305 - 305 ksi @Temperature 140 - 140 °F	Average value: 2.10 GPa Grade Count:1
Overview of materials for Acrylonitrile Butadiene Styrene (ABS), 20% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Acrylonitrile Butadiene Styrene (ABS), 20% Glass Fiber Filled". Specific grades with glass content betwe..
Flexural Modulus	2.10 GPa	305 ksi	ASTM D790
Custom Resins Duratel™ MF3 Acetal Copolymer  (discontinued **) Description: Duratel™ MF3 is a 2.5 melt flow, general purpose acetal copolymer. Information provided by Custom Resins.
Flexural Modulus	2.10 GPa	305 ksi	cond., 2 mm/min; ISO 178-A
Lanxess DurethanÂ® BKV 215 H2.0 DUS008 901510 Nylon 6, Impact Modified PA 6, 15% glass fibers, injection molding, impact modified, heat-aging stabilizedInformation provided by LANXESS.
Flexural Modulus	2.10 GPa	305 ksi	ASTM D790
SABIC Innovative Plastics LNP LUBRICOMP DL003P PC LNP LUBRICOMP* DL003P is a compound based on Polycarbonate resin containing 15% PTFE. Added features of this material include: Exceptional Processing, Internally Lubricated.
Flexural Modulus	2.10 GPa	305 ksi	ISO 178
SABIC Innovative Plastics LNP LUBRILOY D20009P PC LNP* LUBRILOY* D20009P is a compound based on Polycarbonate resin containing Proprietary Lubricant. Added features of this material include: Wear Resistant, Flame Retardant, Exceptional Processing...
Flexural Modulus	2.10 GPa	305 ksi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP STAT-KON CD000I PS LNP* Stat-kon* CD000I is a compound based on Polystyrene resin containing Carbon Powder. Added features of this material include: Electrically Conductive, High Impact.
Flexural Modulus	2.10 GPa	305 ksi	2 mm/min; ISO 178
SABIC Innovative Plastics ValoxÂ® 359 PBT (Europe-Africa-Middle East) VALOX 359 is an unreinforced, flame retarded, low warpage PBT injection moulding resin.
Flexural Modulus	2.10 GPa	305 ksi	2 mm/min; ISO 178
SABIC Innovative Plastics XYLEX X7503 PC+POLYESTER PC-Siloxane copolymer + Polyester alloy, High Impact, Transparent
Flexural Modulus	2.10 GPa	305 ksi	2 mm/min; ISO 178
SABIC Innovative Plastics XYLEX X7503 PC+POLYESTER (Asia Pacific) PC-Siloxane copolymer + Polyester alloy, High Impact, Transparent
Flexural Modulus	2.10 GPa	305 ksi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP THERMOCOMP C1000XXP PS (Europe-Africa-Middle East) LNP* THERMOCOMP* C1000XXP is a compound based on Polystyrene resin. Added features include: High Impact.
Flexural Modulus	2.10 GPa	305 ksi	ASTM D790
Styrolution Polystyrol 495 F GR 2 PS Description: Polystyrol 495 F is a high impact polystyrene with a good heat resistance and high stiffness.Applications: Consumer electronics; TV-front and back; chassis for VCR and CD player. Househ..
Flexural Modulus	2.10 GPa	305 ksi	2 mm/min; ISO 178
SABIC Innovative Plastics NORYL HH180 PPE+PS (Asia Pacific) Noryl* HH180 is a high heat, unfilled modified polyphenylene ether resin with a Vicat B/120 temperature of 185 deg C. Noryl HH180 is only available in color 80365.
Flexural Modulus	2.10 GPa	305 ksi	2 mm/min; ISO 178
SABIC Innovative Plastics ValoxÂ® V3004 PBT (Asia Pacific) Unfilled PBT modified with elastomer. Targeted for flexible hinge, automotive connectors, film applications.
Flexural Modulus	2.10 GPa	305 ksi	Tangent; ASTM D790
Plastics Group Polifil® RMC-30 30% Calcium Carbonate-Reinforced Polypropylene, High Impact Polifil® RMC series compounds are high impact polypropylenes reinforced with fine particle size calcium carbonate. In addition to the highest impact possible, they possess good stiffness, heat agin..
Flexural Modulus	2.10 GPa	305 ksi	1.3 mm/min, 50 mm span, method 1, tangent; ASTM D790
A. Schulman POLYFORT™ FTP 3130H-01/FTP 3130HU-Colors DescriptionPolyfort® FTP 3130H-01 (non-UV stabilized) and FTP 3130HU-Colors (UV-stabilized) are high flow injection molding polyolefin alloys which exhibit an exceptional stiffness-impact balance a..
Flexural Modulus	2.10 GPa	305 ksi	ASTM D790
Unitika FUN-8000 Characteristics: High impact strength High chemical resistance Transparency as high as polycarbonateInformation provided by Unitika Ltd.
Flexural Modulus	2.10 GPa	305 ksi	ASTM D790
Eastman Eastar MN211 Copolyester, Natural Eastar copolyesters are brilliantly clear polymers that have excellent impact strength, chemical resistance, dimensional stability, and low shrinkage rates. MN211 contains a mold release.Application..
Flexural Modulus	2.10 GPa	305 ksi	ASTM D790
Covestro Makrolon® DP 1-1456 Polycarbonate, Impact Grade Impact modified injection molding grade, extremely easy flow and easy mold release, for thin walled applications with long flow lengths.Information provided by Bayer.As of 1 September 2015, Bayer Ma..
Flexural Modulus	2.10 GPa	305 ksi	2mm/min; ISO 178
Denka TH-23 Transparent Resin Polymer (MBS resin) Polymethacrylate Butadiene Styrene "TX Polymer" (methyl methacrylate styrene), MS resins as an alternative to acrylic resins, with low density, low moisture absorption, and good moldability, "TH Polymer/TP Polymer," MBS resins with a..
Flexural Modulus	2.10 GPa	305 ksi	2 mm/min; ISO 178
Eurostar Starglas FX05032 PE Starglas FX05032 is Polyethylene Resin with a Proprietary Additive (foaming agent for polyolefins)Information provided by Eurostar.
Flexural Modulus	2.10 GPa	305 ksi	ISO Data
BASF Ultramid® 8260 HS BK-102 40% Mineral Filled PA6 (Conditioned) Ultramid 8260 HS BK-102 is a heat stabilized, pigmented black, 40% mineral reinforced PA6 injection molding resin. It possesses high stiffness, dimensional stability and heat resistance combined wi..
Flexural Modulus	2.10 GPa	305 ksi	2mm/min; ASTM D790
3M Dyneon™ PVDF 6012/0000 Polyvinylidene Fluoride 3M™ Dyneon™ PVDF 6012/0000 is ideal for multiple applications across a wide array of industries. Widely used in the chemical process industry, wire and cable industry, semiconductor industry, and ..
Flexural Modulus	2.10 GPa	305 ksi	ASTM D790
Ashley Polymers Ashlene® PPO 263 A general purpose grade with good heat resistance and impact strength. Other properties include dimensional stability and moisture resistance.Data provided by the manufacturer
Flexural Modulus	2.10 GPa	305 ksi	2 mm/min; ASTM D790
Solvay Specialty Polymers Solef® 1009 PVDF Homopolymer  (discontinued **) Key features of this grade: Mean Viscosity, All Purpose, Injection/Extrusion, Virgin. Recommended processing is extrusion. Available as powder & granules.General information about SOLEF® PVDF: SO..
Flexural Modulus	2.10 GPa @Temperature 23.0 °C	305 ksi @Temperature 73.4 °F	ISO 178
DuPont Performance Polymers Delrin® 300ATB BK000 Acetal Homopolymer  (Unverified Data**) Delrin® 300ATB BK000 is a filled, medium viscosity, toughened acetal homopolymer for injection molding. It is well suited for antistatic applications.Information provided by DuPont Performance Poly..