Polymer Property : Flexural Modulus = 305 ksi Product List

Mechanical Properties

Tips: 30 items are displayed at most.

Mechanical Properties	Metric	English	Comments
Flexural Modulus	2.10 GPa @Temperature 23.0 °C	305 ksi @Temperature 73.4 °F	ISO 178
Polykemi AB SCANAMID 66 A53^E Nylon 66, Modified Information provided by Polykemi AB
Flexural Modulus	2.10 GPa	305 ksi	1.3 mm/min, 50 mm span; ASTM D 790
SABIC Innovative Plastics Lexan® EXL1036 PC Copolymer (Europe-Africa-Middle East) Lexan* EXL1036 polycarbonate (PC) siloxane copolymer resin is a UV stabilized high viscosity grade designed for (co-)extrusion. This resin offers extreme low temperature (-60 C) ductility and good h..
Flexural Modulus	2.10 GPa	305 ksi	2 mm/min; ISO 178
SABIC Innovative Plastics Lexan® EXL1330 PC Copolymer (Asia Pacific) Lexan* EXL1330 polycarbonate (PC) siloxane copolymer resin is a UV stabilized opaque injection molding (IM) and sheet extrusion grade. This resin offers extreme low temperature (-60 C) ductility in ..
Flexural Modulus	2.10 GPa	305 ksi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics Lexan® EXL8483 PC COPOLYMER (Asia Pacific) Lexan* EXL8483 is a PC/siloxane copolymer resin with medium flow, excellent low temperature impact and 80% post consumer recycle content. Limited availability and restricted color only. Higher color..
Flexural Modulus	2.10 GPa	305 ksi	ASTM D790
Eastman Eastalloy MA510 Polymer  (discontinued **) Eastalloy MA510 Polymer is a clear copolyester/polycarbonate alloy. It affords the consumer excellent impact strength, chemical resistance, dimensional stability, low shrinkage rates and other enhan..
Flexural Modulus	2.10 GPa	305 ksi	ASTM D790
Solvay Specialty Polymers Amodel® AT-5001 Polyphthalamide (PPA) Resin, Dry as Molded  (discontinued **) AMODEL AT-5001 polyphthalamide resin is a neat ductile material that offers superior retention of properties after humid thermal aging, high impact at low temperature, and better mechanical properti..
Flexural Modulus	2.10 GPa @Temperature 23.0 °C	305 ksi @Temperature 73.4 °F	ISO 178
Polykemi AB POLYform POM C M20 Polyoxymethylene Information provided by Polykemi AB
Flexural Modulus	2.10 GPa	305 ksi	0.1 in/min; ASTM D790
Ineos Nova 8077 High Performance Styrenic Enhanced Polystyrene  (discontinued **) High flow, Special additives can be incorporate to improve properties such as coefficient of friction and static dissipation, Custom colorsApplications: Injection molding, Designed for thin wall app..
Flexural Modulus	2.10 GPa	305 ksi	2 mm/min; ISO 178
SABIC Innovative Plastics Lexan® EXL9134 PC Copolymer (Europe-Africa-Middle East) Lexan* EXL9134 polycarbonate (PC) siloxane copolymer resin is a UV stabilized high flow opaque injection molding (IM) grade. This resin offers UL94 V0 @ 1.5mm flame retardancy based on non-bromine, ..
Flexural Modulus	2.10 GPa	305 ksi	1.3 mm/min, 50 mm span; ASTM D 790
SABIC Innovative Plastics Lexan® FXD9810 PC Copolymer (Europe-Africa-Middle East) Non-chlorinated, non-brominated Flame retardant PC-siloxane copolymer blend. Excellent processability, super high flow, good impact, UL rated V-0. Limited translucent colors.This data was supplied b..
Flexural Modulus	2.10 GPa	305 ksi	2mm/min; ASTM D790
3M Dyneon™ PVDF 1012/1001 Polyvinylidene Fluoride  (discontinued **) High molecular weight grade PVDFPowder gradeExcellent chemical resistance to a wide variety of aggressive fluids and solventsGood permeation resistanceExcellent strength and dimensional stabilityInf..
Flexural Modulus	2.10 GPa	305 ksi	ASTM D790
Ineos Nova ZyntarÂ® 7000 Flame Retardant Polystyrene Features:General purpose workhorse resinGood flow for injection moldingUL94 V-0 @ 1.5 mm for all colors UL94 5VA rating FOAMED @ 4.6 mm, 0.87-1.07 g/cc density, natural colorCustom colors availableA..
Flexural Modulus	2.10 GPa	305 ksi
Lehmann & Voss LUVOCOMÂ® AC-80/TF/22/BK Polyacetal-copolymer, with PTFE Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Improved friction and wear behaviour. Emergency running property.Emergency running property, gl..
Flexural Modulus	2.10 GPa	305 ksi	1.3 mm/min, 50 mm span; ASTM D 790
SABIC Innovative Plastics Noryl PX6021 PPE+PS (Asia Pacific) Low heat, flame retardant PPO/HIPS alloy.This data was supplied by SABIC-IP for the Asia Pacific region.
Flexural Modulus	2.10 GPa	305 ksi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP LUBRICOMP KP004A Acetal Homopolymer (Europe-Africa-Middle East) LNP* LUBRICOMP* KP004A is a compound based on Acetal Homopolymer containing PTFE / Silicone. Added features include: Inernally Lubricated
Flexural Modulus	2.10 GPa	305 ksi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics ValoxÂ® IQ357U PBT+PC (Asia Pacific) Valox* Resin IQ357U: Environmentally responsible, low carbon footprint iQ* PBT + PC alloy. UL94 V-0 @0.63 mm. Impact modified and UV stabilized resin.
Flexural Modulus	2.10 GPa	305 ksi	ISO 178
Styrolution PS 495F HIPS Styrolution PS 495F is a high flow, high impact polystyrene with a good heat resistance and a high stiffness.High flow HIPSGood heat resistance with high stiffnessSuitable for gas-assisted injection..
Flexural Modulus	2.10 GPa	305 ksi	2 mm/min; ISO 178
SABIC Innovative Plastics NORYL PX1005X PPE+HIPS (Europe-Africa-Middle East) Noryl PX1005X is an unfilled, low heat resistance, halogen free (according VDE/DIN 472 part 813) flame retardant material.
Flexural Modulus	2.10 GPa	305 ksi	ASTM D790
Wanshijie PETG Sheet PETG is also named GPET. It is made of a kind of non-crystalline PET resin sourced from cyclohexanediol modification. PETG differs greatly from PET and PCT. PETG is a kind of non-crystalline copolym..
Flexural Modulus	2.10 GPa	305 ksi	ASTM-D790
Polyram RamShine PV507 ABS, Flame Retardant Flame retardant ABS for injection molding applicationsInformation provided by Polyram Ram On Ind.
Flexural Modulus	2.10 GPa	305 ksi	ASTM D790
Total PS CPDS 855S Chlorine and Bromine Free Flame Retardant High Impact Polystyrene Total Petrochemicals Polystyrene 855S is a chlorine and bromine free flame retardant high impact polystyrene with excellent thermal stability and processability for injection molding.Suitable Applic..
Flexural Modulus	2.10 GPa	305 ksi	1.3 mm/min, 50 mm span, method 1, tangent; ASTM D790
A. Schulman POLYFORT™ FTP 3130H-01/FTP 3130HU-Colors DescriptionPolyfort® FTP 3130H-01 (non-UV stabilized) and FTP 3130HU-Colors (UV-stabilized) are high flow injection molding polyolefin alloys which exhibit an exceptional stiffness-impact balance a..
Flexural Modulus	2.10 GPa	305 ksi	1.3 mm/min, 50 mm span, method 1, tangent; ASTM D790
A. Schulman POLYFORT™ FTP 3130H-01/FTP 3130HU-Colors DescriptionPolyfort® FTP 3130H-01 (non-UV stabilized) and FTP 3130HU-Colors (UV-stabilized) are high flow injection molding polyolefin alloys which exhibit an exceptional stiffness-impact balance a..
Flexural Modulus	2.10 GPa	305 ksi	1.3 mm/min, 50 mm span, method 1, tangent; ASTM D790
A. Schulman POLYFORT™ FTP 3130H-01/FTP 3130HU-Colors DescriptionPolyfort® FTP 3130H-01 (non-UV stabilized) and FTP 3130HU-Colors (UV-stabilized) are high flow injection molding polyolefin alloys which exhibit an exceptional stiffness-impact balance a..
Flexural Modulus	2.10 GPa	305 ksi	2mm/min; ISO 178
Denka MALECCA K-510 ABS A heat-resistant ABS resin based on "DENKA IP" – a Styrene-N-Phenylmaleimide copolymer. It has been designed as an easy-to-use resin by improving conventional heat-resistant ABS resins which had de..
Flexural Modulus	2.10 GPa	305 ksi	ASTM D790
Eastman Eastar GN046 Copolyester, Natural Eastar Copolyester GN046 is a very high melt strength copolyester targeted for extrusion blow molding applications. Blow molding of large parts (up to several pounds) are possible with this material..
Flexural Modulus	2.10 GPa	305 ksi	ISO 178
Eastman Eastar GN071 Natural PETG Copolyester EASTAR GN071 Copolyester is used for injection molding applications. It is sparkling clear, tough, chemical resistant, odor free, versatile, easy to work with and affordable. Cleaning solutions wi..
Flexural Modulus	2.10 GPa @Temperature 23.0 °C	305 ksi @Temperature 73.4 °F	ISO 178
Polykemi AB POLYfill PPHC T8020 Polypropylene, Mineral Reinforced Information provided by Polykemi AB
Flexural Modulus	2.10 GPa	305 ksi	ISO 178
Total Lacqrene® 740 High Impact Polystyrene  (discontinued **) LACQRENE® alpha 740 is a high gloss, high impact grade of polystyrene.ApplicationWhite goods (washing machines, driers), Toys and games, Garden equipment, All applications needing high gloss with g..
Flexural Modulus	2.10 GPa	305 ksi	ASTM D790A
BP Amoco Accpro® 9965 Enhanced Polypropylene  (discontinued **) Suggested fabrication methods: Injection moldingFeatures: NucleatedTypical applications: CompoundingComplies with FDA specification, Title 21, CFR 177.1520.Typical property data below from injection..