RheTech Products T40P250-00 40% Talc Reinforced Polypropylene Copolymer, Natural
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 40% Talc Filler |
| Manufacturer | RheTech Products |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | RheTech Products T40P250-00 40% Talc Reinforced Polypropylene Copolymer, Natural.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: BracketsHousingsInjection molding conditions reported in table.Information provided by RheTech Products.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.24 g/cc | 1.24 g/cc | 23/23°C; ASTM D792 |
| Filler Content | 40 % | 40 % | ASTM D5630 |
| Linear Mold Shrinkage | 0.0075 cm/cm | 0.0075 in/in | ASTM D955 |
| Melt Flow | 14 g/10 min @Load 2.16 kg, Temperature 230 °C |
14 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 70 | 70 | ASTM D2240 |
| Tensile Strength at Break | 22.8 MPa | 3300 psi | 2 in/min; ASTM D638 |
| Flexural Modulus | 2.96 GPa | 430 ksi | Tangent; ASTM D790 |
| Izod Impact, Notched | 0.320 J/cm @Temperature 23.0 °C |
0.600 ft-lb/in @Temperature 73.4 °F |
ASTM D256 |
| Gardner Impact | 2.03 J | 1.50 ft-lb | ASTM D5420 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 118 °C | 245 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 66.7 °C | 152 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 210 - 238 °C | 410 - 460 °F | |
| Middle Barrel Temperature | 216 - 243 °C | 420 - 470 °F | |
| Front Barrel Temperature | 221 - 249 °C | 430 - 480 °F | |
| Nozzle Temperature | 227 - 238 °C | 440 - 460 °F | |
| Mold Temperature | 26.7 - 48.9 °C | 80.0 - 120 °F | |
| Drying Temperature | 65.6 - 82.2 °C | 150 - 180 °F | |
| Dry Time | 1 - 2 hour | 1 - 2 hour | |
| Moisture Content | <= 0.050 % | <= 0.050 % | Recommended |
| Injection Pressure | 2.76 - 10.3 MPa | 400 - 1500 psi | |
| Hold Pressure | 2.07 - 8.27 MPa | 300 - 1200 psi | |
| Back Pressure | 0.345 - 1.03 MPa | 50.0 - 150 psi |
Users viewing this material also viewed the following:
- Huntsman KRYSTALFLEX® PE 499 Polyurethane Optical Aliphatic Film
- Lanxess Durethan® DP BKV 60 EF 000000 Nylon6, 60% Glass Fiber
- Seals Eastern 5487 Nitrile Rubber
- Solvay Specialty Polymers Ixef® 2030 Polyarylamide (PARA), 55% GlassMineral
- Wellman Wellamid® MR409 22H-NBK4 40% Mineral Reinforced Nylon 66
- A. Schulman PP 1404-01 Polypropylene High Impact Polypropylene
- A. Schulman INVISION™ VX-5065UI Soft Touch Polyolefin Thermoplastic
- A. Schulman PP 3490-01G Polypropylene Homopolymer Polypropylene
- ExxonMobil 32 Mobil DTE Excel Series
- Overview of materials for Polypropylene, Long Glass Fiber 50%
Copyright © lookpolymers.com All Rights Reserved