RheTech Products GC20P255-712UV 20% Glass Fiber Reinforced Polypropylene Copolymer, Chemically Coupled, UV Stabilized, B231 Earth Grey
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 20% Glass Fiber Filler |
| Manufacturer | RheTech Products |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | RheTech Products GC20P255-712UV 20% Glass Fiber Reinforced Polypropylene Copolymer, Chemically Coupled, UV Stabilized, B231 Earth Grey.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Consumer goodsMiscellaneous bracketsExterior componentsInjection molding conditions reported in table.Information provided by RheTech Products.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.05 g/cc | 1.05 g/cc | 23/23°C; ASTM D792 |
| Filler Content | 20 % | 20 % | ASTM D5630 |
| Linear Mold Shrinkage | 0.0020 cm/cm | 0.0020 in/in | ASTM D955 |
| Melt Flow | 10 g/10 min @Load 2.16 kg, Temperature 230 °C |
10 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 74 | 74 | ASTM D2240 |
| Tensile Strength at Break | 48.3 MPa | 7000 psi | 2 in/min; ASTM D638 |
| Flexural Modulus | 2.96 GPa | 430 ksi | Tangent; ASTM D790 |
| Izod Impact, Notched | 1.28 J/cm @Temperature 23.0 °C |
2.40 ft-lb/in @Temperature 73.4 °F |
ASTM D256 |
| Gardner Impact | 0.790 J | 0.583 ft-lb | ASTM D5420 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 153 °C | 307 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 126 °C | 258 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 199 - 227 °C | 390 - 440 °F | |
| Middle Barrel Temperature | 204 - 232 °C | 400 - 450 °F | |
| Front Barrel Temperature | 210 - 238 °C | 410 - 460 °F | |
| Nozzle Temperature | 216 - 227 °C | 420 - 440 °F | |
| Mold Temperature | 26.7 - 48.9 °C | 80.0 - 120 °F | |
| Drying Temperature | 65.6 - 82.2 °C | 150 - 180 °F | |
| Dry Time | 1 - 2 hour | 1 - 2 hour | |
| Moisture Content | <= 0.050 % | <= 0.050 % | Recommended |
| Injection Pressure | 2.76 - 10.3 MPa | 400 - 1500 psi | |
| Hold Pressure | 2.07 - 8.27 MPa | 300 - 1200 psi | |
| Back Pressure | 0.345 - 1.03 MPa | 50.0 - 150 psi |
Users viewing this material also viewed the following:
- Indium Corp. 1075-EX 30 VOC-Free Wave Solder Flux
- MetalTek MTEK 20 Cast UNS N08007 Super Austenitic Stainless Steel
- Karina 846-10/79-IS-RG White PVC Compound
- Latrobe Lescalloy® 4335+V VAC-ARC High Strength Alloy Steel
- Spartech Formalloy HG High-Gloss TPO Alloy Specialty Sheet
- Techmer ES Electrablend® PA6/6 03005 CF Carbon Filled
- SCG Chemicals EL-Leneâ„¢ H5814J High Density Polyethylene Injection Molding
- Denka VINYKON W5520 PVC, W grade for non-migratory sheath and special items
- Eurotec® Tecomid® NB40 GR30 NL IM PA6, 30% glass fiber reinforced, impact modified, natural
- Akro-Plastic Akromid® S3 GF 23 1 (2917) PA 6.10 Dry, 23% Glass Filled
Copyright © lookpolymers.com All Rights Reserved