- Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 307 °F
Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 307 °F Product List
Thermal PropertiesTips: 30 items are displayed at most.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) |
153
°C <br>@Thickness 6.35 mm
|
307
°F <br>@Thickness 0.250 in
|
Unannealed; ASTM D648 |
|
PolyOne LubriOne™ 5209 FPL 20 Natural Acetal (POM) Copolymer
LubriOne™ Lubricated and Wear-Resistant Compounds have been specifically formulated to be self-lubricating materials, offering low coefficient of friction and improved wear resistance properties. L..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
153
°C <br>@Thickness 6.35 mm
|
307
°F <br>@Thickness 0.250 in
|
Unannealed; ASTM D648 |
|
PolyOne LubriOne™ AT-000/05T 2S Acetal (POM) Copolymer
LubriOne™ Lubricated and Wear-Resistant Compounds have been specifically formulated to be self-lubricating materials, offering low coefficient of friction and improved wear resistance properties. L..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 153 °C | 307 °F | ASTM D648 |
|
RheTech Products GC20P255-00 20% Glass Fiber Reinforced Polypropylene Copolymer, Chemically Coupled, Natural
Applications: Underhood componentsElectrical housingsHeadlamp bracketsInjection molding conditions reported in table.Information provided by RheTech Products.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
153
°C <br>@Thickness 3.18 mm
|
307
°F <br>@Thickness 0.125 in
|
Unannealed; ASTM D648 |
|
PolyOne Stat-Tech™ AT-CB2/000 CR Acetal (POM) Copolymer
Stat-Tech™ AT-CB2/000 CR XP020229R2Information provided by PolyOne
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 153 °C | 307 °F | ASTM D648 |
|
LyondellBasell Higlass BJ22GC Polypropylene Copolymer, 30% Glass Fiber
Key Features: conventional melt flow, medium high modulus, UV-stabilized, chemically coupled, glass fiber-reinforced polypropylene copolymer, moderately high rigidity, high impact strength, excellen..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
153
°C <br>@Thickness 3.20 mm
|
307
°F <br>@Thickness 0.126 in
|
unannealed; ASTM D648 |
|
SABIC Innovative Plastics LNP LUBRICOMP KL004L Acetal Copolymer
LNP* LUBRICOMP* KL004L is a compound based on Acetal Copolymer resin containing 20% PTFE. Added features of this material include: Wear Resistant, Low Extractible.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
153
°C <br>@Thickness 3.20 mm
|
307
°F <br>@Thickness 0.126 in
|
unannealed; ASTM D648 |
|
SABIC Innovative Plastics LNP LUBRICOMP LX00430 PEEK
LNP* LUBRICOMP* LX00430 is a compound based on Pelyetheretherketone containing Proprietary Fillers. Added feature of this grade is: Wear Resistant.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 153 °C | 307 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
|
SABIC Innovative Plastics LNP LUBRICOMP PI001 PA 6 (Europe-Africa-Middle East)
LNP* LUBRICOMP* PI001 is a compound based on PA 6 resin containing Silicone. Added features include Internally Lubricated.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 153 °C | 307 °F | ISO 75 |
|
Solvay TECHNYLSTARâ„¢ A205 F Natural S PA66, Eh 50
TECHNYLSTAR A205 F NATURAL S is a polyamide 6.6 with low viscosity for fast cycle molding.Colors: it is supplied in natural color.Available in: Latin America and North AmericaMain Properties: High F..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 153 °C | 307 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
|
SABIC Innovative Plastics LNP LUBRICOMP WL004 PBT (Europe-Africa-Middle East)
LNP* Lubricomp* WL004 is a compound based on Polybutylene Terephalate resin containing PTFE.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
153
°C <br>@Thickness 3.20 mm
|
307
°F <br>@Thickness 0.126 in
|
unannealed; ASTM D648 |
|
SABIC Innovative Plastics LNP STAT-KON DX11411 PC
LNP* STAT-KON* DX11411 is a compound based on Polycarbonate resin containing Proprietary Filler(s). Added feature of this grade is: Electrically Conductive.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 153 °C | 307 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
|
SABIC Innovative Plastics LNP Thermocomp MX88073 PP (Asia Pacific)
LNP* Thermocomp* MX88073 is a compound based on Polypropylene resin containing Glass Fiber.This data was supplied by SABIC-IP for the Asia Pacific region.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 153 °C | 307 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
|
SABIC Innovative Plastics LNP Thermotuf U1000AIS PPA (Asia Pacific)
LNP* Thermotuf* U1000AIS is a compound based on Polyphthalamide resin. Added features of this material include: High Impact, Heat Stabilized.This data was supplied by SABIC-IP for the Asia Pacific ..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 153 °C | 307 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
|
SABIC Innovative Plastics LNP Thermocomp MX88073 PP
LNP* Thermocomp* MX88073 is a compound based on Polypropylene resin containing Glass Fiber.This data was supplied by SABIC-IP for the Americas region.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 153 °C | 307 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
|
SABIC Innovative Plastics LNP THERMOCOMP MX89510 PP
LNP* THERMOCOMP* MX89510 is a compound based on Polypropylene resin containing Proprietary Filler(s).
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 153 °C | 307 °F | ASTM D648 |
|
A. Schulman POLYFLAM™ E-14526-31 30% Glass Reinforced Chemically Coupled Polypropylene
DescriptionPolyfort® E-14526-31 is a 30% glass reinforced chemically coupled polypropylene black. Information provided by A. Schulman.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 153 °C | 307 °F | DIN 53461 |
|
Polyram RamOfin PPH302G4 Polypropylene, 20% Glass Fiber
20% glass fiber reinforced polypropylene for injection molding applicationsInformation provided by Polyram Ram On Ind.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 153 °C | 307 °F | DIN 53461 |
|
Polyram RamOfin PPH302G6 Polypropylene, 30% Glass Fiber
30% glass fiber reinforced polypropylene for injection molding applicationsInformation provided by Polyram Ram On Ind.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 153 °C | 307 °F | ASTM D648 |
|
A. Schulman POLYFLAM™ E-14526-31 30% Glass Reinforced Chemically Coupled Polypropylene
DescriptionPolyfort® E-14526-31 is a 30% glass reinforced chemically coupled polypropylene black. Information provided by A. Schulman.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 153 °C | 307 °F | DIN 53461 |
|
Polyram RamOfin PPH300G6 Polypropylene, 30% Glass Fiber
30% glass fiber reinforced polypropylene for injection molding applicationsInformation provided by Polyram Ram On Ind.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 153 °C | 307 °F | DIN 53461 |
|
Polyram RamOfin PPH300G8 Polypropylene, 40% Glass Fiber
40% glass fiber reinforced polypropylene for injection molding applicationsInformation provided by Polyram Ram On Ind.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 153 °C | 307 °F | ISO 75 |
|
Polyram RamOfin PPH301G6NT Polypropylene, 30% Glass Fiber
30% Glass fiber reinforced polypropylene for injection molding applications. Approved and listed by WRAS Potable Water.Information provided by Polyram.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 153 °C | 307 °F | DIN 53461 |
|
Polyram RamOfin PPH353M8 Polypropylene, 40% Mineral Filled
40% mineral filled polypropylene for injection molding applicationsInformation provided by Polyram Ram On Ind.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 153 °C | 307 °F | ASTM D648 |
|
Aclo Accutech Polypropylene Homopolymer HP0334G25M5CL Glass/Mineral Reinforced Coupled |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 153 °C | 307 °F | ASTM D648 |
|
Aclo Accutech Polypropylene Copolymer CP0436G20CL Glass Reinforced |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 153 °C | 307 °F | ASTM D648 |
|
Aclo Accutech Polypropylene Copolymer CP0436G20M10CL Glass/Mineral Reinforced Coupled |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 153 °C | 307 °F | ASTM D648 |
|
Ashley Polymers Ashlene® 279 PPO Alloy
A general purpose, paintable injection molding grade with high chemical resistance and mechanical performance. Good heat resistance with dimensional stability in dark gray or black only.Data provid..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 153 °C | 307 °F | ASTM D648 |
|
E-Polymers TEKASTER® F101M Unreinforced impact modified PBT
Polyester Resin: TEKASTER is thermoplastic polyester resins (PBT, PET) mostly injection molding. PBT has excellent mechanical properties and well balanced engineering plastics with an electrical pe..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
153
°C <br>@Thickness 3.20 mm
|
307
°F <br>@Thickness 0.126 in
|
unannealed; ASTM D648 |
|
SABIC Innovative Plastics LNP STAT-KON ME003S PP
LNP* STAT-KON* ME003S is a compound based on Polypropylene resin containing 15% Carbon Fiber. Added features of this material include: Electrically Conductive, Heat Stabilized.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 153 °C | 307 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
|
SABIC Innovative Plastics LNP STAT-KON ME006 PP
LNP STAT-KON* ME006 is a compound based on Polypropylene resin containing 30% Carbon Fiber. Added features of this material include: Electrically Conductive.
|
|||