SABIC Innovative Plastics NORYL GTX GTX820 PPE+PS+PA
| Category | Polymer , Thermoplastic , Nylon , Polyphenylene Ether/PPO , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | NORYL GTX |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics NORYL GTX GTX820 PPE+PS+PA.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
GR 20%. Higher stiffness of 800000 psi (4000 MPa) flexural modulus. Excellent chemical and high heat resistance. Application: valves.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.24 g/cc | 1.24 g/cc | ASTM D792 |
| Density | 1.245 g/cc | 0.04498 lb/in³ | ASTM D792 |
| Water Absorption | 0.50 % @Time 86400 sec |
0.50 % @Time 24.0 hour |
ASTM D570 |
| Moisture Absorption | 1.00 % | 1.00 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0060 cm/cm @Thickness 3.20 mm |
0.0040 - 0.0060 in/in @Thickness 0.126 in |
SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0065 - 0.0085 cm/cm @Thickness 3.20 mm |
0.0065 - 0.0085 in/in @Thickness 0.126 in |
SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 119 | 119 | ASTM D785 |
| Flexural Yield Strength | 194 MPa | 28100 psi | 2.6 mm/min, 100 mm span; ASTM D790 |
| Flexural Modulus | 5.96 GPa | 864 ksi | 2.6 mm/min, 100 mm span; ASTM D790 |
| Izod Impact, Notched | 0.800 J/cm | 1.50 ft-lb/in | ASTM D256 |
| 0.530 J/cm @Temperature -30.0 °C |
0.993 ft-lb/in @Temperature -22.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 30.6 - 39.6 µm/m-°C @Temperature -20.0 - 150 °C |
17.0 - 22.0 µin/in-°F @Temperature -4.00 - 302 °F |
ASTM E 831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 254 °C @Thickness 6.40 mm |
489 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 232 °C @Thickness 6.40 mm |
450 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| Vicat Softening Point | 248 °C | 478 °F | Rate B/50; ASTM D1525 |
Users viewing this material also viewed the following:
- Kazanorgsintez 107-277 Low Density Polyethylene Composition with Improved Processibility
- Gouda Vuurvast GOLITE 135 Refractory Insulating Castable
- Indium Corp. Indalloy 61 Bismuth Solder Alloy
- Techmer ES HiFill® HIPS GF30 30% Glass Filled
- Struktol POLYDIS 3710 Reactive flame retardant for flameproof finish of epoxide resins
- Saint-Gobain CHR® 2045-3 Skived PTFE Film Backing Silicone Adhesive Pressure Sensitive Tape
- A. Schulman POLYBATCH™ Green 30424 Concentrate Based In Polyethylene
- China Tungsten ZP25 Tungsten Carbide
- 3M Super 77™ Cylinder Spray Adhesive
Copyright © lookpolymers.com All Rights Reserved