Polymer Resources NY6-GP2 General Purpose Nylon 6, Nucleated

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced
Manufacturer Polymer Resources, LTD
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polymer Resources NY6-GP2 General Purpose Nylon 6, Nucleated.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
General Purpose Nylon 6, Nucleated Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Nylon grades are tested dry as molded (DAM).Information provided by Polymer Resources Corporation.
Physical Properties Metric English Comments
Specific Gravity 1.13 g/cc
1.13 g/cc
ASTM D792
Linear Mold Shrinkage 0.0080 - 0.012 cm/cm
0.0080 - 0.012 in/in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 89.6 MPa
13000 psi
ASTM D638
Tensile Strength, Yield 89.6 MPa
13000 psi
ASTM D638
Flexural Strength 108 MPa
15700 psi
ASTM D790
Flexural Modulus 3.10 GPa
450 ksi
ASTM D790
Izod Impact, Notched 0.534 J/cm

@Temperature 22.8 °C
 1.00 ft-lb/in

@Temperature 73.0 °F
 ASTM D256
Gardner Impact 36.2 J
26.7 ft-lb
ASTM D3029
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 191 °C
375 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 73.9 °C
165 °F
ASTM D648
UL RTI, Electrical 125 °C

@Thickness 0.800 mm
 257 °F

@Thickness 0.0315 in
 UL 746
125 °C

@Thickness 1.50 mm
 257 °F

@Thickness 0.0591 in
 UL 746
125 °C

@Thickness 3.00 mm
 257 °F

@Thickness 0.118 in
 UL 746
125 °C

@Thickness 5.99 mm
 257 °F

@Thickness 0.236 in
 UL 746
UL RTI, Mechanical with Impact 65.0 °C

@Thickness 0.800 mm
 149 °F

@Thickness 0.0315 in
 UL 746
85.0 °C

@Thickness 1.50 mm
 185 °F

@Thickness 0.0591 in
 UL 746
85.0 °C

@Thickness 3.00 mm
 185 °F

@Thickness 0.118 in
 UL 746
85.0 °C

@Thickness 5.99 mm
 185 °F

@Thickness 0.236 in
 UL 746
UL RTI, Mechanical without Impact 65.0 °C

@Thickness 0.800 mm
 149 °F

@Thickness 0.0315 in
 UL 746
75.0 °C

@Thickness 1.50 mm
 167 °F

@Thickness 0.0591 in
 UL 746
75.0 °C

@Thickness 3.00 mm
 167 °F

@Thickness 0.118 in
 UL 746
75.0 °C

@Thickness 5.99 mm
 167 °F

@Thickness 0.236 in
 UL 746
Flammability, UL94 V-2

@Thickness 1.50 mm
 V-2

@Thickness 0.0591 in
V-2

@Thickness 3.00 mm
 V-2

@Thickness 0.118 in
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+14 ohm-cm
1.00e+14 ohm-cm
ASTM D257
Dielectric Strength 29.9 kV/mm
760 kV/in
ASTM D149
Comparative Tracking Index >= 600 V
>= 600 V
UL 746
Hot Wire Ignition, HWI 7.0 - 15 sec

@Thickness 0.800 mm
 7.0 - 15 sec

@Thickness 0.0315 in
 UL 746
7.0 - 15 sec

@Thickness 1.50 mm
 7.0 - 15 sec

@Thickness 0.0591 in
 UL 746
15 - 30 sec

@Thickness 3.00 mm
 15 - 30 sec

@Thickness 0.118 in
 UL 746
30 - 60 sec

@Thickness 5.99 mm
 30 - 60 sec

@Thickness 0.236 in
 UL 746
High Amp Arc Ignition, HAI >= 120 arcs

@Thickness 0.800 mm
 >= 120 arcs

@Thickness 0.0315 in
 UL 746
>= 120 arcs

@Thickness 1.50 mm
 >= 120 arcs

@Thickness 0.0591 in
 UL 746
>= 120 arcs

@Thickness 3.00 mm
 >= 120 arcs

@Thickness 0.118 in
 UL 746
>= 120 arcs

@Thickness 5.99 mm
 >= 120 arcs

@Thickness 0.236 in
 UL 746
High Voltage Arc-Tracking Rate, HVTR 10.0 - 25.4 mm/min
0.394 - 1.00 in/min
UL 746
Processing Properties Metric English Comments
Rear Barrel Temperature 221 - 246 °C
430 - 475 °F
Middle Barrel Temperature 238 - 254 °C
460 - 490 °F
Front Barrel Temperature 243 - 260 °C
470 - 500 °F
Melt Temperature 238 - 279 °C
460 - 535 °F
Mold Temperature 79.4 - 93.3 °C
175 - 200 °F
Drying Temperature 73.9 - 85.0 °C
165 - 185 °F
Dry Time 3.00 - 4.00 hour
3.00 - 4.00 hour
Descriptive Properties Value Comments
Vent 0.0003