- Polymer Property : Flexural Strength = 15700 psi
Polymer Property : Flexural Strength = 15700 psi Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Flexural Strength | 108 MPa | 15700 psi | |
| Plastcom SLOVAMID 66/6 T 30 TS PA66/6, 30% mineral filling FeaturesPA 66/PA 6 alloy with the content of 30 % chemically modified mineral filling. Used for holders of electric hand tools, for hobby tools, gears, covers of electric tools, flat products, autom.. |
|||
| Flexural Strength | 108 MPa | 15700 psi | |
| Quadrant EPP Quadrant PPSU unfilled, extruded (ISO Data) Quadrant PPSU is a black, amorphous high performance thermoplastic, offering better impact strength and chemical resistance than polysulfone and polyetherimide. Quadrant PPSU also has superior hydro.. |
|||
| Flexural Strength | 108 MPa | 15700 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics Lexan® 505R PC Lexan* 505R Polycarbonate (PC) resin is a 10% glass fiber filled, injection moldable grade. Lexan 505R contains non-chlorinated, non-brominated flame retardant systems with UL-94 V0 rating at 1.5mm... |
|||
| Flexural Strength | 108 MPa | 15700 psi | ASTM D790 |
| Polymer Resources NY6-GP2 General Purpose Nylon 6, Nucleated General Purpose Nylon 6, Nucleated Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Nylon grades are tested dry .. |
|||
| Flexural Strength | 108 MPa | 15700 psi | ASTM D790 |
| SABIC Innovative Plastics Lexan® JK2000 PC+ABS (Asia Pacific) Lexan* JK2000 compound is a glass reinforced, non-Br and non-Cl FR polycarbonate blends designed for thinwall molding applications. |
|||
| Flexural Strength | 108 MPa | 15700 psi | ISO 178 |
| SABIC Innovative Plastics LNP LUBRICOMP DFL42 PC LNP* Lubricomp* DFL-4042 a compound based on Polycarbonate resin containing 10% Glass Fiber, 20% PTFE. Added features include: Internally Lubricated. |
|||
| Flexural Strength | 108 MPa | 15700 psi | ISO 178 |
| SABIC Innovative Plastics LNP LUBRICOMP EL002 PEI LNP* Lubricomp* EL002 is a compound based on Polyetherimide resin containing 10% PTFE. Added features of this material include: Internally Lubricated. |
|||
| Flexural Strength | 108 MPa | 15700 psi | ISO 178 |
| SABIC Innovative Plastics LNP LUBRICOMP KFL23LH Acetal Copolymer LNP LUBRICOMP* KFL23LH is a compound based on Acetal Copolymer resin containing 15% Glass Fiber, 10% PTFE. Added features of this material include: Wear Resistant, Low Extractable. |
|||
| Flexural Strength | 108 MPa | 15700 psi | ASTM D790 |
| SABIC Innovative Plastics LNP STAT-KON DD0009 PC LNP* STAT-KON* DD0009 is a compound based on Polycarbonate resin containing Carbon Powder. Added features of this material include: Electrically Conductive, Flame Retardant. |
|||
| Flexural Strength | 108 MPa | 15700 psi | ASTM D790 |
| Techmer ES HiFill® PA6 E HS Availability: North AmericaForms: PelletsAdditive: Heat StabilizerFeatures: Heat StabilizedProcessing Method: ExtrusionTPCI# 9586102Information provided by TP Composites, Inc. |
|||
| Flexural Strength | 108 MPa | 15700 psi | ASTM D790 |
| Techmer ES HiFill® PA6 HS L BK Heat Stabilized Availability: North AmericaForms: PelletsAdditive: Lubricant and Heat StabilizerFeatures: Lubricated and Heat StabilizedAppearance: BlackTPCI# 7190102Information provided by TP Composites, Inc. |
|||
| Flexural Strength | 108 MPa | 15700 psi | ASTM D790 |
| Techmer ES Plastiblend® PA6 HS L MB Nylon 6 Availability: North AmericaForms: PelletsAdditive: Heat Stabilizer and LubricantHeat Stabilized and LubricatedTPCI# 7018102Information provided by TP Composites, Inc. |
|||
| Flexural Strength | 108 MPa | 15700 psi | 2.8 mm/min; ASTM D790 |
| Samsung Cheil Industries Infino® TN-1200 PC, Unreinforced FR Information provided by Samsung Cheil Industries. |
|||
| Flexural Strength | 108 MPa | 15700 psi | 2.8 mm/min; ASTM D638 |
| Samsung Cheil Industries Infino® XI-4208 PA, Glass Filled Information provided by Samsung Cheil Industries. |
|||
| Flexural Strength | 108 MPa | 15700 psi | 2.8 mm/min; ASTM D790 |
| Samsung Cheil Industries Infino® NF-3017H PC/ABS, Unreinforced FR Information provided by Samsung Cheil Industries. |
|||
| Flexural Strength | 108 MPa | 15700 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| SABIC Innovative Plastics LNP Thermocomp OK006 PPS - Linear LNP* Thermocomp* OK006 is based on a Linear Polyphenylene Sulfide (PPS) containing Talc.This data was supplied by SABIC-IP for the Americas region. |
|||
| Flexural Strength | 108 MPa | 15700 psi | 2.8 mm/min; ASTM D790 |
| Samsung Cheil Industries Starex® GR-5020T SAN, 20% Glass Filled Information provided by Samsung Cheil Industries. |
|||
| Flexural Strength | 108 MPa | 15700 psi | 2.8 mm/min; ASTM D638 |
| Samsung Cheil Industries Starex® VB-4921 ABS, Glass Filled FR Information provided by Samsung Cheil Industries. |
|||
| Flexural Strength | 108 MPa | 15700 psi | ASTM D790 |
| Techmer ES HiFill® PA6 HS L Heat Stabilized Availability: North AmericaForms: PelletsAdditive: Lubricant and Heat StabilizerFeatures: Lubricated and Heat StabilizedTPCI# 7190102Information provided by TP Composites, Inc. |
|||
| Flexural Strength | 108 MPa | 15700 psi | 2.8 mm/min; ASTM D790 |
| Samsung Cheil Industries Starex® GR-4020L ABS, Glass Filled ABS/GF material that is used in printer LBP fuserInformation provided by Samsung Cheil Industries. |
|||
| Flexural Strength | 108 MPa | 15700 psi | 2.8 mm/min; ASTM D790 |
| Samsung Cheil Industries Infino® NH-3204G PC, Glass Filled FR Information provided by Samsung Cheil Industries. |
|||
| Flexural Strength | 108 MPa | 15700 psi | 2.8 mm/min; ASTM D638 |
| Samsung Cheil Industries Infino® VB-3100G PBT/ABS, Glass Filled FR Information provided by Samsung Cheil Industries. |
|||
| Flexural Strength | 108 MPa | 15700 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics NORYL GTX GTX679 PPE+PA6 Noryl GTX* GTX679 Resin is a blend of Polyphenylene Ether(PPE) + Polyamide(PA) resin that is mineral filled, conductive, and suitable for injection molding. The conductivity level is optimized to al.. |
|||
| Flexural Strength | 108 MPa | 15700 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics NORYL GTX GTX679 PPE+PA6 (Europe-Africa-Middle East) Noryl GTX* GTX679 Resin is a blend of Polyphenylene Ether(PPE) + Polyamide(PA) resin that is mineral filled, conductive, and suitable for injection molding. The conductivity level is optimized to al.. |
|||
| Flexural Strength | 108 MPa | 15700 psi | ISO 178 |
| Unitika A3130HR-25 PA6, 25% Mineral Reinforced, Dry Information provided by Unitika Ltd. |
|||
| Flexural Strength | 108 MPa | 15700 psi | ASTM D790 |
| E-Polymers TEKAMID® TB120CR Fast Crystallinity PA6 Resin Polyamide (Nylon) Resin. TEKAMID is widely being used in manufacturing of automotive and industrial parts with its outstanding mechanical, thermal and chemical properties.T-series: Impact modified,.. |
|||
| Flexural Strength | 108 MPa | 15700 psi | ASTM D790 |
| Adell BJ-33 Nylon 6, 15% Glass Reinforced; High Impact Data provided by Adell Plastics, Inc. |
|||
| Flexural Strength | 108 MPa | 15700 psi | ASTM Test |
| BASF Ultramid® 8202 HS BK-102 PA6 (Dry) Ultramid 8202 HS BK-102 is an unfilled, heat stabilized, pigmented black, low viscosity, general purpose injection molding PA6 exhibiting excellent fluidity for filling thin sections. It possesses .. |
|||
| Flexural Strength | 108 MPa | 15700 psi | ASTM D790 |
| Plaskolite West Optix® CA-61 General Purpose Acrylic Resin Injection Molding and Extrusion Grade Pellets. Good heat resistance, medium flow. |
|||