- HOME
- POLYMER SEARCH
- Polymer Property : Linear Mold Shrinkage = 0.012 cm/cm
Polymer Property : Linear Mold Shrinkage = 0.012 cm/cm Product List
Physical PropertiesTips: 30 items are displayed at most.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Linear Mold Shrinkage | 0.010 - 0.012 cm/cm | 0.010 - 0.012 in/in | With Flow; ISO 2577 |
|
Polykemi AB POLYfill PPC T4030 E20 Polypropylene Copolymer, Mineral Reinforced, Elastomer Modified
Information provided by Polykemi AB
|
|||
| Linear Mold Shrinkage | 0.010 - 0.012 cm/cm | 0.010 - 0.012 in/in | With Flow; ISO 2577 |
|
Polykemi AB POLYfill PPC TS20020 Polypropylene Copolymer, Mineral Reinforced
Information provided by Polykemi AB
|
|||
| Linear Mold Shrinkage | 0.0070 - 0.012 cm/cm | 0.0070 - 0.012 in/in | ISO 2577 |
|
Panjin Zhongrun Chemerize 012P High Viscosity CoPEEK
Information provided by Bieglo Gmbh.
|
|||
| Linear Mold Shrinkage | 0.010 - 0.012 cm/cm | 0.010 - 0.012 in/in | Across Flow; ISO 2577 |
|
Polykemi AB POLYfill PPHC T15020 Polypropylene, Mineral Reinforced
Information provided by Polykemi AB
|
|||
| Linear Mold Shrinkage | 0.010 - 0.012 cm/cm | 0.010 - 0.012 in/in | With Flow; ISO 2577 |
|
Polykemi AB POLYfill PPHC TS25020 Polypropylene, Mineral Reinforced
Information provided by Polykemi AB
|
|||
| Linear Mold Shrinkage | 0.0080 - 0.012 cm/cm | 0.0080 - 0.012 in/in | (longitudinal) Injection; ISO 2257 |
|
Raschig Group MELOPLAS® 3025 MF
Cellulose-reinforced and inorganically filled MF molding compound in white and colored shades. High surface hardness, good UV and heat stability, very good resistance to chemicals - also to foodstu..
|
|||
| Linear Mold Shrinkage | 0.010 - 0.012 cm/cm | 0.010 - 0.012 in/in | With Flow; ISO 2577 |
|
Polykemi AB POLYfill PPH T3022D Polypropylene Homopolymer, Mineral Reinforced, Detergent Resistant
Information provided by Polykemi AB
|
|||
| Linear Mold Shrinkage | 0.010 - 0.012 cm/cm | 0.010 - 0.012 in/in | Across Flow; ISO 2577 |
|
Polykemi AB POLYfill PPH T5020 Polypropylene Homopolymer, Mineral Reinforced
Information provided by Polykemi AB
|
|||
| Linear Mold Shrinkage | 0.0090 - 0.012 cm/cm | 0.0090 - 0.012 in/in | |
|
Lehmann & Voss LUVOCOM® 20-7314 Polyphthalamide, with PTFE
Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Improved friction and wear behaviour. Emergency running property.Low influence from moisture an..
|
|||
| Linear Mold Shrinkage | 0.010 - 0.012 cm/cm | 0.010 - 0.012 in/in | ASTM D1299 |
|
Loxim 821 02T HB Polypropylene Compound, 20% Talc Filled, Flame Retardant
Information provided by Loxim Industries
|
|||
| Linear Mold Shrinkage | 0.0070 - 0.012 cm/cm | 0.0070 - 0.012 in/in | |
|
Lehmann & Voss LUVOCOM® 1105/MS/15/TF/15 PEEK, with PTFE, lubricant modified
Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Dynamic stressed parts at high movement velocity.Chemical and hydrolysis resistance parts,..
|
|||
| Linear Mold Shrinkage | 0.010 - 0.012 cm/cm | 0.010 - 0.012 in/in | ASTM D955 |
|
Teknor Apex APEX® 6500-105 Polyvinyl Chloride, Flexible
Notes: 60°C General Purpose; RoHS Compliant Uses: Connectors; Grommets; Plugs; Strain ReliefsForms: Pellets Processing Method: Extrusion Agency Ratings: UL QMFZ2 .E54709 Wire Types: Molded Compon..
|
|||
| Linear Mold Shrinkage | 0.0020 - 0.012 cm/cm | 0.0020 - 0.012 in/in | ASTM D955 |
|
Samyang Tribit® 1550GN30 PBT Alloy, Reinforced Flame Retardancy
Crystallization is fast, formability is excellent and thermal resistance, chemical resistance, electrical properties and abrasion resistance are excellent.1550GN30 is a reinforced, flame retardant (..
|
|||
| Linear Mold Shrinkage | 0.0090 - 0.012 cm/cm | 0.0090 - 0.012 in/in | ASTM D955 |
|
A. Schulman POLYFLAM™ RPP 1174 Talc Filled, Homopolymer Polypropylene
DescriptionPolyflam® RPP 1174 is a high performance talc filled homopolymer polypropylene product with UL V0 flammability and 105°C temperature index at 0.81 mm. RPP 1174 is non-dripping and has ..
|
|||
| Linear Mold Shrinkage | 0.0060 - 0.012 cm/cm | 0.0060 - 0.012 in/in | ASTM D955 |
|
Cheng Yu Plastic ML848 Flame Retardant PC |
|||
| Linear Mold Shrinkage | 0.010 - 0.012 cm/cm | 0.010 - 0.012 in/in | Internal |
|
Ecomass® 1950TU76 Tungsten Filled Polyamide
Nontoxic alternative to Lead (Pb), weighting, balancing and radiation shielding applicationsTungsten Powder Filled Polyamide (PA6/10)Very Good ToughnessInformation provided by Technical Polymers
|
|||
| Linear Mold Shrinkage |
0.0080
-
0.012
cm/cm <br>@Thickness 4.00 mm
|
0.0080
-
0.012
in/in <br>@Thickness 0.157 in
|
|
|
CP-Polymer-Technik Wellamid® 6000/58 CP Nylon 6, Impact Modified Until -40°C, Conditioned
Information provided by CP-Polymer-Technik GmbH & Co. KG
|
|||
| Linear Mold Shrinkage |
0.0080
-
0.012
cm/cm <br>@Thickness 4.00 mm
|
0.0080
-
0.012
in/in <br>@Thickness 0.157 in
|
|
|
CP-Polymer-Technik Wellamid® 6600 HWS Nylon 66, Finely Crystalline, Heat Stabilized, Dry
Information provided by CP-Polymer-Technik GmbH & Co. KG
|
|||
| Linear Mold Shrinkage |
0.0080
-
0.012
cm/cm <br>@Thickness 4.00 mm
|
0.0080
-
0.012
in/in <br>@Thickness 0.157 in
|
|
|
CP-Polymer-Technik Wellamid® 6600/506 HWCP Nylon 66, Impact Modified, Heat Stabilized, Dry
Information provided by CP-Polymer-Technik GmbH & Co. KG
|
|||
| Linear Mold Shrinkage |
0.0080
-
0.012
cm/cm <br>@Thickness 4.00 mm
|
0.0080
-
0.012
in/in <br>@Thickness 0.157 in
|
|
|
CP-Polymer-Technik Wellamid® 6600/508 HWUVCP Nylon 66, Impact Modified, UV Stabilized, Heat Stabilized, Conditioned
Information provided by CP-Polymer-Technik GmbH & Co. KG
|
|||
| Linear Mold Shrinkage |
0.0080
-
0.012
cm/cm <br>@Thickness 4.00 mm
|
0.0080
-
0.012
in/in <br>@Thickness 0.157 in
|
|
|
CP-Polymer-Technik Wellamid® 6600/508 HWUVCP Nylon 66, Impact Modified, UV Stabilized, Heat Stabilized, Dry
Information provided by CP-Polymer-Technik GmbH & Co. KG
|
|||
| Linear Mold Shrinkage | 0.0060 - 0.012 cm/cm | 0.0060 - 0.012 in/in | ASTM D955 |
|
Cheng Yu Plastic ML3415 PC, 15% Glass Fiber |
|||
| Linear Mold Shrinkage | 0.010 - 0.012 cm/cm | 0.010 - 0.012 in/in | Asahi Kasei Method |
|
Asahi Kasei Tenac®-C MT754 Copolymer Acetal Resin
20% Mineral filled, high stiffness, low warp gradeInformation provided by Asahi Kasei Corporation.
|
|||
| Linear Mold Shrinkage | 0.0080 - 0.012 cm/cm | 0.0080 - 0.012 in/in | ASTM D955 |
|
Beijing Chemical Industry KAIFA® MN301-M30 Nylon 66 Resin
Mineral filled, Good flowInformation provided by Beijing Chemical Industry Research Institute (Group)
|
|||
| Linear Mold Shrinkage | 0.010 - 0.012 cm/cm | 0.010 - 0.012 in/in | With Flow; ISO 2577 |
|
Polykemi AB POLYfill PPH T8020 Polypropylene Homopolymer, Mineral Reinforced
Information provided by Polykemi AB
|
|||
| Linear Mold Shrinkage | 0.010 - 0.012 cm/cm | 0.010 - 0.012 in/in | Across Flow; ISO 2577 |
|
Polykemi AB POLYfill PPH TS8030 Polypropylene Homopolymer, Mineral Reinforced
Information provided by Polykemi AB
|
|||
| Linear Mold Shrinkage | 0.010 - 0.012 cm/cm | 0.010 - 0.012 in/in | Across Flow; ISO 2577 |
|
Polykemi AB POLYfill PPHC TS15020 Polypropylene, Mineral Reinforced
Information provided by Polykemi AB
|
|||