Polykemi AB POLYabs F00 ABS
| Category | Polymer , Thermoplastic , ABS Polymer |
| Manufacturer | Polykemi AB |
| Trade Name | POLYabs |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polykemi AB POLYabs F00 ABS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Polykemi AB
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.0060 - 0.0080 cm/cm | 0.0060 - 0.0080 in/in | With Flow; ISO 2577 |
| 0.0060 - 0.0080 cm/cm | 0.0060 - 0.0080 in/in | Across Flow; ISO 2577 | |
| Melt Index of Compound | 18 g/10 min @Load 5.00 kg, Temperature 230 °C |
18 g/10 min @Load 11.0 lb, Temperature 446 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | <= 40.0 MPa | <= 5800 psi | ISO/R527 |
| Elongation at Yield | 6.0 % | 6.0 % | ISO/R527 |
| Flexural Strength | <= 75.0 MPa | <= 10900 psi | ISO 178 |
| Flexural Modulus | 2.10 GPa @Temperature 23.0 °C |
305 ksi @Temperature 73.4 °F |
ISO 178 |
| Charpy Impact, Notched | 1.20 J/cm² @Temperature -20.0 °C |
5.71 ft-lb/in² @Temperature -4.00 °F |
ISO 179 |
| 1.70 J/cm² @Temperature 23.0 °C |
8.09 ft-lb/in² @Temperature 73.4 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 87.0 °C | 189 °F | 120°C/h; ISO 75/1 |
| Deflection Temperature at 1.8 MPa (264 psi) | 76.0 °C | 169 °F | 120°C/h; ISO 75/1 |
| Vicat Softening Point | 100 °C @Load 5.001 kg |
212 °F @Load 11.03 lb |
50°C/h; ISO 306 |
| 105 °C @Load 1.00 kg |
221 °F @Load 2.21 lb |
50°C/h; ISO 306 | |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 190 - 230 °C | 374 - 446 °F | |
| Mold Temperature | 60.0 - 80.0 °C | 140 - 176 °F | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | in circulation dryer |
| 2 - 4 hour | 2 - 4 hour | in fresh-air dryer | |
| 2 - 4 hour | 2 - 4 hour | in desiccant air dryer | |
| Injection Pressure | 90.0 - 150 MPa | 13100 - 21800 psi | |
| Back Pressure | 1.00 - 1.50 MPa | 145 - 218 psi |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Holding Pressure () | 20-40 | % of injection pressure |
| Injection Speed () | High |
Users viewing this material also viewed the following:
- MV Labs PR870 Pr2(C2O4)3·xH2O Praseodymium oxalate hydrate
- Potters Industries Q-Cel® 5019
- SABIC Innovative Plastics Cycolac® MG8000SR ABS (Europe-Africa-Middle East)
- Chevron Phillips 7109DLT LLDPE Blown Film Resin, Hexene Copolymer (discontinued **)
- SABIC Innovative Plastics Noryl GTX GTX8710 PPE+PA
- ExxonMobil 627 Mobilgear 600 Series
- Dow Corning SILASTIC® LC-45-2004 PART A&B KIT
- Covestro Bayfill® EA 4004 Polyurethane Energy-Absorbing Semi-Rigid Foam, Rigid Grade, MDI-based 2-Component Liquid System
- Domo Domamid® 24 T-HS Polyamide 6
- Ineos H12BLME Polypropylene Homopolymer
Copyright © lookpolymers.com All Rights Reserved