- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 169 °F
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 169 °F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 76.0 °C | 169 °F | ASTM D648 |
| Plaskolite Optix® CA-51 General Purpose Acrylic Resin Injection Molding and Extrusion Grade Pellets. Medium heat resistance and medium flow. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 76.0 °C | 169 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| SABIC Innovative Plastics Cycolac® GPM5500F ABS (Europe-Africa-Middle East) CYCOLAC GPM5500F is a multi purpose injection moulding grade, providing a favourable balance of engineering properties and is FDA and European Directive 2002/72/EC
(FCEU) compliant for food contac.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 76.0 °C @Thickness 3.20 mm |
169 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics GELOY CR7020 ASA ASA copolymer. Profile/sheet coextrusion over ABS. Excellent weatherability, good flow/aesthetics and high impact. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 76.0 °C @Thickness 3.20 mm |
169 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics Geloy EXGY30CP ASA Pearlescent GELOY ASA resin with copper-look for capstock extrusion. Outstanding weatherability.This data was supplied by SABIC-IP for the Americas region. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 76.1 °C @Thickness 6.35 mm |
169 °F @Thickness 0.250 in |
Annealed; ASTM D648 |
| PolyOne Geon™ 80510 Polyvinyl Chloride, Rigid (PVC, Rigid) Information provided by PolyOne |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 76.0 °C @Thickness 3.20 mm |
169 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP LUBRICOMP AL004 ABS (Asia Pacific) LNP* Lubricomp* AL004 is a compound based on Acrylonitrile Butadiene Styrene resin containing Lubricants. Added features of this material include: Internally Lubricated. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 76.0 °C | 169 °F | 4 mm thick;10.0 mm wide molded rod; ISO 75/Method Af |
| Premix Thermoplastics PRE-ELEC® PPE 1461
(discontinued **) PRE-ELEC PPE 1461 is a conductive thermoplastic compound based on modified polyphenylene ether (PPE). Conductivity is achieved by using special conductive carbon black. In addition to a low electric.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 76.0 °C @Thickness 6.40 mm |
169 °F @Thickness 0.252 in |
ASTM D648 |
| Kingfa FRHIPS-220 Flame Retardant Polystyrene Features:UL 94 V-0 @ 1.6 & 3.2mmExcellent balance properties, high strengthExcellent heat stabilityExcellent electrical propertiesApplications:Injection moldingGas moldingTV & Audio housingElectrica.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 76.0 °C @Thickness 6.40 mm |
169 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| LG Chemical AF312B ABS, Flame Retardant Feature: Injection Molding, Flame RetardantApplication: Electric/Electronic Applications (TV, Monitor Housing) IT/OA deviceCAS No. 9003-56-9, 79-94-7 and 1309-64-4Information provided by LG Chemical.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 76.0 °C | 169 °F | ASTM D648 |
| LG Chemical LUPOL HG-3200 High Gloss Polypropylene, 20% Mineral Fillers LUPOL resins, based on polyolefin with a wide range of characteristics, are a family of low cost engineering plastics.Applications: Automotive: Bumper cover, instrument panel, glove box, air cleaner.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 76.0 °C | 169 °F | |
| Ineos ABS Lustran® LGA Key Features:UnfilledSuitable processing methods:Injection molding |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 76.0 °C | 169 °F | unannealed; ASTM D648 |
| KKPC Kuhmo HI 425EH Extrusion Molding HIPS Key features: ESCR Common Uses: Refrigerator inner liners, door liners, disposable cups, food packaging sheet, wrapping films, trays, washing machinesHIPS is a functional resin made by copolymerizat.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 75.9 °C | 169 °F | annealed; ASTM D648 |
| KYDEX® 5555 Low Heat Release Aviation Thermoforming Sheet Features:Over two hundred colors and eight thicknesses availableChemical resistantMeets flamespread and smoke density requirements for mass transitSuggested Applications:Seat partsBulkhead laminates.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 75.9 °C | 169 °F | annealed; ASTM D648 |
| KYDEX® 6565(d) Decorative Low Heat Release Thermoplastic Sheet, Aviation Features:Wide range of thicknesses availableVery resistance to a wide range of concentrate chemicals, easy to cleanForms to deep draws with low forces when heated to the upper end of the proper form.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 76.0 °C | 169 °F | Annealed; ASTM D648 |
| Spartech Royalite R632M Carbon Black Filled ABS/PVC Resin Data provided by the manufacturer. This static-conductive material is UL®-listed and meets minimum static-decay requirements outlined in MIL-B-1705B and NFPA Code 56A specifications. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 76.0 °C | 169 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP STAT-LOY A3000 ABS (Asia Pacific) LNP STAT-LOY A3000 is a compound based on Acrylonitrile butadiene Styrene resin containing Anti-Static. Added features of this material include: Antistatic. Also known as: STAT-LOY A |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 76.0 °C @Thickness 3.20 mm |
169 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics LNP Stat-loy AX06484X ABS LNP* Stat-Loy* AX06484 is a compound based on ABS resin containing mineral filler. Characteristics of this grade is it is extrudeable and static dissipative.This data was supplied by SABIC-IP for t.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 76.0 °C | 169 °F | ASTM D648 |
| Shuman 710 Utility Black ABS Good impact strength, easy processability, good chemical resistance, good wear and abrasion resistance.Data provided by the manufacturer. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 76.1 °C | 169 °F | ASTM D648 |
| Shuman 780H Grey ABS Good impact strength, easy processability, good chemical resistanceInformation provided by Shuman Plastics, Inc. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 76.0 °C | 169 °F | ISO 75 |
| Styrolution Terblend® N NM-12 ABS/PA6 (Dry) Terblend N NM-12 is an ABS/PA6 blend combining high impact strength and rigidity with an excellent processability and surface appearance.Information provided by STYROLUTION, which is a joint venture.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 76.0 °C | 169 °F | ASTM D648 |
| Supreme Petrochem SC 6501 Toughened Polystyrene Characteristics Excellent melt strength Extremely tough Easy printability Easy miscibility with most grades of polystyrene Processing Extrusion Thermoforming Injection MoldingApplications Impac.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 76.0 °C | 169 °F | ASTM D648 |
| A. Schulman POLYFORT™ FPP 1007X Extra High Flow, Talc Fortified Homopolymer Polypropylene DescriptionPolyfort® FPP 1007X is an extra high flow, 40% talc fortified homopolymer polypropylene. Information provided by A. Schulman. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 76.0 °C | 169 °F | ASTM D648 |
| A. Schulman POLYFORT™ FPP 809 Talc Filled Homopolymer Polypropylene DescriptionPolyfort® FPP 809 is a 40% talc-filled homopolymer polypropylene.Information provided by A. Schulman. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 76.0 °C | 169 °F | ASTM D648 |
| A. Schulman POLYFORT™ FPP 1007X Extra High Flow, Talc Fortified Homopolymer Polypropylene DescriptionPolyfort® FPP 1007X is an extra high flow, 40% talc fortified homopolymer polypropylene. Information provided by A. Schulman. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 76.0 °C | 169 °F | ASTM D648 |
| A. Schulman POLYFORT™ FPP 1007X Extra High Flow, Talc Fortified Homopolymer Polypropylene DescriptionPolyfort® FPP 1007X is an extra high flow, 40% talc fortified homopolymer polypropylene. Information provided by A. Schulman. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 76.0 °C | 169 °F | ASTM D648 |
| Eastman Tenite 350A0096914 Propionate Natural Tenite cellulosic plastics are noted for their excellent balance of properties - toughness, hardness, strength, surface gloss, clarity, and a warm feel. The mechanical properties of Tenite cellulosi.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 76.1 °C | 169 °F | 0.125 in bar Unannealed/Conditioned 48 hours at 23°C; ASTM D648 |
| Diamond Polymers ABS 9501 Description: Injection Molding Grade, Ultra High ImpactInformation provided by Diamond Polymers, Inc. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 76.0 °C | 169 °F | |
| Polimeri Europa SINKRAL D720 ABS, Impact Grade
(discontinued **) Symbol according to ISO 1043-1: ABS Grade designation according to ISO 2580-ABS 1,MG,095-08-35-15 High impact injection moulding grade, with improved flow compared with SINKRAL B620 and a high glo.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 76.0 °C | 169 °F | |
| Arkema Group Oroglas® VS-UVT Acrylic, Injection Molding Grade
(discontinued **) The outstanding flow of OROGLAS VS-UVT makes it as the material of choice for injection molding of part with thin wall thickness.The ultraviolet transmitting ( uvt) formulation is developed to meet .. |
|||