- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 76.0 °C
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 76.0 °C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 76.0 °C | 169 °F | |
| Plastcom SLOVALEN PH 99 GB 30 LS PP, 30% glass beads, mod. of mech. properties FeaturesModified homopolymer PP for injection moulding, chemically reinforced with 30% glass beads, contains the modifier of mechanical properties. Increased strength in comparison with unfilled PP... |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 76.0 °C @Thickness 3.20 mm |
169 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP LUBRICOMP AL004 ABS (Asia Pacific) LNP* Lubricomp* AL004 is a compound based on Acrylonitrile Butadiene Styrene resin containing Lubricants. Added features of this material include: Internally Lubricated. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 76.0 °C @Thickness 3.20 mm |
169 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Cycolac® EX58 ABS (Europe-Africa-Middle East) High impact ABS for sheet extrusion and blow molding applications. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 76.0 °C | 169 °F | Unannealed; ASTM Data |
| Americas Styrenics Styron® 495R High Impact Polystyrene
(discontinued **) Data provided by Dow Chemical.Americas Styrenics was formed in 2008 as a joint venture between Dow Chemical and Chevron Phillips Chemical Company. Styron was a Dow trade name before the JV formatio.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 76.0 °C | 169 °F | 4 mm thick;10.0 mm wide molded rod; ISO 75/Method Af |
| Premix Thermoplastics PRE-ELEC® PPE 1461
(discontinued **) PRE-ELEC PPE 1461 is a conductive thermoplastic compound based on modified polyphenylene ether (PPE). Conductivity is achieved by using special conductive carbon black. In addition to a low electric.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 76.0 °C @Thickness 3.20 mm |
169 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP LUBRICOMP AL004 ABS LNP* Lubricomp* AL004 is a compound based on Acrylonitrile Butadiene Styrene resin containing 20% PTFE. Added features of this material include: Internally Lubricated. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 76.0 °C @Thickness 6.40 mm |
169 °F @Thickness 0.252 in |
ASTM D648 |
| Kingfa HF-606 Flame Retardant ABS Features:UL 94 V-0 @ 1.6-3.0mm, 5VB @ 2.0mmHigh flowModerate UV stabilityHigh stiffnessApplications:Injection moldingMonitor cabinetCD-ROMPower switchInformation Provided by Kingfa Sci. & Tech. Co.,.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 76.0 °C | 169 °F | |
| Ineos ABS Lustran® LGM Key Features:UnfilledSuitable processing methods:Injection molding |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 76.0 °C @Thickness 3.20 mm |
169 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP LUBRICOMP RL002 PA 66 LNP LUBRICOMP* RL002 is a compound based on Nylon 66 resin containing 10% PTFE. Added features of this material include: Wear Resistant. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 76.0 °C @Thickness 3.20 mm |
169 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP LUBRICOMP RN001S PA 66 (Asia Pacific) LNP* Lubricomp* RN001S is a compound based on Nylon 66 resin containing MOS2. Added features of this material include: Internally Lubricated, Heat Stabilized. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 76.0 °C | 169 °F | Annealed; ASTM D648 |
| Spartech Royalite R632M Carbon Black Filled ABS/PVC Resin Data provided by the manufacturer. This static-conductive material is UL®-listed and meets minimum static-decay requirements outlined in MIL-B-1705B and NFPA Code 56A specifications. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 76.0 °C | 169 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics Xenoy® IQ1103 PBT+PC Xenoy iQ*1103 resin - Environmentally responsible and sustainable low carbon footprint resin. Xenoy iQ1103 is an unreinforced, impact modified alloy of PC (polycarbonate) + Valox iQ* PBT (polybuty.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 76.0 °C | 169 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP STAT-LOY A3000 ABS LNP STAT-LOY* A3000 is a compound based on ABS resin. Added feature of this material is: Antistatic. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 76.0 °C | 169 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP Stat-loy AX06484X ABS LNP* Stat-Loy* AX06484 is a compound based on ABS resin containing mineral filler. Characteristics of this grade is it is extrudeable and static dissipative.This data was supplied by SABIC-IP for t.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 76.0 °C | 169 °F | ASTM D648 |
| Shuman 720 Black ABS Good impact strength, easy processability, good chemical resistance, good wear and abrasion resistance.Data provided by the manufacturer. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 76.0 °C @Thickness 6.40 mm |
169 °F @Thickness 0.252 in |
ASTM D648 |
| Samsung Cheil Industries Starex® VH-0819 ABS, Unreinforced FR Flame-retardant high flow ABS that can be used for the exterior of large TV and OA devicesInformation provided by Samsung Cheil Industries. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 76.0 °C | 169 °F | Unannealed; ASTM Data |
| Styron Magnum™ 341 ABS, Low Gloss MAGNUM® ABS resins are thermoplastic materials which provide an excellent balance of processability, impact resistance and heat resistance as imparted by the various polymer compositions. MAGNUM .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 76.0 °C | 169 °F | ASTM D648 |
| Supreme Petrochem SC 6501 Toughened Polystyrene Characteristics Excellent melt strength Extremely tough Easy printability Easy miscibility with most grades of polystyrene Processing Extrusion Thermoforming Injection MoldingApplications Impac.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 76.0 °C | 169 °F | ASTM D648 |
| A. Schulman POLYFORT™ FPP 1007X Extra High Flow, Talc Fortified Homopolymer Polypropylene DescriptionPolyfort® FPP 1007X is an extra high flow, 40% talc fortified homopolymer polypropylene. Information provided by A. Schulman. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 76.0 °C | 169 °F | ISO 75 |
| Wellman Wellamid® 22LN2-N Unfilled Nylon 66, Lubricated & Nucleated Typical Applications: Automotive components, gears, switches, bearings, pulleys, fasteners, electrical coil forms, chain-saw hand guards, cable ties, furniture hardware, small appliance housings, ae.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 76.0 °C | 169 °F | ASTM D648 |
| A. Schulman POLYFORT™ FPP 1007X Extra High Flow, Talc Fortified Homopolymer Polypropylene DescriptionPolyfort® FPP 1007X is an extra high flow, 40% talc fortified homopolymer polypropylene. Information provided by A. Schulman. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 76.0 °C | 169 °F | ASTM D648 |
| A. Schulman POLYFORT™ FPP 3443U UV Resistant Homopolymer Polypropylene DescriptionPolyfort® FPP 3443U is a 40% talc fortified UV resistant homopolymer polypropylene product. Information provided by A. Schulman. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 76.0 °C | 169 °F | ASTM D648 |
| A. Schulman POLYFORT™ FPP 809 Talc Filled Homopolymer Polypropylene DescriptionPolyfort® FPP 809 is a 40% talc-filled homopolymer polypropylene.Information provided by A. Schulman. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 76.0 °C | 169 °F | ISO 75-1, 2 |
| Polyplastics Duranex® 407EP Polybutylene Terephthalate (PBT), Higher gloss, Better surface appearance DURANEX® is a crystalline thermoplastic based on polybutylene terephthalate (PBT) that can be readily strengthened, modified, or otherwise performance enhanced through the addition of glass fibers .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 76.0 °C | 169 °F | |
| BASF Polystyrol® 165 H Polystyrene (Europe) High molecular grades, often blended with high-impact extrusion grades (e.g. for dairy products).Data was collected by ISO methods and provided by BASF. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 76.0 °C | 169 °F | ASTM Test |
| BASF Ultramid® B3S Q661 PA6 (Dry) Ultramid B3S Q661 is a general purpose, PA6 resin for injection molding. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 76.0 °C | 169 °F | ISO 75-2/AF |
| Addiplast Addilene H 442 M30 Polypropylene Homopolymer High heat resistance, detergent stabilizedInformation provided by Addiplast. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 76.0 °C @Thickness 6.40 mm |
169 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics NORYL FN215X PPE+PS Structural foam resin. 170F (77C) HDT. Improved reliability and productivity. All values at 20% weight reduction. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 76.0 °C | 169 °F | |
| Polimeri Europa SINKRAL D720 ABS, Impact Grade
(discontinued **) Symbol according to ISO 1043-1: ABS Grade designation according to ISO 2580-ABS 1,MG,095-08-35-15 High impact injection moulding grade, with improved flow compared with SINKRAL B620 and a high glo.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 76.0 °C | 169 °F | ASTM D648 |
| A. Schulman POLYFORT™ FPP 1007X Extra High Flow, Talc Fortified Homopolymer Polypropylene DescriptionPolyfort® FPP 1007X is an extra high flow, 40% talc fortified homopolymer polypropylene. Information provided by A. Schulman. |
|||