Polymer Property : Linear Mold Shrinkage = 0.0060 cm/cm Product List

Physical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Physical Properties Metric English Comments
Linear Mold Shrinkage 0.0060 - 0.0080 cm/cm
0.0060 - 0.0080 in/in
Across Flow; ISO 2577
Polykemi AB POLYabs S00 AS UV ABS, High Flow, UV-Stabilized, Antistatic
Information provided by Polykemi AB
Linear Mold Shrinkage 0.0060 - 0.0080 cm/cm
0.0060 - 0.0080 in/in
With Flow; ISO 2577
Polykemi AB POLYabs SS0 ABS, High Flow
Information provided by Polykemi AB
Linear Mold Shrinkage 0.0060 - 0.0080 cm/cm
0.0060 - 0.0080 in/in
Across Flow; ISO 2577
Polykemi AB POLYfill PPH GF5020 PD1 Polypropylene Homopolymer, Glass Fibre-Reinforced, Chemically Coupled
Information provided by Polykemi AB
Linear Mold Shrinkage 0.0060 - 0.0080 cm/cm
0.0060 - 0.0080 in/in
Across Flow; ISO 2577
Polykemi AB POLYabs HF0 ABS
Information provided by Polykemi AB
Linear Mold Shrinkage 0.0060 - 0.0080 cm/cm
0.0060 - 0.0080 in/in
ASTM D955
Ineos ABS Lustran® 1148 General Purpose, High-Impact  (discontinued **)
Information provided by Bayer Corporation, Plastics DivisionLANXESS was spun-off from Bayer in early 2005. Business renamed Ineos ABS after INEOS acquires a majority shareholding under a JV with La..
Linear Mold Shrinkage 0.0060 - 0.0080 cm/cm
0.0060 - 0.0080 in/in
Lehmann & Voss LUVOCOM® 50-7216 Polycarbonate, with PTFE, easy flowing
Applications: Data processing machinery, precision engineering, film and photo industry, sporting and leisure goods, medical enineering.Improved friction and wear behaviour. Emergency running proper..
Linear Mold Shrinkage 0.0060 - 0.0080 cm/cm
0.0060 - 0.0080 in/in
Lehmann & Voss LUVOCOM® 50-8276 Polycarbonate, with PTFE
Applications: Data processing machinery, precision engineering, film and photo industry, sporting and leisure goods, medical enineering.High dimensionally stable precision parts, even at elevated te..
Linear Mold Shrinkage 0.0060 - 0.0080 cm/cm

@Temperature 23.0 °C
0.0060 - 0.0080 in/in

@Temperature 73.4 °F
Plumb; ASTM D955
Kingfa JE2-R2 ABS/PBT Alloy
Features:Low costExcellent balance propertiesGood processing propertiesGood heat stabilityGood size stabilityGood surfaceApplications:CD-ROM, DVDPrinter, scanner, photocopier cabinetElectric and ele..
Linear Mold Shrinkage 0.0060 cm/cm
0.0060 in/in
ASTM D955
Global GPP-130-C 30% Glass Filled Chemically Coupled Polypropylene
Information provided by Global Polymers Corporation.
Linear Mold Shrinkage 0.0060 cm/cm
0.0060 in/in
ASTM D955
Global PC-1415-R General Purpose Polycarbonate
Information provided by Global Polymers Corporation.
Linear Mold Shrinkage 0.0060 - 0.014 cm/cm
0.0060 - 0.014 in/in
ISO 294-4:1997
Inno-Comp INNOPOL® CS 1-3820 20% Glass-Fiber-Filled Polypropylene Homopolymer
INNOPOL® CS 1-3820 is a 20% glass-fiber-filled polypropylene homopolymer compound. This grade is available in natural and custom colored form.INNOPOL® CS 1-3820 is recommended for producing in..
Linear Mold Shrinkage 0.0060 cm/cm
0.0060 in/in
Isotropy
Solvay TECHNYL® A 218 V35 PA66, 35% glass fiber, DRY
Description: TECHNYL® A 218 V35 is a polyamide 66, reinforced with 35% of glass fiber, heat stabilized, for injection molding. This product is available in natural and black colors.Benefits: The ..
Linear Mold Shrinkage 0.0060 - 0.0080 cm/cm
0.0060 - 0.0080 in/in
ISO 294-4
Styrolution Novodur® 4105 ABS
Novodur Ultra 4105 is a PC modified high heat injection molding grade with high impact strength.Information provided by Styrolution
Linear Mold Shrinkage 0.0060 cm/cm
0.0060 in/in
ASTM D955
Styron Pulse® 2100LG ABS + PC
Information provided by DowThis product line was spun off from Dow Chemical to Styron in 2010.
Linear Mold Shrinkage 0.0060 - 0.018 cm/cm

@Thickness 3.20 mm,
Time 259000 sec
0.0060 - 0.018 in/in

@Thickness 0.126 in,
Time 72.0 hour
ISO 294
A. Schulman FORMION™ FI 120E Non-Reinforced, Extrusion Grade Zinc Ionomer
DescriptionFormion® FI 120E is a non-reinforced, transparent, extrusion grade Zinc Ionomer. It has been formulate for high durability, cut and puncture resistance, and low temperature ductility.Ap..
Linear Mold Shrinkage 0.0060 cm/cm
0.0060 in/in
ASTM D955
Tipco Tipcolite® TG 613 Phenolic Compound, Mineral & Wood Flour, Soft Flow & Good Surface Finish
Soft Flow Phenolic Compound, Reinforced with Mineral & Wood FlourApplications: General PurposeProcessing: Compression MoldingInformation provided by the Manufacturer, Tipco Industries Ltd., India...
Linear Mold Shrinkage 0.0060 cm/cm
0.0060 in/in
GB/15585
Zhejiang Juner PC-A6-2 Top-Grade Flame Retardant UV-Resistant
Applications: Top-Grade Wall Switch, BracketInformation provided by Zhejiang Juner New Materials Co, Ltd.
Linear Mold Shrinkage 0.0060 - 0.018 cm/cm

@Thickness 3.20 mm,
Time 259000 sec
0.0060 - 0.018 in/in

@Thickness 0.126 in,
Time 72.0 hour
ISO 294
A. Schulman FORMION™ FI 120 Non-Reinforced, Injection Molding Grade Zinc Ionomer
DescriptionFormion® FI 120 is a non-reinforced, transparent, injection molding grade Zinc Ionomer. It has been formulated for high durability, scratch resistance, low temperature ductility, and lo..
Linear Mold Shrinkage 0.0060 cm/cm

@Thickness 1.59 mm
0.0060 in/in

@Thickness 0.0625 in
ASTM D955
Plastics Group Polifil® GFPPCC-10 10% Glass Reinforced Polypropylene
Polifil® GFPPCC series compounds are homopolymer polypropylenes reinforced with chemically coupled glass fibers. These compounds offer superior strength and stiffness, improved elevated temperature..
Linear Mold Shrinkage 0.0060 - 0.0080 cm/cm
0.0060 - 0.0080 in/in
Polyram RamOfin PPC500 Polypropylene, Flame Retardant
Flame retardant polypropylene for injection molding applicationsInformation provided by Polyram Ram On Ind.
Linear Mold Shrinkage 0.0060 - 0.018 cm/cm

@Thickness 3.20 mm
0.0060 - 0.018 in/in

@Thickness 0.126 in
72 hr; ISO 294
A. Schulman FORMION™ FI 105 Non-Reinforced, Injection Molding Grade Sodium Ionomer
DescriptionFormion® FI 105 is a non-reinforced, transparent, injection molding grade Sodium Ionomer. It has been formulated for high durability, scratch resistance, low temperature ductility, and ..
Linear Mold Shrinkage 0.0060 cm/cm
0.0060 in/in
GB/15585
Zhejiang Juner PC-A2 Top-Grade Flame Retardant UV-Resistant
Applications: Top-Grade Wall Switch, BracketInformation provided by Zhejiang Juner New Materials Co, Ltd.
Linear Mold Shrinkage 0.0060 - 0.0080 cm/cm
0.0060 - 0.0080 in/in
ASTM D955
Covestro Makroblend® EL 703 Polycarbonate + Polyester-based Blend, Impact Modified, Flame-Retardant, UV Stabilized
Information provided by Bayer Corporation, Plastics DivisionAs of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and officially adopted its new name – Covestro.
Linear Mold Shrinkage 0.0060 cm/cm
0.0060 in/in
ASTM D955
Ashley Polymers Ashlene® 1641 Polycarbonate
A general purpose injection molding grade, natural resin, UL approved. Also available as: 1641R (with release); 1643 (with UV stabilizers); 1643R (with release and UV stabilizers).Data provided by ..
Linear Mold Shrinkage 0.0060 cm/cm
0.0060 in/in
BASF Ultramid® B3UG4 Grey 22975 20% Glass Filled PA66 FR (Conditioned)
Description: Halogen-free and phosphorus free flame retardant injection-molding grade with outstanding free-flow properties, good electrical properties and low smoke density; resistant to glow wire..
Linear Mold Shrinkage 0.0060 cm/cm
0.0060 in/in
ASTM D955
Aaron Industries AAROPRENE® GFPP 2010 Glass Filled Polypropylene
AAROPRENE® GFPP 2000 Series Glass Reinforced CompoundsMelt flow index may be specified. Color may be specified.
Linear Mold Shrinkage 0.0060 cm/cm
0.0060 in/in
ASTM D955
Ashley Polymers Ashlene® R3137 BK PC/PBT
A thermoplastic alloy offering a high level of chemical resistance combined with high impact and excellent mechanical properties. Black.Data provided by the manufacturer
Linear Mold Shrinkage 0.0060 cm/cm
0.0060 in/in
ASTM D955
Ashley Polymers Ashlene® P258 PPO
A high flow grade for applications requiring good impact strength and a high heat deflection temperature.Data provided by the manufacturer