| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DuPont Performance Polymers Zytel® 45HSB NC010 Nylon 66
(Unverified Data**).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Zytel® 45HSB NC010 is a high viscosity, heat stabilized polyamide 66 resin for injection molding and extrusion.Information provided by DuPont Performance Polymers
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.14 g/cc | 1.14 g/cc | DAM; ASTM D792 |
| Density | 1.14 g/cc | 0.0412 lb/in³ | DAM; ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.014 cm/cm @Thickness 2.00 mm |
0.014 in/in @Thickness 0.0787 in |
DAM; ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.014 cm/cm @Thickness 2.00 mm |
0.014 in/in @Thickness 0.0787 in |
DAM; ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 83.0 MPa @Temperature 23.0 °C |
12000 psi @Temperature 73.4 °F |
DAM; ASTM D638 |
| Tensile Strength, Yield | 55.0 MPa @Temperature 23.0 °C |
7980 psi @Temperature 73.4 °F |
50%RH; ISO 527 |
| 83.0 MPa @Temperature 23.0 °C |
12000 psi @Temperature 73.4 °F |
DAM; ISO 527 | |
| Elongation at Break | >= 50 % @Temperature 23.0 °C |
>= 50 % @Temperature 73.4 °F |
DAM; nominal; ISO 527 |
| >= 50 % @Temperature 23.0 °C |
>= 50 % @Temperature 73.4 °F |
50%RH; nominal; ISO 527 | |
| 90 % @Temperature 23.0 °C |
90 % @Temperature 73.4 °F |
DAM; ASTM D638 | |
| Elongation at Yield | 4.0 % @Temperature 23.0 °C |
4.0 % @Temperature 73.4 °F |
DAM; ISO 527 |
| 25 % @Temperature 23.0 °C |
25 % @Temperature 73.4 °F |
50%RH; ISO 527 | |
| Tensile Modulus | 1.30 GPa @Temperature 23.0 °C |
189 ksi @Temperature 73.4 °F |
50%RH; ISO 527 |
| 3.10 GPa @Temperature 23.0 °C |
450 ksi @Temperature 73.4 °F |
DAM; ISO 527 | |
| Flexural Modulus | 2.80 GPa @Temperature 23.0 °C |
406 ksi @Temperature 73.4 °F |
DAM; ISO 178 |
| 3.03 GPa @Temperature 23.0 °C |
439 ksi @Temperature 73.4 °F |
DAM; ASTM D790 | |
| Izod Impact, Notched | 0.640 J/cm @Temperature 23.0 °C |
1.20 ft-lb/in @Temperature 73.4 °F |
DAM; ASTM D256 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² @Temperature -40.0 °C |
2.86 ft-lb/in² @Temperature -40.0 °F |
DAM; ISO 180/1A |
| 6.00 kJ/m² @Temperature 23.0 °C |
2.86 ft-lb/in² @Temperature 73.4 °F |
DAM; ISO 180/1A | |
| Charpy Impact, Notched | 0.550 J/cm² @Temperature -30.0 °C |
2.62 ft-lb/in² @Temperature -22.0 °F |
DAM; ISO 179/1eA |
| 0.600 J/cm² @Temperature 23.0 °C |
2.86 ft-lb/in² @Temperature 73.4 °F |
DAM; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 500 µm/m-°C @Temperature 23.0 - 55.0 °C |
278 µin/in-°F @Temperature 73.4 - 131 °F |
DAM; ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 100 µm/m-°C @Temperature 23.0 - 55.0 °C |
55.6 µin/in-°F @Temperature 73.4 - 131 °F |
DAM; ISO 11359-1/-2 |
| Melting Point | 262 °C | 504 °F | 10°C/min; DAM; ISO 11357-1/-3 |
| 262 °C | 504 °F | DAM; ASTM D3418 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 200 °C | 392 °F | DAM; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 65.0 °C | 149 °F | DAM; ASTM D648 |
| 70.0 °C | 158 °F | DAM; ISO 75-1/-2 | |
| UL RTI, Electrical | 140 °C @Thickness 3.00 mm |
284 °F @Thickness 0.118 in |
DAM; UL 746B |
| 140 °C @Thickness 1.50 mm |
284 °F @Thickness 0.0591 in |
DAM; UL 746B | |
| 140 °C @Thickness 0.710 mm |
284 °F @Thickness 0.0280 in |
DAM; UL 746B | |
| UL RTI, Mechanical with Impact | 95.0 °C @Thickness 0.710 mm |
203 °F @Thickness 0.0280 in |
DAM; UL 746B |
| 110 °C @Thickness 1.50 mm |
230 °F @Thickness 0.0591 in |
DAM; UL 746B | |
| 110 °C @Thickness 3.00 mm |
230 °F @Thickness 0.118 in |
DAM; UL 746B | |
| UL RTI, Mechanical without Impact | 115 °C @Thickness 0.710 mm |
239 °F @Thickness 0.0280 in |
DAM; UL 746B |
| 125 °C @Thickness 1.50 mm |
257 °F @Thickness 0.0591 in |
DAM; UL 746B | |
| 125 °C @Thickness 3.00 mm |
257 °F @Thickness 0.118 in |
DAM; UL 746B | |
| Flammability, UL94 | HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
DAM; IEC 60695-11-10 |
| HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
DAM; IEC 60695-11-10 | |
| HB @Thickness 0.710 mm |
HB @Thickness 0.0280 in |
DAM; IEC 60695-11-10 | |
| HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
DAM; UL94 | |
| HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
DAM; UL94 | |
| HB @Thickness 0.710 mm |
HB @Thickness 0.0280 in |
DAM; UL94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Comparative Tracking Index | 600 V @Temperature 23.0 °C |
600 V @Temperature 73.4 °F |
DAM; UL 746A |
| >= 600 V @Temperature 23.0 °C |
>= 600 V @Temperature 73.4 °F |
DAM; UL 746A |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 280 - 290 °C | 536 - 554 °F | DAM; Extrusion |
| 285 °C | 545 °F | DAM; Optimum; Extrusion | |
| 290 °C | 554 °F | DAM; Optimum; Injection Molding | |
| 280 - 300 °C | 536 - 572 °F | DAM; Injection Molding | |
| Mold Temperature | 70.0 °C | 158 °F | DAM; optimum; Injection Molding |
| 50.0 - 90.0 °C | 122 - 194 °F | DAM; Injection Molding | |
| Drying Temperature | 80.0 °C | 176 °F | DAM; Extrusion |
| 80.0 °C | 176 °F | DAM; Injection Molding | |
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | DAM; Injection Molding |
| 4.00 - 6.00 hour | 4.00 - 6.00 hour | DAM; Extrusion | |
| Moisture Content | <= 0.050 % | <= 0.050 % | DAM; Extrusion |
| <= 0.050 % | <= 0.050 % | DAM; Injection Molding |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Additive | Heat Stabilizer | DAM |
| Appearance | Natural Color | DAM |
| Drying Recommended | Yes, if moisture content of resin exceeds recommended level | DAM |
| Extrudable - Coating | Yes | DAM |
| Extrudable - Filament | Yes | DAM |
| Extrudable - Sheet | Yes | DAM |
| Extrudable - Tubing | Yes | DAM |
| Features | Heat Aging Resistance, Good | DAM |
| Molecular Wt., High | DAM | |
| Viscosity, High | DAM | |
| Forms | Pellets | DAM |
| Generic | Nylon 66 | DAM |
| Heat Stabilized | Yes | DAM |
| Material Status | Current | DAM |
| Part Marking Code | >PA66< | ISO 11469; DAM |
| Polymer Family | Polyamide | DAM |
| Polymer Type | PA66 | DAM |
| Processing Method | Extrusion | DAM |
| Extrusion | DAM | |
| Injection Molding | DAM | |
| Product Category | Extrusion Resins | DAM |
| Unreinforced Resins | DAM | |
| Resin Identification | PA66 | ISO 1043; DAM |
| RoHS Compliance | Contact Manufacturer | DAM |
| Ultrasonic Weldable | Yes | DAM |
| Uses | Gears | DAM |
| Stock Material for Machining | DAM |
Users viewing this material also viewed the following:
- MV Labs CR1000 Cr2(SO4)3·xH2O Chromium(III) sulfate hydrate
- PolyOne Maxxam™ PPR-40G Nat Polypropylene Homopolymer (PP Homopolymer)
- Karina 40/447-FC-LMP Green Color Concentrate for PVC
- Lubrizol Estane® UB601 Thermoplastic Polyurethane
- Eagle Brass 302 Austenitic Stainless Steel, 1/2 Hardened
- CP-Polymer-Technik Wellamid® 6000 GV 10 HWCP 10% Glass Fiber Nylon 6, Heat Stabilized, Conditioned
- DuPont Teijin Films Mylar® RL43 Polyester Packaging Film, 50 Gauge
- BASF Quadrol® Specialty Polyol
Copyright © lookpolymers.com All Rights Reserved