GRECO ISOPAK 525 ABS Resin
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Molded |
| Manufacturer | GRECO |
| Trade Name | ISOPAK |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | GRECO ISOPAK 525 ABS Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
General Purpose Injection GradeInformation provided by Greater Eastern Resins Industrial Co., Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.03 g/cc | 1.03 g/cc | ASTM D792 |
| Water Absorption | 0.30 % @Temperature 23.0 °C, Time 86400 sec |
0.30 % @Temperature 73.4 °F, Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage | 0.0040 cm/cm | 0.0040 in/in | ASTM D955 |
| Melt Flow | 1.0 - 2.0 g/10 min @Load 5.00 kg, Temperature 200 °C |
1.0 - 2.0 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 110 | 110 | ASTM D785 |
| Tensile Strength | 50.0 MPa | 7250 psi | ASTM D638 |
| Elongation at Break | 25 % | 25 % | ASTM D412 |
| Flexural Yield Strength | 78.5 MPa | 11400 psi | ASTM D790 |
| Flexural Modulus | 2.55 GPa | 370 ksi | ASTM D790 |
| Izod Impact, Notched | 2.16 J/cm | 4.04 ft-lb/in | ASTM D256 A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 90.0 °C | 194 °F | ASTM D648 |
| UL RTI, Mechanical without Impact | 60.0 °C | 140 °F | UL-746B |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Hot Wire Ignition, HWI | 17 sec | 17 sec | .062" and above; UL-746A |
| High Amp Arc Ignition, HAI | 200 arcs | 200 arcs | .062" and above; UL-746A |
| High Voltage Arc-Tracking Rate, HVTR | 0.000 mm/min | 0.000 in/min | .062" and above; UL-746A |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Wire & Cable W2403 Polyvinyl Chloride, Flexible (PVC, Flexible)
- Polykemi AB POLYblend 45V GF10 PC/ABS-blend, Flame Retardant
- Nilit FRIANYL B63 SG-GV 2010 Nylon 6 for injection molding, 20% mineral filled and 10% glass fiber reinforced
- Tipco Tipcofil® AU 027 - Unfilled Nylon-6 Compound, with High Heat Stability, for Injection Molding
- Wellman EcoLon® 2200-BK1 Nylon 66, 40% Mineral/Glass Reinforced
- Hexcel® HexWeb® HRP - 3/16 - 8.0 Fiberglass/Phenolic Honeycomb
- DuPont™ Fusabond® E158 Polymer Modifier
- BASF Elastollan 1185 A FHF TPUR Flame Retardant Halogen Free
- Ashley Polymers Ashlene® 1061R Polycarbonate
Copyright © lookpolymers.com All Rights Reserved