- Victrex® WG101™ Polyaryletherketone
Victrex® WG101™ Polyaryletherketone
| Category | Polymer , Thermoplastic , Polyketone |
| Manufacturer | Victrex |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Victrex® WG101™ Polyaryletherketone.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Product Description: High performance thermoplastic material, PolyArylEtherKetone (PAEK), semi crystalline, black, granules for injection moulding, easy flow with wear additivesWG101 does not contain polyetrafluoroethylene (PTFE) or other halogenated additivesTypical Application Areas: Tribological applications with thin cross sections or long flow lengths, with higher strength and stiffness. Excellent wear resistance, very low coefficient of friction and low coefficient of thermal expansion. Chemically resistant to aggressive environments.Information provided by Victrex
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.44 g/cc | 0.0520 lb/in³ | Crystalline; ISO 1183 |
| Water Absorption | 0.30 % | 0.30 % | by immersion; ISO 62-1 |
| 0.60 % @Time 360000 sec |
0.60 % @Time 100 hour |
by immersion; ISO 62-1 | |
| Viscosity | 325000 cP @Temperature 400 °C |
325000 cP @Temperature 752 °F |
Melt; ISO 11443 |
| Linear Mold Shrinkage, Flow | 0.00 cm/cm | 0.00 in/in | 390°C nozzle, 200°C tool; ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0050 cm/cm | 0.0050 in/in | 390°C nozzle, 200°C tool; ISO 294-4 |
| Spiral Flow | 13.5 cm @Thickness 1.00 mm |
5.31 in @Thickness 0.0394 in |
390°C nozzle, 200°C tool; Victrex |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 85 | 85 | ISO 868 |
| Tensile Strength at Break | 55.0 MPa @Temperature 275 °C |
7980 psi @Temperature 527 °F |
ISO 527 |
| 65.0 MPa @Temperature 225 °C |
9430 psi @Temperature 437 °F |
ISO 527 | |
| 85.0 MPa @Temperature 175 °C |
12300 psi @Temperature 347 °F |
ISO 527 | |
| 125 MPa @Temperature 125 °C |
18100 psi @Temperature 257 °F |
ISO 527 | |
| 195 MPa @Temperature 23.0 °C |
28300 psi @Temperature 73.4 °F |
ISO 527 | |
| Elongation at Break | 1.8 % | 1.8 % | ISO 527 |
| Tensile Modulus | 19.5 GPa | 2830 ksi | ISO 527 |
| Flexural Strength | 70.0 MPa @Temperature 275 °C |
10200 psi @Temperature 527 °F |
ISO 178 |
| 140 MPa @Temperature 175 °C |
20300 psi @Temperature 347 °F |
ISO 178 | |
| 220 MPa @Temperature 125 °C |
31900 psi @Temperature 257 °F |
ISO 178 | |
| 290 MPa @Temperature 23.0 °C |
42100 psi @Temperature 73.4 °F |
ISO 178 | |
| Flexural Modulus | 17.0 GPa | 2470 ksi | ISO 178 |
| Compressive Strength | 45.0 MPa @Temperature 250 °C |
6530 psi @Temperature 482 °F |
ISO 604 |
| 65.0 MPa @Temperature 200 °C |
9430 psi @Temperature 392 °F |
ISO 604 | |
| 160 MPa @Temperature 120 °C |
23200 psi @Temperature 248 °F |
ISO 604 | |
| 230 MPa @Temperature 23.0 °C |
33400 psi @Temperature 73.4 °F |
ISO 604 | |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² | 2.86 ft-lb/in² | ISO 180/A |
| Izod Impact, Unnotched (ISO) | 35.0 kJ/m² | 16.7 ft-lb/in² | ISO 180/U |
| Charpy Impact Unnotched | 3.50 J/cm² | 16.7 ft-lb/in² | ISO 179/1eA |
| Charpy Impact, Notched | 0.500 J/cm² | 2.38 ft-lb/in² | ISO 179/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 9.00 µm/m-°C | 5.00 µin/in-°F | Below Tg; ISO 11359 |
| 10.0 µm/m-°C | 5.56 µin/in-°F | Above Tg; ISO 11359 | |
| CTE, linear, Transverse to Flow | 35.0 µm/m-°C | 19.4 µin/in-°F | Average below Tg; ISO 11359 |
| 85.0 µm/m-°C | 47.2 µin/in-°F | Average above Tg; ISO 11359 | |
| Thermal Conductivity | 1.30 W/m-K | 9.02 BTU-in/hr-ft²-°F | Average; ISO/CD 22007-4 |
| 2.20 W/m-K | 15.3 BTU-in/hr-ft²-°F | Along flow; ISO 22007-4 | |
| Melting Point | 343 °C | 649 °F | ISO 11357 |
| Deflection Temperature at 1.8 MPa (264 psi) | 343 °C | 649 °F | ISO 75-f |
| Glass Transition Temp, Tg | 143 °C | 289 °F | Onset; ISO 11357 |
| 147 °C | 297 °F | Midpoint; ISO 11357 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+8 ohm-cm | 1.00e+8 ohm-cm | 1V; IEC 60093 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | <= 100 °C | <= 212 °F | Hopper Temperature |
| Nozzle Temperature | 390 °C | 734 °F | |
| Zone 1 | 370 °C | 698 °F | |
| Zone 2 | 375 °C | 707 °F | |
| Zone 3 | 380 °C | 716 °F | |
| Zone 4 | 385 °C | 725 °F | |
| Mold Temperature | 180 - 210 °C | 356 - 410 °F | normal |
| <= 250 °C | <= 482 °F | ||
| Dry Time | 3 hour @Temperature 150 °C |
3 hour @Temperature 302 °F |
|
| 5 hour @Temperature 120 °C |
5 hour @Temperature 248 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Black | |
| Gate | > 2mm or 0.5 x part thickness | |
| Runner | Die/nozzle > 3mm, manifold > 3.5mm |