Polymer Property : Flexural Strength = 20300 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Strength	140 MPa @Temperature 175 °C	20300 psi @Temperature 347 °F	ISO 178
Victrex® WG101™ Polyaryletherketone Product Description: High performance thermoplastic material, PolyArylEtherKetone (PAEK), semi crystalline, black, granules for injection moulding, easy flow with wear additivesWG101 does not contai..
Flexural Strength	140 MPa @Temperature 20.0 Â°C	20300 psi @Temperature 68.0 Â°F
McDanel Advanced Ceramics MV-HR1 Mullite Mullite (3Al2O3 â€¢ 2SiO2) is a refractory oxide material combining low thermal expansion, good mechanical strength, and resilience at elevated temperatures. Mullite is formulated to produce den..
Flexural Strength	140 MPa @Strain 6.00 %	20300 psi @Strain 6.00 %	cond., 2 mm/min; ISO 178-A
Lanxess DurethanÂ® AM 40 X H2.0 901510 Nylon 66, Glass Fiber/Mineral Reinforced PA 66, 40% glass fibers/mineral, injection molding, heat-aging stabilized, low tendency to warpInformation provided by LANXESS.
Flexural Strength	140 MPa @Temperature 80.0 °C	20300 psi @Temperature 176 °F	Absolute Drying; ASTM-D790
Toyobo GLAMIDE® T-602G30 MXD66 GLAMIDE® is very tough and exhibits high abrasion resistance. It has a high melting point and heat resistance, has well-balanced proportions of mechanical properties, performs self-distinguishing a..
Flexural Strength	140 MPa @Temperature -40.0 °C	20300 psi @Temperature -40.0 °F	Absolute Drying; ASTM-D790
Toyobo GLAMIDE® T-662 Nylon-66 GLAMIDE® is very tough and exhibits high abrasion resistance. It has a high melting point and heat resistance, has well-balanced proportions of mechanical properties, performs self-distinguishing a..
Flexural Strength	140 MPa @Temperature 80.0 °C	20300 psi @Temperature 176 °F	Practical Use (Water Absorption 1.75%); ASTM-D790
Toyobo GLAMIDE® T-665C30 Nylon-66 GLAMIDE® is very tough and exhibits high abrasion resistance. It has a high melting point and heat resistance, has well-balanced proportions of mechanical properties, performs self-distinguishing a..
Flexural Strength	140 MPa @Temperature 23.0 °C	20300 psi @Temperature 73.4 °F	Absolute Drying; ASTM-D790
Toyobo GLAMIDE® T-777-02 Nylon-6 GLAMIDE® is very tough and exhibits high abrasion resistance. It has a high melting point and heat resistance, has well-balanced proportions of mechanical properties, performs self-distinguishing a..
Flexural Strength	140 MPa @Temperature -40.0 °C	20300 psi @Temperature -40.0 °F	Absolute Drying; ASTM-D790
Toyobo GLAMIDE® T-803 Nylon-6 GLAMIDE® is very tough and exhibits high abrasion resistance. It has a high melting point and heat resistance, has well-balanced proportions of mechanical properties, performs self-distinguishing a..
Flexural Strength	140 MPa @Temperature 23.0 °C	20300 psi @Temperature 73.4 °F	Absolute Drying; ASTM-D790
Toyobo GLAMIDE® TY-145TZ Nylon-6 GLAMIDE® is very tough and exhibits high abrasion resistance. It has a high melting point and heat resistance, has well-balanced proportions of mechanical properties, performs self-distinguishing a..
Flexural Strength	140 MPa @Temperature -40.0 °C	20300 psi @Temperature -40.0 °F	Absolute Drying; ASTM-D790
Toyobo GLAMIDE® T-779 Nylon-6 GLAMIDE® is very tough and exhibits high abrasion resistance. It has a high melting point and heat resistance, has well-balanced proportions of mechanical properties, performs self-distinguishing a..