Polymer Property : CTE, linear, Parallel to Flow = 5.56 µin/in-°F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 10.0 - 15.0 µm/m-°C @Temperature 50.0 - 150 °C |
5.56 - 8.33 µin/in-°F @Temperature 122 - 302 °F |
ISO 11359-2 |
| Raschig Group DECAL® 666/8/2B Phenolic Glass-fiber reinforced phenolic molding compound. Excellent heat resistance, low mould shrinkage and post-shrinkage, good chemical resistance and mechanical properties. This product meets the allowe.. |
|||
| CTE, linear, Parallel to Flow | 10.0 - 15.0 µm/m-°C @Temperature 50.0 - 150 °C |
5.56 - 8.33 µin/in-°F @Temperature 122 - 302 °F |
ISO 11359-2 |
| Raschig Group DECAL® 937 Phenolic Mica reinforced phenolic molding compound. This product meets the allowed upper limits for heavy metals and PCAs and also conforms to the requirements of the EU directives 2002/95 (RoHS), 2002/96 (W.. |
|||
| CTE, linear, Parallel to Flow | 10.0 µm/m-°C @Temperature 20.0 °C |
5.56 µin/in-°F @Temperature 68.0 °F |
ASTM E381 |
| Solvay Specialty Polymers Kadel® E-1300 Polyketone
(discontinued **) High performance proprietary semi-crystalline polymer based resins with exceptional solvent resistance and high temperature performance. They provide strength and stiffness, plus superior chemical r.. |
|||
| CTE, linear, Parallel to Flow | 10.0 µm/m-°C | 5.56 µin/in-°F | Above Tg; ISO 11359 |
| Victrex® WG101™ Polyaryletherketone Product Description: High performance thermoplastic material, PolyArylEtherKetone (PAEK), semi crystalline, black, granules for injection moulding, easy flow with wear additivesWG101 does not contai.. |
|||
| CTE, linear, Parallel to Flow | 10.0 - 20.0 µm/m-°C @Temperature 50.0 - 100 °C |
5.56 - 11.1 µin/in-°F @Temperature 122 - 212 °F |
ISO 11359-2 |
| Raschig Group SURAPLAST UPA 63 UP Glass fiber reinforced polyester molding compound. Minimal mold shrinkage and post-shrinkage, very good arc resistance, very good mechanical strength. This product meets the allowed upper limits for.. |
|||
| CTE, linear, Parallel to Flow | 10.0 µm/m-°C @Temperature 20.0 °C |
5.56 µin/in-°F @Temperature 68.0 °F |
ISO 11359-1/-2 |
| DSM Akulon® Ultraflow™ K-FG0 Nylon 6-50% Glass Reinforced (European and Asian Grade) (Dry)
(discontinued **)& The Akulon® product portfolio is engineered for optimum performance to suit different processing techniques and end use markets. Akulon Nylon 6 is used for extrusion applications including barrier .. |
|||
| CTE, linear, Parallel to Flow | 10.0 µm/m-°C | 5.56 µin/in-°F | ISO 11359-1/-2 |
| Lanxess Durethan® DP BKV 60 H2.0 EF 900116 Nylon 6, 60% Glass Fiber PA 6, injection molding grade, 60% glass fibers, low viscosity, good flowability (Easy Flow), good heat-resistanceApplication Examples: gearbox housings, spring holders, automotive door handles |
|||
| CTE, linear, Parallel to Flow | 10.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
5.56 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| SABIC Innovative Plastics LNP STAT-KON EE004 PEI (Asia Pacific) LNP* Stat-kon* EE004 is a compound based on Polyetherimide resin containing Carbon Fiber. Added features of this material include: Electrically Conductive. |
|||
| CTE, linear, Parallel to Flow | 10.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
5.56 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| SABIC Innovative Plastics LNP THERMOCOMP EC004XXC PEI (Asia Pacific) LNP* Thermocomp* EC004XXC is a compound based on Polyetherimide resin containing Carbon Fiber. Added features of this material include: Electrically Conductive. |
|||
| CTE, linear, Parallel to Flow | 10.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
5.56 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| SABIC Innovative Plastics LNP THERMOCOMP LX04015 PEEK (Europe-Africa-Middle East) LNP* THERMOCOMP* LX04015 is a compound based on Polyetheretherketone containing Carbon Fiber. Added features include: Electrically Conductive |
|||
| CTE, linear, Parallel to Flow | 10.0 µm/m-°C | 5.56 µin/in-°F | ASTM E831 |
| Sumitomo Bakelite North America CF 9040A Carbon Fiber Reinforced Phenolic CF 9040A is a high strength carbon fiber phenolic molding compoundInformation provided by Sumitomo Bak North America, Inc. |
|||
| CTE, linear, Parallel to Flow | 10.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
5.56 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| SABIC Innovative Plastics LNP STAT-KON DE003E PC (Europe-Africa-Middle East) LNP* Stat-kon* DE003E is a compound based on Polycarbonate resin containing Carbon Fiber. Added features of this material include: Easy Molding, Electrically Conductive. |
|||
| CTE, linear, Parallel to Flow | 10.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
5.56 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| SABIC Innovative Plastics LNP STAT-KON EE004 PEI (Europe-Africa-Middle East) LNP* Stat-kon* EE004 is a compound based on Polyetherimide resin containing Carbon Fiber. Added features of this material include: Electrically Conductive. |
|||
| CTE, linear, Parallel to Flow | 10.0 µm/m-°C | 5.56 µin/in-°F | ISO 11359-1/-2 |
| EMS-Grivory Grivory® 1SVX-65H black 9288 PA1010-GF65 Product Description: Grilamid 1SVX-65H black is a 65% glass fiber reinforced Polyamide 1010 injection molding grade with the following product profile: Raw materials based on renewable resources Exc.. |
|||
| CTE, linear, Parallel to Flow | 10.0 µm/m-°C | 5.56 µin/in-°F | ISO 11359-1/-2 |
| EMS-Grivory Grivory® GC-4H PA*-CF40 Product description: Grivory GC-4H is a 40% carbon-fiber reinforced engineering thermoplastic material based on a combination of semi-crystalline polyamide with partially aromatic copolyamide. Grivo.. |
|||
| CTE, linear, Parallel to Flow | 10.0 µm/m-°C | 5.56 µin/in-°F | ISO 11359-1/-2 |
| EMS-Grivory Grivory® GV-2H black PA*-GF20 Product description: Grivory GV-2H is a 20% glass-fiber reinforced engineering thermoplastic material based on a combination of semicrystalline polyamide with partially aromatic copolyamide. Grivory.. |
|||
| CTE, linear, Parallel to Flow | 10.0 µm/m-°C | 5.56 µin/in-°F | ISO 11359-1/-2 |
| EMS-Grivory Grivory® GVX-7 H black 9915 PA*-GF70 Product description: Grivory GVX-7H black 9915 is a 70% glass fiber reinforced engineering thermoplastic material based on a combination of semicrystalline polyamide with partially aromatic copolyam.. |
|||
| CTE, linear, Parallel to Flow | 10.0 µm/m-°C | 5.56 µin/in-°F | ISO 11359-1/-2 |
| EMS-Grivory Grivory® XE 4108 black 9992 PA612-GF50 Product description: Grilamid XE 4108 black 9992 is a 50% glass fiber reinforced, heat stabilized polyamide 612 injection molding grade. The main features of Grilamid XE 4108 are: low water absorpti.. |
|||
| CTE, linear, Parallel to Flow | 10.0 µm/m-°C | 5.56 µin/in-°F | ISO 11359-1/-2 |
| EMS-Grivory Grivory® XE 4108 nat PA612-GF50 Product description: Grilamid XE 4108 natural is a 50% glass fiber reinforced, heat stabilized polyamide 612 injection molding grade. The main features of Grilamid XE 4108 are: low water absorptiong.. |
|||
| CTE, linear, Parallel to Flow | 10.0 µm/m-°C | 5.56 µin/in-°F | ISO 11359-1/-2 |
| EMS-Grivory Grivory® XE 4116 black 9288 PA1010-GF55 Product description: Grilamid XE 4116 black 9288 is a 55% glass fiber reinforced Polyamide 1010 injection molding grade. This grade is especially suitable for the manufacturing of thin-walled, paint.. |
|||
| CTE, linear, Parallel to Flow | 10.0 µm/m-°C | 5.56 µin/in-°F | DAM; ISO 11359-1/-2 |
| DuPont Performance Polymers Zytel® 77G43L BK031 Nylon 612
(Unverified Data**) 43% Glass Reinforced Polyamide 612Information provided by DuPont Performance Polymers |
|||
| CTE, linear, Parallel to Flow | 10.0 µm/m-°C @Temperature 20.0 °C |
5.56 µin/in-°F @Temperature 68.0 °F |
ISO 11359-1/-2 |
| DSM Akulon® K224-G0 (Dry) 50% Glass Reinforced Nylon 6 (North America) Description: The Akulon portfolio is engineered for optimum performance to suit different processing techniques and end use markets.Unfilled Extrusion ResinsAkulon resins are available with melt vis.. |
|||
| CTE, linear, Parallel to Flow | 10.0 µm/m-°C @Temperature 20.0 °C |
5.56 µin/in-°F @Temperature 68.0 °F |
ISO 11359-1/-2 |
| DSM Akulon® Ultraflow™ K-FHG0 Nylon 6-50% Glass Reinforced (European Grade) (Dry) The Akulon® product portfolio is engineered for optimum performance to suit different processing techniques and end use markets. Akulon Nylon 6 is used for extrusion applications including barrier .. |
|||
| CTE, linear, Parallel to Flow | 10.0 µm/m-°C | 5.56 µin/in-°F | ISO 11359-1/-2 |
| EMS-Grivory Grivory® LBV-65H FWA black 9225 PA12-GF65 Product description: Grilamid LBV-65H FWA black 9225 is a 65% glass fiber reinforced, heat stabilized polyamide 12 injection molding grade with the following special features High stiffness combined.. |
|||
| CTE, linear, Parallel to Flow | 10.0 µm/m-°C @Thickness 2.00 mm, Temperature 23.0 - 55.0 °C |
5.56 µin/in-°F @Thickness 0.0787 in, Temperature 73.4 - 131 °F |
ISO 11359-2 |
| Ascend Performance Materials Vydyne® 21SPF BLK Nylon 66, Conditioned Vydyne® 21SPF BLK is a, general-purpose PA66 resin used for extrusion-compounding. Available in black, it is designed principally for injection-molding fabrication. This grade offers a well-balance.. |
|||
| CTE, linear, Parallel to Flow | 10.0 µm/m-°C @Thickness 2.00 mm, Temperature 23.0 - 55.0 °C |
5.56 µin/in-°F @Thickness 0.0787 in, Temperature 73.4 - 131 °F |
ISO 11359-2 |
| Ascend Performance Materials Vydyne® M344 BLK Nylon 66, Flame Retardant, DAM Vydyne® M344 BLK is a halogenated, unfilled, flame-retardant PA66/6 copolymer designed with excellent strength and toughness. It is lubricated for machine feed and easy mold release and has Underwr.. |
|||
| CTE, linear, Parallel to Flow | 10.0 - 15.0 µm/m-°C @Temperature 23.0 - 80.0 °C |
5.56 - 8.33 µin/in-°F @Temperature 73.4 - 176 °F |
ISO 11359-1/-2 |
| BASF Ultramid® B3G8 BK00564 40% Glass Filled PA6 (Dry) Ultramid B3G8 BK00564 is a 40% glass filled, pigmented black, injection molding PA6 grade. |
|||
| CTE, linear, Parallel to Flow | 10.0 µm/m-°C @Thickness 2.00 mm, Temperature 23.0 - 55.0 °C |
5.56 µin/in-°F @Thickness 0.0787 in, Temperature 73.4 - 131 °F |
ISO 11359-2 |
| Ascend Performance Materials Vydyne® 75HF Nylon 66/6, Heat Stabilized, DAM Vydyne® 75HF is a medium-high-viscosity, heat-stabilized PA66/6 copolymer resin designed for extrusion applications. It is available in natural color only. Vydyne 75HF resin offers a well-balanced .. |
|||
| CTE, linear, Parallel to Flow | 10.0 - 15.0 µm/m-°C @Temperature 23.0 - 80.0 °C |
5.56 - 8.33 µin/in-°F @Temperature 73.4 - 176 °F |
DIN 11359-1/-2 |
| BASF Ultramid® B3WG10 BK 00564 50% Glass Filled PA6 (Dry) Description: 50% glass-fiber reinforced and heat aging resistant injection-molding grade for technical parts with very high stiffness.Information provided by BASF |
|||
| CTE, linear, Parallel to Flow | 10.0 µm/m-°C @Thickness 2.00 mm, Temperature 23.0 - 55.0 °C |
5.56 µin/in-°F @Thickness 0.0787 in, Temperature 73.4 - 131 °F |
ISO 11359-2 |
| Ascend Performance Materials Vydyne® 22HSP NT Nylon 66, DAM Availability:Asia PacificEuropeNorth AmericaAdditive: Lubricant Features:Fast Molding CycleGasoline ResistanceGeneral PurposeGood Abrasion ResistanceGood Chemical ResistanceGood Mold ReleaseGood Tou.. |
|||