Toyobo GLAMIDE® T-662 Nylon-66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Unreinforced, Flame Retardant |
| Manufacturer | Toyobo |
| Trade Name | GLAMIDE® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Toyobo GLAMIDE® T-662 Nylon-66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
GLAMIDE® is very tough and exhibits high abrasion resistance. It has a high melting point and heat resistance, has well-balanced proportions of mechanical properties, performs self-distinguishing and a specific grade approved as UL94V-0 class is provided, and it exhibits excellent chemical resistance and oil resistance. Grade T-662 is a standard type, non-reinforced Nylon-66.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.14 g/cc | 1.14 g/cc | Absolute Drying; ASTM-D792 |
| Water Absorption | 1.2 % | 1.2 % | Absolute Drying; ASTM-D570 |
| Moisture Absorption at Equilibrium | 2.5 % | 2.5 % | Absolute Drying; ASTM-D570 |
| Linear Mold Shrinkage | 0.0060 - 0.012 cm/cm @Thickness 1.00 mm |
0.0060 - 0.012 in/in @Thickness 0.0394 in |
Absolute Drying |
| 0.015 - 0.022 cm/cm @Thickness 3.00 mm |
0.015 - 0.022 in/in @Thickness 0.118 in |
Absolute Drying |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 120 | 120 | Absolute Drying; ASTM-D785 |
| Tensile Strength, Ultimate | 28.0 MPa @Temperature 80.0 °C |
4060 psi @Temperature 176 °F |
Practical Use (Water Absorption 2.5%); ASTM-D638 |
| 38.0 MPa @Temperature 80.0 °C |
5510 psi @Temperature 176 °F |
Absolute Drying; ASTM-D638 | |
| 50.0 MPa @Temperature 23.0 °C |
7250 psi @Temperature 73.4 °F |
Practical Use (Water Absorption 2.5%); ASTM-D638 | |
| 82.0 MPa @Temperature 23.0 °C |
11900 psi @Temperature 73.4 °F |
Absolute Drying; ASTM-D638 | |
| 110 MPa @Temperature -40.0 °C |
16000 psi @Temperature -40.0 °F |
Practical Use (Water Absorption 2.5%); ASTM-D638 | |
| 116 MPa @Temperature -40.0 °C |
16800 psi @Temperature -40.0 °F |
Absolute Drying; ASTM-D638 | |
| Elongation at Break | 120 % | 120 % | Absolute Drying; ASTM-D638 |
| >= 200 % | >= 200 % | Practical Use (Water Absorption 2.5%); ASTM-D638 | |
| Flexural Strength | 40.0 MPa @Temperature 80.0 °C |
5800 psi @Temperature 176 °F |
Practical Use (Water Absorption 2.5%); ASTM-D790 |
| 66.0 MPa @Temperature 23.0 °C |
9570 psi @Temperature 73.4 °F |
Practical Use (Water Absorption 2.5%); ASTM-D790 | |
| 66.0 MPa @Temperature 80.0 °C |
9570 psi @Temperature 176 °F |
Absolute Drying; ASTM-D790 | |
| 117 MPa @Temperature 23.0 °C |
17000 psi @Temperature 73.4 °F |
Absolute Drying; ASTM-D790 | |
| 120 MPa @Temperature -40.0 °C |
17400 psi @Temperature -40.0 °F |
Practical Use (Water Absorption 2.5%); ASTM-D790 | |
| 140 MPa @Temperature -40.0 °C |
20300 psi @Temperature -40.0 °F |
Absolute Drying; ASTM-D790 | |
| Flexural Modulus | 0.600 GPa @Temperature 80.0 °C |
87.0 ksi @Temperature 176 °F |
Practical Use (Water Absorption 2.5%); ASTM-D790 |
| 1.00 GPa @Temperature 80.0 °C |
145 ksi @Temperature 176 °F |
Absolute Drying; ASTM-D790 | |
| 1.40 GPa @Temperature 23.0 °C |
203 ksi @Temperature 73.4 °F |
Practical Use (Water Absorption 2.5%); ASTM-D790 | |
| 2.90 GPa @Temperature 23.0 °C |
421 ksi @Temperature 73.4 °F |
Absolute Drying; ASTM-D790 | |
| 4.00 GPa @Temperature -40.0 °C |
580 ksi @Temperature -40.0 °F |
Practical Use (Water Absorption 2.5%); ASTM-D790 | |
| 4.30 GPa @Temperature -40.0 °C |
624 ksi @Temperature -40.0 °F |
Absolute Drying; ASTM-D790 | |
| Compressive Strength | 90.0 MPa | 13100 psi | Absolute Drying; ASTM-D695 |
| Izod Impact, Notched | 0.350 J/cm @Temperature -40.0 °C |
0.656 ft-lb/in @Temperature -40.0 °F |
Absolute Drying; ASTM-D256 |
| 0.400 J/cm @Temperature -40.0 °C |
0.749 ft-lb/in @Temperature -40.0 °F |
Practical Use (Water Absorption 2.5%); ASTM-D256 | |
| 0.450 J/cm @Temperature 23.0 °C |
0.843 ft-lb/in @Temperature 73.4 °F |
Absolute Drying; ASTM-D256 | |
| 3.00 J/cm @Temperature 23.0 °C |
5.62 ft-lb/in @Temperature 73.4 °F |
Practical Use (Water Absorption 2.5%); ASTM-D256 | |
| Taber Abrasion, mg/1000 Cycles | 8.0 | 8.0 | CS-17, Absolute Drying; ASTM-D1044 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 80.0 µm/m-°C | 44.4 µin/in-°F | Absolute Drying; ASTM-D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 230 °C | 446 °F | Absolute Drying; ASTM-D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 80.0 °C | 176 °F | Absolute Drying; ASTM-D648 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+9 - 1.00e+10 ohm-cm | 1.00e+9 - 1.00e+10 ohm-cm | Practical Use (Water Absorption 2.5%); ASTM-D257 |
| 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | Absolute Drying; ASTM-D257 | |
| Dielectric Constant | 3.9 @Frequency 1000 Hz |
3.9 @Frequency 1000 Hz |
Absolute Drying; ASTM-D150 |
| 6.5 @Frequency 1000 Hz |
6.5 @Frequency 1000 Hz |
Practical Use (Water Absorption 2.5%); ASTM-D150 | |
| Dielectric Strength | 13.0 kV/mm @Thickness 2.00 mm |
330 kV/in @Thickness 0.0787 in |
Practical Use (Water Absorption 2.5%); ASTM-D149 |
| 20.0 kV/mm @Thickness 2.00 mm |
508 kV/in @Thickness 0.0787 in |
Absolute Drying; ASTM-D149 | |
| Arc Resistance | 110 sec | 110 sec | Practical Use (Water Absorption 2.5%); ASTM-D495 |
| 120 sec | 120 sec | Absolute Drying; ASTM-D495 | |
| Comparative Tracking Index | >= 600 V | >= 600 V | IEC Method |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 270 - 290 °C | 518 - 554 °F | |
| Mold Temperature | 40.0 - 80.0 °C | 104 - 176 °F | |
| Injection Pressure | 30.0 - 40.0 MPa | 4350 - 5800 psi |