Polymer Property : Flexural Strength = 17000 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Strength	117 MPa @Thickness 1.57 mm	17000 psi @Thickness 0.0620 in	CW; ASTM D790
Industrial Laminates/Norplex NP310 Cotton Fabric Description: Canvas machining grade for structural and mechanical applications. Better impact strength than phenolic paper grades. MIL-I-24768/16. Thickness Tested: 0.062, 0.125", and 0.500".
Flexural Strength	117 MPa @Thickness 1.57 mm	17000 psi @Thickness 0.0620 in	CW; ASTM D790
Industrial Laminates/Norplex NP313 Cotton Fabric Description: Canvas phenolic laminate with molybdenum disulfide lubricant. Mechanical properties slightly lower than NP310.Thickness Tested: 0.062", 0.125" & 0.500"
Flexural Strength	117 MPa @Thickness 1.57 mm	17000 psi @Thickness 0.0620 in	CW; ASTM D790
Industrial Laminates/Norplex NP629 Paper Base Laminate Description: It is a paper-phenolic high-pressure laminate. It is intended primarily for mechanical applications and is suitable for electrical applications as well. Thickness Tested: 0.062", 0.125"..
Flexural Strength	117 MPa @Thickness 1.57 mm	17000 psi @Thickness 0.0620 in	LW; ASTM D790
Industrial Laminates/Norplex NP318 Cotton Fabric Description: Post-forming canvas phenolic material. Mechanical and electrical properties similar to NP310E. It is made from a cotton fabric weighing more than 4 ounces per square yard and having a t..
Flexural Strength	117 MPa @Thickness 1.57 mm	17000 psi @Thickness 0.0620 in	CW; ASTM D790
Industrial Laminates/Norplex NP625 Paper Base Laminate Description: Paper phenolic grade with better moisture resistance than NP612. Requires less heat to punch and shear than NP611.
Flexural Strength	117 MPa @Temperature 23.0 °C	17000 psi @Temperature 73.4 °F	Absolute Drying; ASTM-D790
Toyobo GLAMIDE® T-662 Nylon-66 GLAMIDE® is very tough and exhibits high abrasion resistance. It has a high melting point and heat resistance, has well-balanced proportions of mechanical properties, performs self-distinguishing a..