- Solvay Specialty Polymers AvaSpire® AV-651 CF30 Polyaryletherketone (PAEK), 30% Carbon Fiber
Solvay Specialty Polymers AvaSpire® AV-651 CF30 Polyaryletherketone (PAEK), 30% Carbon Fiber
| Category | Polymer , Thermoplastic , Polyketone , Polyaryletherketone (PAEK), Carbon Fiber Filled |
| Manufacturer | Solvay Specialty Polymers |
| Trade Name | AvaSpire® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay Specialty Polymers AvaSpire® AV-651 CF30 Polyaryletherketone (PAEK), 30% Carbon Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
AvaSpire® AV-651 CF30 is a 30% carbon fiber reinforced version of AvaSpire® AV-651. This formulation offers some advantages relative to 30% carbon fiber reinforced PEEK which include better dimensional stability and warp resistance during injection molding. The AV-651 CF30 grade offers the highest strength, stiffness, and fatigue resistance of any AV-651-based grade. Furthermore, this resin generally retains most of the desirable ultra-performance attributes of carbon fiber reinforced PEEK. Those attributes include chemical resistance, fatigue resistance, and long term thermal oxidative stability.Features: Autoclave Sterilizable; E-beam Sterilizable; Ethylene Oxide Sterilizable; Fatigue Resistant; Flame Retardant; Good Chemical Resistance; Good Dimensional Stability; Good Sterilizability; Heat Sterilizable; High Heat Resistance; High Stiffness; High Strength; Radiation (Gamma) Resistant; Radiation Sterilizable; Radiotranslucent; Steam Resistant; Steam SterilizableUses: Dental Applications; Hospital Goods; Medical Devices; Medical/Healthcare Applications; Pump Parts; Seals; Surgical InstrumentsInjection Molding Notes: Back Pressure: MinimumInformation provided by Solvay Specialty Polymers.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.42 g/cc | 0.0513 lb/in³ | ASTM D792 |
| Filler Content | 30 % | 30 % | Carbon Fiber |
| Water Absorption | 0.20 % @Time 86400 sec |
0.20 % @Time 24.0 hour |
ISO 62 |
| Viscosity | 540000 cP @Shear Rate 1000 1/s, Temperature 400 °C |
540000 cP @Shear Rate 1000 1/s, Temperature 752 °F |
Melt Viscosity; ASTM D3835 |
| Linear Mold Shrinkage, Flow | 0.00 - 0.0020 cm/cm @Thickness 3.18 mm |
0.00 - 0.0020 in/in @Thickness 0.125 in |
|
| Linear Mold Shrinkage, Transverse | 0.0090 - 0.011 cm/cm @Thickness 3.18 mm |
0.0090 - 0.011 in/in @Thickness 0.125 in |
ASTM D955 |
| Melt Flow | 4.5 g/10 min @Load 2.16 kg, Temperature 400 °C |
4.5 g/10 min @Load 4.76 lb, Temperature 752 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 104 | 104 | ASTM D785 |
| Tensile Strength | 184 MPa | 26700 psi | 5 mm/min; ASTM D638 |
| Tensile Strength, Yield | 192 MPa | 27800 psi | 5 mm/min, Type 1A; ISO 527-2 |
| Elongation at Break | 1.5 % | 1.5 % | Type 1A, 5 mm/min; ISO 527-2 |
| 1.5 % | 1.5 % | 5 mm/min; ASTM D638 | |
| Tensile Modulus | 20.7 GPa | 3000 ksi | 5 mm/min; ASTM D638 |
| 21.1 GPa | 3060 ksi | 1 mm/min, Type 1A; ISO 527-2 | |
| Flexural Strength | 262 MPa | 38000 psi | ASTM D790 |
| 280 MPa | 40600 psi | ISO 178 | |
| Flexural Modulus | 17.2 GPa | 2490 ksi | ASTM D790 |
| 19.1 GPa | 2770 ksi | ISO 178 | |
| Compressive Strength | 168 MPa | 24400 psi | ASTM D695 |
| Shear Strength | 94.0 MPa | 13600 psi | ASTM D732 |
| Izod Impact, Notched | 0.590 J/cm | 1.11 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 5.90 J/cm | 11.1 ft-lb/in | ASTM D256 |
| Izod Impact, Notched (ISO) | 8.40 kJ/m² | 4.00 ft-lb/in² | ISO 180 |
| Izod Impact, Unnotched (ISO) | 37.0 kJ/m² | 17.6 ft-lb/in² | ISO 180 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 8.20 µm/m-°C @Temperature -50.0 - 50.0 °C |
4.56 µin/in-°F @Temperature -58.0 - 122 °F |
1 |
| Specific Heat Capacity | 1.32 J/g-°C @Temperature 50.0 °C |
0.315 BTU/lb-°F @Temperature 122 °F |
ASTM C351 |
| 1.77 J/g-°C @Temperature 200 °C |
0.423 BTU/lb-°F @Temperature 392 °F |
ASTM C351 | |
| Thermal Conductivity | 0.360 W/m-K | 2.50 BTU-in/hr-ft²-°F | ASTM C177 |
| Melting Point | 345 °C | 653 °F | ASTM D3418 |
| Deflection Temperature at 1.8 MPa (264 psi) | 212 °C @Thickness 3.20 mm |
414 °F @Thickness 0.126 in |
Annealed; ASTM D648 |
| Glass Transition Temp, Tg | 158 °C | 316 °F | DSC |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 366 °C | 691 °F | |
| Middle Barrel Temperature | 371 °C | 700 °F | |
| Front Barrel Temperature | 377 °C | 711 °F | |
| Nozzle Temperature | 382 °C | 720 °F | |
| Melt Temperature | 366 - 388 °C | 691 - 730 °F | |
| Mold Temperature | 149 - 177 °C | 300 - 351 °F | |
| Drying Temperature | 149 °C @Time 14400 sec |
300 °F @Time 4.00 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| Latin America | ||
| North America | ||
| Color | Black | |
| Form | Pellets | |
| Injection Rate | Fast | |
| Processing Technique | Injection Molding; Machining; Profile Extrusion | |
| RoHS Compliance | RoHS Compliant | |
| Screw Compression Ratio | 2.0:1.0 to 3.0:1.0 |
Users viewing this material also viewed the following:
- High Temp Metals Alloy 49 Iron-Nickel High Permeability Alloy, Strip, Formed and Deep Draw Quality
- Fibre Glast 180 Clear Gel Coat
- Lanxess Durethan® BM 240 000000 Nylon 6, Mineral Reinforced
- A. Schulman POLYTROPE™ TPP 1010E-01 Olefinic Elastomer For Sheet Extrusion
- E-Polymers TEKAMID® HG10L 10% Glass Fiber Reinforced High Impact PA/ABS Alloy
- Colorite Polymers Weatherflex™ CS1521WX (NTL01B) Wire and Cable Vinyl Compound
- Arkema Group Nakan® RMA 705 N PVC, Rigid Injection Molding Grade
- Asahi Kasei Thermofil P-9900-0576 Unreinforced, Flame Retardant, Heat Stabilized
- BASF Pluracol® 1528 FF Molded Foam Polyol
- ATI Allegheny Ludlum Stainless Steel Chromium-Nickel Type 304, 0% Cold Rolled (UNS S30400)
Copyright © lookpolymers.com All Rights Reserved