Polymer Property : Flexural Strength = 40600 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Strength	<= 280 MPa	<= 40600 psi	ISO 178
Polykemi AB SCANMID 6 B11^ F45 Nylon 6, Glass Fiber Reinforced Information provided by Polykemi AB
Flexural Strength	280 MPa	40600 psi	ISO 178
Solvay Specialty Polymers AvaSpire® AV-651 CF30 Polyaryletherketone (PAEK) (Unverified Data**) AvaSpire AV-651 CF30 is a 30% carbon fiber reinforced version of AvaSpire AV-651. This formulation offers some advantages relative to 30% carbon fiber reinforced PEEK which include better dimensiona..
Flexural Strength	280 MPa @Temperature 22.0 Â°C	40600 psi @Temperature 71.6 Â°F	25 mm wide 100 mm long, flat samples; ISO 14125
Menzolit MenzolitÂ® SMC 1100 Unsaturated Polyester UP SMC 1100 is a special vinylester SMC for high strength applications. The reinforcement has been put to a level that combines mouldability with high strength and stiffness properties. The specific re..
Flexural Strength	280 MPa	40600 psi	ISO 178
Solvay TECHNYLÂ® A 218 V30 BK 34 NG PA66, 30% glass fiber, DRY Description: TECHNYLÂ® A 218 V30 Black 34 NG is a polyamide 66, reinforced with 30% of glass fiber, heat stabilized, for injection molding. The product is available in black color.Benefits: This p..
Flexural Strength	280 MPa	40600 psi	ASTM D790
Solvay TECHNYLÂ® A 218HP V50 PA66, 35% glass fiber, DRY Description: TECHNYLÂ® A 218HP V50 is a polyamide 66, reinforced with 50% of glass fiber, heat stabilized, for injection molding. This product is available in black color.Benefits: The product off..
Flexural Strength	280 MPa	40600 psi	ISO 178
SABIC Innovative Plastics LNP LUBRICOMP QCL34 PA6.10 LNP* LUBRICOMP* QCL34 is a compound based on Nylon 6/10 resin containing 15% PTFE, 20% Carbon Fiber. Added features of this material include: Wear Resistant, Electrically Conductive.
Flexural Strength	280 MPa	40600 psi	ISO 178
Solvay Specialty Polymers AvaSpireÂ® AV-651 CF30 Polyaryletherketone (PAEK), 30% Carbon Fiber AvaSpireÂ® AV-651 CF30 is a 30% carbon fiber reinforced version of AvaSpireÂ® AV-651. This formulation offers some advantages relative to 30% carbon fiber reinforced PEEK which include better di..
Flexural Strength	280 MPa @Strain 3.50 %	40600 psi @Strain 3.50 %	ISO 178
Solvay Specialty Polymers KalixÂ® 9945 HFFR Polyamide, High Performance (HPPA), 45% Glass Fiber KalixÂ® 9945 HFFR is a 45% glass-fiber reinforced, halogen-free flame retardant High Performance Polyamide. It is hot-water moldable and intended for use in components requiring superior mechanica..
Flexural Strength	280 MPa	40600 psi	ISO 178
Solvay Specialty Polymers RytonÂ® BR42B Polyphenylene Sulfide (PPS), 40% Glass Fiber RytonÂ® BR42B 40% glass fiber reinforced polyphenylene sulfide compound is specially formulated to provide low coefficient of friction and reduced wear rate for use in applications requiring low s..
Flexural Strength	280 MPa	40600 psi	ASTM D790
Solvay Specialty Polymers RytonÂ® R-4-280BL Polyphenylene Sulfide (PPS), Glass Fiber RytonÂ® R-4-280BL 40% glass fiber reinforced polyphenylene sulfide compound provides a combination of enhanced mechanical strength and good flow for injection molding.Features: Good Chemical Resis..
Flexural Strength	280 MPa	40600 psi	ISO 178
Solvay Specialty Polymers RytonÂ® R-4XT Polyphenylene Sulfide (PPS), 40% Glass Fiber RytonÂ® R-4XT and R-4-02XT 40% glass fiber reinforced polyphenylene sulfide compounds provide enhanced mechanical strength with good electrical properties and outstanding chemical resistance, even..
Flexural Strength	280 MPa	40600 psi	ASTM D790
SABIC Innovative Plastics LNP THERMOCOMP EC006 PEI LNP THERMOCOMP* EC006 is a compound based on Polyetherimide resin containing 30% Carbon Fiber. Added features of this material include: Electrically Conductive.
Flexural Strength	280 MPa	40600 psi	ASTM D790
SABIC Innovative Plastics LNP THERMOCOMP EC006 PEI (Asia Pacific) LNP THERMOCOMP* EC006 is a compound based on Polyetherimide resin containing Carbon Fiber. Added features of this material include: Electrically Conductive.
Flexural Strength	280 MPa	40600 psi	2 mm/min; ISO 178
Sax Polymers SAXAMID 226F6 Nylon 6.6, 30% Glass Fiber SAXAMID 226F6 is a general purpose polyamide 6.6 injection-molding-grade reinforced with 30% glass fibers. It has very high mechanical strength in combination with good flow properties. It shows hig..
Flexural Strength	280 MPa	40600 psi	ASTM C1161
M Cubed Technologies SSC-802 Reaction-Bonded Silicon Carbide Medium-grained reaction-bonded SiC for high wear applications. Bullnoses, fan liners, hydrocyclone liners, etc. Can be cast into very large shapes (greater than 4 ft. square, 5-6 inches thick)Info..
Flexural Strength	280 MPa	40600 psi	ASTM D790
Polyram PlusTek PB300G7 Nylon 6, 35% Glass Fiber 35% glass-fiber reinforced, heat stabilized polyamide 6 for injection molding applicationsInformation provided by Polyram Ram On Ind.
Flexural Strength	280 MPa	40600 psi	ASTM D790
Polyram PlusTek PB304G7 Nylon 6, 35% Glass Fiber 35% glass-fiber reinforced, heat stabilized and impact modified polyamide 6 for injection molding applicationsInformation provided by Polyram Ram On Ind.
Flexural Strength	280 MPa	40600 psi	ISO 178
Tisan TISSAN® UNR Styrene Acrylonitrile Properties:Natural or ColoredGlass fiber and glass beadMineral filledFlame retardantGood thermal and chemical resistanceExcellent transparencyExcellent mechanical propertiesDimensional stabilityEasy..
Flexural Strength	280 MPa	40600 psi	dry; ISO 178
DSM Novamid® 1015G33-8 NAT PA6-GF33 33% Glass Reinforced, Injection Molding
Flexural Strength	280 MPa	40600 psi	2 mm/min; ISO 178
Eurostar Staramide BG7H PA6, 35% Glass Fiber Filled, Heat Stabilized, Injection Molded Staramide BG7H is a Heat Stabilized, 35% Glass Fiber Reinforced, Polyamide 6, Injection Molding ResinInformation provided by Eurostar.
Flexural Strength	>= 280 MPa	>= 40600 psi	cold bending
China-Yixing Longly Refractories Steatite Ceramics (High Frequency Porcelain) LONGLY's steatite ceramics (namely high frequency porcelain, strengthened porcelain, magnesia porcelain), molecular formula as MgO-SiO2, is pure white. Steatite is the appropriate option when good ..
Flexural Strength	280 MPa	40600 psi	2 mm/min; ISO 178
Eurostar Staramide PF007 PA6, 35% Glass Fiber Filled, Injection Molded Staramide PF007 is a 35% Glass Fiber Reinforced, Polyamide 6 Injection Molding ResinInformation provided by Eurostar.
Flexural Strength	280 MPa	40600 psi	2.8mm/min; ASTM D790
Asia International Enterprise (Hong Kong) 60G6-33GF Nylon 66, 33% Filled Information provided by Asia International Enterprise (Hong Kong) Ltd.
Flexural Strength	280 MPa	40600 psi	ASTM D790
Gharda Chemicals G-PAEK™ 1230GF Ultra High Performance PEK Polymer Product Details: Ultra High Performance Thermoplastic material, 30% glass fiber reinforced in Poly Aryl Ether Ketone, semi-crystalline granules suitable for injection molding, standard flow, Beige ..
Flexural Strength	280 MPa	40600 psi	ISO 178
Solvay Specialty Polymers Amodel® A-1933 HSL Polyphthalamide (PPA) (Unverified Data**) Amodel A-1933 HSL is a 33% glass reinforced grade of polyphthalamide (PPA) resin. This grade was developed specifically for improved performance in a 50/50 ethylene glycol and water environment. Thi..