Solvay Specialty Polymers Amodel® AS-1935 HS Polyphthalamide (PPA), 35% Glass Fiber

Category Polymer , Thermoplastic , Polyphthalamide (PPA) , Polyphthalamide (PPA), 40% Glass Fiber Reinforced
Manufacturer Solvay Specialty Polymers
Trade Name Amodel®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay Specialty Polymers Amodel® AS-1935 HS Polyphthalamide (PPA), 35% Glass Fiber.pdf
  Online Service   lookpolymers   27660005
Material Notes:
Amodel® AS-1935 HS is a 35% glass reinforced grade of polyphthalamide (PPA) resin developed specifically for improved performance in a 50/50 ethylene glycol and water environment. This material exceeds the performance required by the automotive industry for polymeric materials exposed to antifreeze at 226°F (108°C), even when tested at 275°F (135°C).Features: Antifreeze Resistant; Glycol Resistant; Good Chemical Resistance; Good Creep Resistance; Good Dimensional Stability; Good Stiffness; Heat Stabilized; High Heat Resistance; High StrengthUses: Automotive Applications; Automotive Under the Hood; Housings; Industrial Applications; Industrial Parts; Machine/Mechanical Parts; Metal Replacement; Power/Other Tools; Thick-walled Parts; Valves/Valve PartsInjection Molding Notes: Amodel® compounds are shipped in moisture-resistant packages at moisture levels according to specifications. Sealed, undamaged bags should be preferably stored in a dry room at a maximum temperature of 50°C (122°F) and should be protected from possible damage. If only a portion of a package is used, the remaining material should be transferred into a sealable container. It is recommended that Amodel® resins be dried prior to molding.Automotive Specifications HYUNDAI MS211-19 AS-1935 HS Color: BK 238 BlackInformation provided by Solvay Specialty Polymers.
Physical Properties Metric English Comments
Density 1.49 g/cc
0.0538 lb/in³
ISO 1183
Filler Content 35 %
35 %
Glass Fiber
Linear Mold Shrinkage, Flow 0.0020 cm/cm
0.0020 in/in
Linear Mold Shrinkage, Transverse 0.0060 cm/cm
0.0060 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 205 MPa
29700 psi
210 MPa
30500 psi
ISO 527-2
Elongation at Break 2.2 %
2.2 %
ISO 527-2
2.2 %
2.2 %
Tensile Modulus 12.5 GPa
1810 ksi
12.6 GPa
1830 ksi
1 mm/min, Type 1A; ISO 527-2
Flexural Strength 275 MPa
39900 psi
300 MPa
43500 psi
ISO 178
Flexural Modulus 11.3 GPa
1640 ksi
11.5 GPa
1670 ksi
ISO 178
Izod Impact, Notched 0.650 J/cm
1.22 ft-lb/in
Izod Impact, Notched (ISO) 8.50 kJ/m²
4.04 ft-lb/in²
Type 1, Notch A; ISO 180
Charpy Impact Unnotched 6.60 J/cm²
31.4 ft-lb/in²
Type 1, Edgewise; ISO 179
Charpy Impact, Notched 0.800 J/cm²
3.81 ft-lb/in²
Type 1, Edgewise; ISO 179
Thermal Properties Metric English Comments
Melting Point 323 °C
613 °F
ISO 11357-3
Deflection Temperature at 1.8 MPa (264 psi) 290 °C
554 °F
Unannealed; Flatwise; ISO 75-2/A
Processing Properties Metric English Comments
Processing Temperature 79.4 °C
175 °F
Rear Barrel Temperature 313 - 330 °C
595 - 626 °F
Front Barrel Temperature 326 - 339 °C
619 - 642 °F
Melt Temperature 330 - 350 °C
626 - 662 °F
Mold Temperature 150 °C
302 °F
Drying Temperature 121 °C

@Time 14400 sec
250 °F

@Time 4.00 hour
Moisture Content <= 0.10 %
<= 0.10 %
Descriptive Properties Value Comments
Additive Heat Stabilizer
Availability Africa & Middle East
Asia Pacific
Latin America
North America
Color Black
Form Pellets
Processing Technique Injection Molding
RoHS Compliance RoHS Compliant