Polymer Property : Flexural Modulus = 1640 ksi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Modulus	11.3 GPa	1640 ksi	1.3 mm/min, 50 mm span; ASTM D790
Ovation Polymers UTTAP SF 50030GF Polyethersulfone, 30% Glass Reinforced Glass reinforced (30 %) Polyether Sulfone, excellent chemical and electrical resistance, high stiffness, modulus and HDT. *All properties are measured after 48 hours of conditioning at 23°C and 50%..
Flexural Modulus	11.3 GPa	1640 ksi	1.3 mm/min, 50 mm span; ASTM D790
Ovation Polymers UTTAP™ SF 50030 GF Polyether Sulfone, 30% Glass Fiber Excellent chemical and electrical resistance, high stiffness, modulus and HDTAll properties after 48hrs conditioning at 23°C/50% RH
Flexural Modulus	11.3 GPa	1640 ksi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP KONDUIT PX08322 PA 6 (Europe-Africa-Middle East) Thermally conductive mineral filled PA6 non-halogen FR compound
Flexural Modulus	11.3 GPa	1640 ksi	ASTM D790
LNP Thermocomp® OF-1006 Polyphenylene Sulfide, Glass Fiber Reinforcement (discontinued **) Forms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP grades are still active under new names..
Flexural Modulus	11.3 GPa	1640 ksi	ASTM D790
LNP Lubricomp® EFL-4036 Polyetherimide, Glass Fiber Reinforcement, PTFE Lubricant (discontinued **) Features: LubricatedForms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP grades are still ac..
Flexural Modulus	11.3 GPa @Temperature 22.0 Â°C	1640 ksi @Temperature 71.6 Â°F	25 mm wide 100 mm long, flat samples; ISO 14125
Menzolit MenzolitÂ® BMC 2900 Unsaturated Polyester UP BMC 2900 is a specially designed BMC to meet the EC Safety Signs Directive (92/58/EEC) on the provision and use of safety signs at work. In areas where it is not possible to include the use of illu..
Flexural Modulus	11.3 GPa	1640 ksi	ASTM D790
SABIC Innovative Plastics LNP LUBRICOMP EFL36 PEI LNP LUBRICOMP* EFL36 is a compound based on Polyetherimide resin containing 30% Glass Fiber, 15% PTFE. Added features of this material include: Internally Lubricated.
Flexural Modulus	11.3 GPa	1640 ksi	ASTM D790
SABIC Innovative Plastics LNP LUBRICOMP EFL36 PEI (Asia Pacific) LNP LUBRICOMP* EFL36 is a compound based on Polyetherimide resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated.
Flexural Modulus	11.3 GPa	1640 ksi	ASTM D790
SABIC Innovative Plastics LNP LUBRICOMP EFL36 PEI (Europe-Africa-Middle East) LNP LUBRICOMP* EFL36 is a compound based on Polyetherimide resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated.
Flexural Modulus	11.3 GPa	1640 ksi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics LNP LUBRICOMP EFL36XXC PEI LNP* Lubricomp* EFL36XXC is a compound based on Polyetherimide containing 30% Glass Fiber, 155 PTFE. Characteristics of this grade are: Internally Lubricated.
Flexural Modulus	11.3 GPa	1640 ksi	ISO 178
SABIC Innovative Plastics LNP LUBRILOY RF208 PA 66 LNP LUBRILOY* RF208 is a compound based on Nylon 66 resin containing 40% Glass Fiber, Proprietary Lubricant. Added features of this material include: Wear Resistant.
Flexural Modulus	11.3 GPa	1640 ksi	ISO 178
SABIC Innovative Plastics LNP LUBRILOY RF208 PA 66 (Asia Pacific) LNP LUBRILOY* RF208 is a compound based on Nylon 66 resin containing Glass Fiber, Proprietary Lubricant. Added features of this material include: Internally Lubricated.
Flexural Modulus	11.3 GPa	1640 ksi	ASTM D790
Solvay Specialty Polymers AmodelÂ® AS-1935 HS Polyphthalamide (PPA), 35% Glass Fiber AmodelÂ® AS-1935 HS is a 35% glass reinforced grade of polyphthalamide (PPA) resin developed specifically for improved performance in a 50/50 ethylene glycol and water environment. This material e..
Flexural Modulus	11.3 GPa	1640 ksi	2.8 mm/min; ASTM D638
Samsung Cheil Industries InfinoÂ® VB-5400G PBT, Glass Filled FR Information provided by Samsung Cheil Industries.
Flexural Modulus	11.3 GPa	1640 ksi	ISO 178
SABIC Innovative Plastics LNP THERMOCOMP RF008ESY PA 66 LNP THERMOCOMP* RF008ESY is a compound based on Nylon 66 resin containing 40% Glass Fiber. Added features of this material include: Easy Molding, Heat Stabilized.
Flexural Modulus	11.3 GPa	1640 ksi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP STAT-KON DX05042 PC (Europe-Africa-Middle East) LNP* Stat-kon* DX05042 is a compound based on Polycarbonate resin containing Glass Fiber, PTFE, Carbon Fiber. Added features of this material include: Electrically Conductive, Easy Molding.
Flexural Modulus	11.3 GPa	1640 ksi	2.8 mm/min; ASTM D638
Samsung Cheil Industries InfinoÂ® VB-5400G PBT, Glass Filled FR Information provided by Samsung Cheil Industries.
Flexural Modulus	11.3 GPa	1640 ksi	1.3 mm/min, 50 mm span; ASTM D 790
SABIC Innovative Plastics LNP Verton RV008ESV_GY7E072 PA 66 Preliminary data for 40% long glass fiber filled, single color pellet gray, PA66This data was supplied by SABIC-IP for the Americas region.
Flexural Modulus	11.3 GPa	1640 ksi	ASTM D790
Plenco 1501 Polyester, Briquette, Transfer Molded PLENCO 01501 is a general purpose, mineral filled granular polyester molding compound, offering excellent arc and track resistance properties, low post shrinkage, and improved mechanical strength va..
Flexural Modulus	11.3 GPa	1640 ksi	cond; ISO 178
DSM EcoPaXX® Q-HG10 PA410-GF50 50% Glass Reinforced, Heat Stabilized
Flexural Modulus	11.3 GPa	1640 ksi	1.3 mm/min, 50 mm span; ASTM D 790
SABIC Innovative Plastics LNP Verton RX93407D PA 66 LNP* Verton* RX93407D is a compound based on Nylon 66 resin.This data was supplied by SABIC-IP for the Americas region.