SABIC Innovative Plastics XYLEX X8210 PC+POLYESTER (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/PET Polyester Blend , Polyester, TP , Polyethylene Terephthalate (PET) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Xylex |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics XYLEX X8210 PC+POLYESTER (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PC+POLYESTER alloy. Unreinforced, transparent, impact modified for low temperature ductility
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D792 |
| Density | 1.16 g/cc | 0.0419 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.150 % | 0.150 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.37 % | 0.37 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0080 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0080 in/in @Thickness 0.126 in |
SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0040 - 0.0060 cm/cm @Thickness 3.20 mm |
0.0040 - 0.0060 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 10 g/10 min @Load 2.16 kg, Temperature 265 °C |
10 g/10 min @Load 4.76 lb, Temperature 509 °F |
ASTM D1238 |
| 14 g/10 min @Load 1.20 kg, Temperature 300 °C |
14 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 | |
| Melt Index of Compound | 10 g/10 min @Load 2.16 kg, Temperature 265 °C |
10 g/10 min @Load 4.76 lb, Temperature 509 °F |
MVR [cm^3/10 min]; ISO 1133 |
| 13 g/10 min @Load 1.20 kg, Temperature 300 °C |
13 g/10 min @Load 2.65 lb, Temperature 572 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 45.0 MPa | 6530 psi | 50 mm/min; ISO 527 |
| 46.0 MPa | 6670 psi | Type I, 50 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 43.0 MPa | 6240 psi | Type I, 50 mm/min; ASTM D638 |
| 45.0 MPa | 6530 psi | 50 mm/min; ISO 527 | |
| Elongation at Break | 150 % | 150 % | Type I, 50 mm/min; ASTM D638 |
| >= 150 % | >= 150 % | 50 mm/min; ISO 527 | |
| Elongation at Yield | 4.6 % | 4.6 % | 50 mm/min; ISO 527 |
| 5.0 % | 5.0 % | Type I, 50 mm/min; ASTM D638 | |
| Tensile Modulus | 1.48 GPa | 215 ksi | 50 mm/min; ASTM D638 |
| 1.50 GPa | 218 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 58.0 MPa | 8410 psi | 2 mm/min; ISO 178 |
| Flexural Yield Strength | 65.0 MPa | 9430 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 1.60 GPa | 232 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 1.60 GPa | 232 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 8.00 J/cm | 15.0 ft-lb/in | ASTM D256 |
| 2.00 J/cm @Temperature -30.0 °C |
3.75 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| 6.40 J/cm @Temperature -20.0 °C |
12.0 ft-lb/in @Temperature -4.00 °F |
ASTM D256 | |
| Izod Impact, Notched (ISO) | 45.0 kJ/m² | 21.4 ft-lb/in² | 80*10*4; ISO 180/1A |
| 11.0 kJ/m² @Temperature -30.0 °C |
5.23 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| 30.0 kJ/m² @Temperature -10.0 °C |
14.3 ft-lb/in² @Temperature 14.0 °F |
80*10*4; ISO 180/1A | |
| Charpy Impact, Notched | 7.10 J/cm² | 33.8 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Dart Drop, Total Energy | 81.0 J @Temperature 23.0 °C |
59.7 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 83.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
46.1 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 110 µm/m-°C @Temperature -40.0 - 40.0 °C |
61.1 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| CTE, linear, Transverse to Flow | 89.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
49.4 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 110 µm/m-°C @Temperature -40.0 - 40.0 °C |
61.1 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 79.0 °C @Thickness 3.20 mm |
174 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 81.0 °C | 178 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 82.0 °C | 180 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae | |
| 75.0 °C @Thickness 3.20 mm |
167 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 92.0 °C | 198 °F | Rate B/50; ISO 306 |
| 97.0 °C | 207 °F | Rate B/120; ISO 306 | |
| 97.0 °C | 207 °F | Rate B/50; ASTM D1525 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 4.0 % @Thickness 2.54 mm |
4.0 % @Thickness 0.100 in |
ASTM D1003 |
| Transmission, Visible | 85 % | 85 % | 2.54 mm; ASTM D1003 |