Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 46.0 MPa | 6670 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Cycoloy® CU6800 PC+ABS Non-chlorinated and non-brominated flame retardant PC/ABS featuring excellent flow properties. UL-94 V1 listed at 2.0mm intended for a wide range of different applications. |
|||
Tensile Strength at Break | 46.0 MPa | 6670 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Cycoloy® CY5105 PC+ABS (Europe-Africa-Middle East) Flame retardant PC/ABS blend using non-brominated and non-chlorinated flame retardant systems, offering excellent flow / impact balance for large size applicationsThis data was supplied by SABIC-IP .. |
|||
Tensile Strength at Break | 46.0 MPa | 6670 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Cycoloy® FXC630SK PC+ABS (Asia Pacific) PC+ABS, ECO-conforming flame retardant with diamond sparkle appearance. |
|||
Tensile Strength at Break | 46.0 MPa | 6670 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics Lexan® EXL4016H PC Copolymer 6% GF reinforced opaque polycarbonate-siloxane copolymer with good impact strength, stiffness and hydrolytic stability. |
|||
Tensile Strength at Break | 46.0 MPa | 6670 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Lexan® FXG1413T PC Copolymer (Asia Pacific) PC-siloxane copolymer in special ""Diamond Sparkle"" colors. Medium flow. Improved toughness compared to medium flow standard PC in same color. Color package may affect performance. |
|||
Tensile Strength at Break | 46.0 MPa | 6670 psi | ASTM D638 |
Ineos Nova PS 3190 Crystal Polystyrene
(discontinued **) Information provided by Nova ChemicalsINEOS NOVA began October 1 2007 as an expansion of the 50:50 joint venture between NOVA Chemicals and INEOS to include North American assets. |
|||
Tensile Strength at Break | 46.0 MPa | 6670 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP CGI11 PS (Europe-Africa-Middle East) LNP * Lubricomp* CGI11 is a compound based on Polystyrene resin containing Graphite. Added features include: Internally Lubricated. |
|||
Tensile Strength at Break | 46.0 MPa | 6670 psi | ISO 527 |
GEHR Plastics PVDF Polyvinylidene Fluoride Polyvinylidene fluoride shows a higher tensile strength, pressure resistance and dimensional stability than the related PTFE, but friction and insulation properties are lower. PVDF has a high mechan.. |
|||
Tensile Strength at Break | 46.0 MPa | 6670 psi | ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP DP003EH PC LNP LUBRICOMP* DP003EH is a compound based on Polycarbonate resin containing 15% PTFE/Silicone. Added features of this material include: Easy Molding, Internally Lubricated, Healthcare. |
|||
Tensile Strength at Break | 46.0 MPa | 6670 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics NORYL SE100HX PPE+PS Improved productivity and reliability. Nonchlorinated, nonbrominated FR. |
|||
Tensile Strength at Break | 46.0 MPa | 6670 psi | ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP KZL16 Acetal Copolymer LNP LUBRICOMP* KZL16 is a compound based on Acetal Copolymer resin containing Glass Fiber, Milled Glass, PTFE. Added features of this material include: Internally Lubricated. |
|||
Tensile Strength at Break | 46.0 MPa | 6670 psi | ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP RL0049S PA 66 LNP LUBRICOMP* RL0049S is a compound based on Nylon 66 resin containing 20% PTFE. Added features of this material include: Flame Retardant, Heat Stabilized, Wear Resistant. |
|||
Tensile Strength at Break | 46.0 MPa | 6670 psi | ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP ZL003 PPE+PS (Asia Pacific) LNP LUBRICOMP ZL003 is a compound based on PPE+PS Blend resin containing PTFE. Added features of this material include:internally Lubricated. Also known as LUBRICOMP ZL-4030 |
|||
Tensile Strength at Break | 46.0 MPa | 6670 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Xenoy® IQ1103R PBT+PC (Europe-Africa-Middle East) Xenoy* Resin iQ1103R - Environmetally responsible, sustainable, and low carbon footprint resin. Xenoy iQ1103R is an unreinforced, impact modified PC + iQ-PBT alloy with excellent low temperature im.. |
|||
Tensile Strength at Break | 46.0 MPa | 6670 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Xenoy® IQ1103U PBT+PC Xenoy* Resin iQ1103U - Environmetally responsible, sustainable, and low carbon footprint resin. Xenoy iQ1103U is an unreinforced, UV stable, impact modified PC+ iQ-PBT alloy with excellent low temp.. |
|||
Tensile Strength at Break | 46.0 MPa | 6670 psi | Type I, 50 mm/min; ASTM D 638 |
SABIC Innovative Plastics Xylex X8300HP PC+POLYESTER (Europe-Africa-Middle East) Transparent, US Food Contact compliant, chemically resistant.
This grade will no longer be supported with biocompatibility information and should not be used for medical applications which require b.. |
|||
Tensile Strength at Break | 46.0 MPa | 6670 psi | ISO 527-1/-2 |
Styrolution Polystyrol 143 E GR 2 PS Description: Polystyrol 143 E is a medium strength, easy flowing general purpose grade, suitable for blending with impact modified Polystyrol, Styrolux and coextruded gloss layers.Applications: In b.. |
|||
Tensile Strength at Break | 46.0 MPa | 6670 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP PH0240A PA 6 LNP* THERMOCOMP* PH0240A is a compound based on Nylon 6 resin. Added features of this grade include: High Impact, High Specific Gravity. |
|||
Tensile Strength at Break | 46.0 MPa | 6670 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Valox® 745 PBT (Asia Pacific) 30% mineral reinforced polyester improved toughness and low warpage. Typical applications are telephone ringer frames and card racks. |
|||
Tensile Strength at Break | 46.0 MPa | 6670 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics XYLEX X8300 PC+POLYESTER (Europe-Africa-Middle East) PC+Polyester, UV Stabilized, Transparent |
|||
Tensile Strength at Break | 46.0 MPa | 6670 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP NX11302 PC+ABS (Asia Pacific) This is a PC/ABS compound with colorable, good plating, surface and mechanical performance, a good candidate for Laser Direct Structuring applications |
|||
Tensile Strength at Break | 46.0 MPa | 6670 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP YF005 POLYESTER ELASTOMER LNP* THERMOCOMP* YF005 is a compound based on Polyester Elastomer resin containing 25% Glass Fiber. |
|||
Tensile Strength at Break | 46.0 MPa | 6670 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics NORYL EXNL0303 PPE+HIPS (Europe-Africa-Middle East) EXNL0303 is a modified PPE-HIPS blend that presents an excellent balance of non halogenated flame retardance, lower smoke production upon burning and low specific gravity for light weight parts. Nor.. |
|||
Tensile Strength at Break | 46.0 MPa | 6670 psi | ASTM D638 |
Eastman Tritan GX100 Copolyester Eastman Tritan copolyester GX100's strength, clarity and temperature resistance make it ideal for demanding applications. Extruded Sheet is manufactured with Eastman's Tritan copolyester GX100 resi.. |
|||
Tensile Strength at Break | 46.0 MPa | 6670 psi | conditioned; ISO 527-1/-2 |
EMS-Grivory Grivory® R 47 HW 10 PA6 Grilon R 47 HW 10 is a flexible, cold impact resistant and heat stabilized polyamide 6 for applications in the extrusion. The material can be processed on all for polyamides suitable tube-extrusion .. |
|||
Tensile Strength at Break | 46.0 MPa | 6670 psi | 5 mm/min; ISO 527 |
Eurostar Starglas CF006 Styrenic, 30% Glass Filled, Injection Molding Starglas CF006 is a 30% Glass Fiber Reinforced Styrenic Injection Molding ResinInformation provided by Eurostar. |
|||
Tensile Strength at Break | >= 46.0 MPa | >= 6670 psi | 5 mm/min.; IS 867-1963 |
Amity Thermosets ATM 123 Phenolic Molding Organic Filler, Compression Molded Characteristics:Glossy surface free of filler marks Surface good & free of flaws Good mouldabilitySurface free of filler marks even after turningGood mechanical strengthColor-black, brownMedium flow.. |
|||
Tensile Strength at Break | 46.0 - 56.0 MPa | 6670 - 8120 psi | 5 mm/min.; IS 867-1963 |
Amity Thermosets ATS 134 Phenolic Molding Inorganic, graphite Filler, Compression Molded Characteristics: Low coefficient of frictionSelf lubricating ( graphite modified )Good thermal conductivityGood glide propertiesNot suitable for electrical applicationColor- black gray Soft/medium f.. |
|||
Tensile Strength at Break | 46.0 - 55.0 MPa | 6670 - 7980 psi | 5 mm/min.; IS 867-1963 |
Amity Thermosets ATS 1613-R Phenolic Molding Nylon and glass Filler, Compression Molded Characteristics:High dielectric & mechanical strengthWeather resistant Good electric insulationLow water absorption Good mechanical tension bearing capacityColor-blackMedium flow Applications:Railwa.. |
|||
Tensile Strength at Break | 46.0 - 55.0 MPa | 6670 - 7980 psi | 5 mm/min.; IS 867-1963 |
Amity Thermosets ATR 126 Phenolic Molding Organic Filler, Compression Molded Characteristics:Ammonia freeGood mouldabilityGood mechanical strengthGood electrical insulationGood surface finishMedium thermal stability Color-black, brownSoft/medium flow Applications:Telecommuni.. |