SABIC Innovative Plastics NORYL PX6120 PPE+PS (Asia Pacific)

Category Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Noryl
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics NORYL PX6120 PPE+PS (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Noryl PX6120 is an unfilled material with good flow, high Impact and chemical resistance against cleaners. Noryl PX6120 is developed for personal care appplications.
Physical Properties Metric English Comments
Specific Gravity 1.05 g/cc
1.05 g/cc
ASTM D792
Density 1.05 g/cc
0.0379 lb/in³
ISO 1183
Moisture Absorption 0.0500 %
0.0500 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.25 %
0.25 %
ISO 62
Linear Mold Shrinkage, Flow 0.0060 - 0.0080 cm/cm

@Thickness 3.20 mm
0.0060 - 0.0080 in/in

@Thickness 0.126 in
SABIC Method
Linear Mold Shrinkage, Transverse 0.0060 - 0.0080 cm/cm

@Thickness 3.20 mm
0.0060 - 0.0080 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 11.9 g/10 min

@Load 5.00 kg,
Temperature 280 °C
11.9 g/10 min

@Load 11.0 lb,
Temperature 536 °F
ASTM D1238
Melt Index of Compound 12 g/10 min

@Load 5.00 kg,
Temperature 280 °C
12 g/10 min

@Load 11.0 lb,
Temperature 536 °F
MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 39.0 MPa
5660 psi
50 mm/min; ISO 527
44.0 MPa
6380 psi
Type I, 50 mm/min; ASTM D638
Tensile Strength, Yield 46.0 MPa
6670 psi
50 mm/min; ISO 527
48.0 MPa
6960 psi
Type I, 50 mm/min; ASTM D638
Elongation at Break 39 %
39 %
50 mm/min; ISO 527
40.8 %
40.8 %
Type I, 50 mm/min; ASTM D638
Elongation at Yield 2.4 %
2.4 %
50 mm/min; ISO 527
2.8 %
2.8 %
Type I, 50 mm/min; ASTM D638
Tensile Modulus 2.43 GPa
352 ksi
1 mm/min; ISO 527
2.67 GPa
387 ksi
5 mm/min; ASTM D638
Flexural Yield Strength 73.0 MPa
10600 psi
2 mm/min; ISO 178
78.0 MPa
11300 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 2.26 GPa
328 ksi
2 mm/min; ISO 178
2.33 GPa
338 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 3.67 J/cm
6.88 ft-lb/in
ASTM D256
2.11 J/cm

@Temperature -30.0 °C
3.95 ft-lb/in

@Temperature -22.0 °F
ASTM D256
Izod Impact, Notched (ISO) 24.0 kJ/m²
11.4 ft-lb/in²
80*10*4; ISO 180/1A
14.0 kJ/m²

@Temperature -30.0 °C
6.66 ft-lb/in²

@Temperature -22.0 °F
80*10*4; ISO 180/1A
Charpy Impact, Notched 2.50 J/cm²
11.9 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy 52.0 J

@Temperature 23.0 °C
38.4 ft-lb

@Temperature 73.4 °F
ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 93.2 µm/m-°C

@Temperature -40.0 - 40.0 °C
51.8 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
93.2 µm/m-°C

@Temperature -40.0 - 40.0 °C
51.8 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
CTE, linear, Transverse to Flow 95.6 µm/m-°C

@Temperature -40.0 - 40.0 °C
53.1 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
95.6 µm/m-°C

@Temperature -40.0 - 40.0 °C
53.1 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi) 109 °C
228 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
105 °C

@Thickness 3.20 mm
221 °F

@Thickness 0.126 in
unannealed; ASTM D648
Vicat Softening Point 126 °C
259 °F
Rate B/50; ASTM D1525
126 °C
259 °F
Rate B/50; ISO 306
129 °C
264 °F
Rate B/120; ISO 306