Hexcel® HexPly® F655 Bismaleimide Resin, Carbon Fabric Form

Category	Polymer , Thermoset , Polyimide, TS
Manufacturer	Hexcel
Trade Name	HexPly®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Hexcel® HexPly® F655 Bismaleimide Resin, Carbon Fabric Form.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Fiber: T300-3KInformation provided by HexCel

Physical Properties	Metric	English	Comments
Density	1.53 - 1.56 g/cc	0.0553 - 0.0564 lb/in³	Laminate
Volatiles	<= 2.0 %	<= 2.0 %	Prepreg

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	573 MPa @Temperature 177 °C	83100 psi @Temperature 351 °F	T300, Plain Weave; Fill Tension; Wet
	574 MPa @Temperature -59.0 °C	83300 psi @Temperature -74.2 °F	T300, Plain Weave; Fill Tension;
	579 MPa @Temperature 232 °C	84000 psi @Temperature 450 °F	T300, Plain Weave; Fill Tension; AMC
	638 MPa @Temperature 232 °C	92500 psi @Temperature 450 °F	T300, Plain Weave; Fill Tension; Dry
	665 MPa @Temperature 23.0 °C	96500 psi @Temperature 73.4 °F
Tensile Modulus	60.0 GPa @Temperature 232 °C	8700 ksi @Temperature 450 °F	T300, Plain Weave; Fill Tension; AMC
	60.7 GPa @Temperature 177 °C	8800 ksi @Temperature 351 °F	T300, Plain Weave; Fill Tension; Wet
	61.4 GPa @Temperature 23.0 °C	8910 ksi @Temperature 73.4 °F
	64.8 GPa @Temperature -59.0 °C	9400 ksi @Temperature -74.2 °F	T300, Plain Weave; Fill Tension;
Compressive Yield Strength	420 MPa @Temperature 177 °C	60900 psi @Temperature 351 °F	T300, Plain Weave; Fill Compression; Wet
	445 MPa @Temperature 232 °C	64500 psi @Temperature 450 °F	T300, Plain Weave; Fill Compression; AMC
	896 MPa @Temperature 23.0 °C	130000 psi @Temperature 73.4 °F
	1111 MPa @Temperature -59.0 °C	161100 psi @Temperature -74.2 °F	T300, Plain Weave; Fill Compression
Compressive Modulus	57.4 GPa @Temperature 232 °C	8330 ksi @Temperature 450 °F	T300, Plain Weave; Fill Compression; Dry
	57.9 GPa @Temperature 23.0 °C	8400 ksi @Temperature 73.4 °F
	58.6 GPa @Temperature 177 °C	8500 ksi @Temperature 351 °F	T300, Plain Weave; Fill Compression; Wet
	58.7 GPa @Temperature -59.0 °C	8510 ksi @Temperature -74.2 °F	T300, Plain Weave; Fill Compression
Shear Strength	37.9 MPa @Temperature 232 °C	5500 psi @Temperature 450 °F	T300, Plain Weave; Fill Short Beam; AMC
	43.41 MPa @Temperature 177 °C	6296 psi @Temperature 351 °F	T300, Plain Weave; Fill Short Beam; Wet
	51.68 MPa @Temperature 232 °C	7496 psi @Temperature 450 °F	T300, Plain Weave; Fill Short Beam; Dry
	94.41 MPa @Temperature 23.0 °C	13690 psi @Temperature 73.4 °F
	97.88 MPa @Temperature -59.0 °C	14200 psi @Temperature -74.2 °F	T300, Plain Weave; Fill Short Beam

Descriptive Properties	Value	Comments
Cured Thickness per Ply (cm)	0.013-0.015	Laminate
Dry Resin Content (%)	33-37	Prepreg
Fiber Volume (%)	54-59	Laminate

Users viewing this material also viewed the following: